COMPOSITION FOR PRODUCING HEAT-RESISTANT COMPOSITES
FIELD: construction.SUBSTANCE: composition for producing heat-resistant composites includes, in mass %: spent catalyst IM-2201 10-15, crushed stone from carbonate rocks with the fraction of 5-10 mm 33-40, HPOwith the density of not less than 1.69 g/cm10-15, alumina-chromium waste of aluminium alloys etching with the particle size of 0.1 to 5 mcm 24-30, burnt clays ground up to passing through a 0.14 mm sieve and with the content of oxides, wt %: SiO- 61.5; AlO- 19.8; FeO- 7.4; CaO - 6.7; MgO - 2.2; RO - 1.1; LOI - 1.3, 10-13.EFFECT: increasing compressive tensile strength and thermal stability of heat-resistant composites, industrial waste utilisation.3 tbl
Изобретение относится к области строительных материалов, в частности к производству жаростойких композитов (бетонов) на основе химических связующих. Композиция для изготовления жаростойких композитов включает, мас.%: отработанный катализатор ИМ-2201 10-15, щебень из карбонатных пород фракции 5-10 мм 33-40, НРОплотностью не менее 1,69 г/см10-15, алюмохромистые отходы травления алюминиевых сплавов с размером частиц от 0,1 до 5 мкм 24-30, глиежи, размолотые до прохода через сито 0,14 мм и с содержанием оксидов, мас.%: SiO- 61,5; AlO-19,8; FeO- 7,4; СаО - 6,7; MgO - 2,2; RO - 1,1; п.п.п. - 1,3, 10-13. Технический результат – повышение предела прочности при сжатии и термостойкости жаростойких композитов, утилизация промышленных отходов. 3 табл.
COMPOSITION FOR PRODUCING HEAT-RESISTANT COMPOSITES
FIELD: construction.SUBSTANCE: composition for producing heat-resistant composites includes, in mass %: spent catalyst IM-2201 10-15, crushed stone from carbonate rocks with the fraction of 5-10 mm 33-40, HPOwith the density of not less than 1.69 g/cm10-15, alumina-chromium waste of aluminium alloys etching with the particle size of 0.1 to 5 mcm 24-30, burnt clays ground up to passing through a 0.14 mm sieve and with the content of oxides, wt %: SiO- 61.5; AlO- 19.8; FeO- 7.4; CaO - 6.7; MgO - 2.2; RO - 1.1; LOI - 1.3, 10-13.EFFECT: increasing compressive tensile strength and thermal stability of heat-resistant composites, industrial waste utilisation.3 tbl
Изобретение относится к области строительных материалов, в частности к производству жаростойких композитов (бетонов) на основе химических связующих. Композиция для изготовления жаростойких композитов включает, мас.%: отработанный катализатор ИМ-2201 10-15, щебень из карбонатных пород фракции 5-10 мм 33-40, НРОплотностью не менее 1,69 г/см10-15, алюмохромистые отходы травления алюминиевых сплавов с размером частиц от 0,1 до 5 мкм 24-30, глиежи, размолотые до прохода через сито 0,14 мм и с содержанием оксидов, мас.%: SiO- 61,5; AlO-19,8; FeO- 7,4; СаО - 6,7; MgO - 2,2; RO - 1,1; п.п.п. - 1,3, 10-13. Технический результат – повышение предела прочности при сжатии и термостойкости жаростойких композитов, утилизация промышленных отходов. 3 табл.
COMPOSITION FOR PRODUCING HEAT-RESISTANT COMPOSITES
Композиция для изготовления жаростойких композитов