BINDER
FIELD: construction.SUBSTANCE: invention relates to the building materials industry and can be used in the manufacture of acid-resistant concrete and mortar based on the unfired binder. Binder contains a reactive component, a hardening accelerator and an alkaline activator; according to the invention, kaolinite clay activated to a specific surface of 640 m/kg is used as the reactive component and baked at a temperature of 600–650 °C, which is mixed with volcanic tuff, dried before grinding at a temperature of 105 °C for 2 hours and ground to a specific surface of 520 m/kg in the presence of a sodium silicofluoride hardening accelerator and an alkaline activator based on sodium hydroxide and sodium liquid glass with a silicate module of 2.8 and a density of 1.24 g/cmat the following component ratio, wt. %: metakaolin 26.8–61.2, volcanic tuff 21.4–51.2, sodium silicofluoride NaSiF5.8–8.0, liquid glass NaSiO11.0–13.0, sodium hydroxide NaOH 0.6–1.0.EFFECT: technical result is an increase in the effectiveness of acid-resistant binder due to the improvement of its physical and mechanical and operational properties.1 cl, 1 tbl
Изобретение относится к промышленности строительных материалов и может быть использовано при изготовлении кислотоупорных бетонов и растворов на основе безобжигового вяжущего.Техническим результатом является повышение эффективности кислотоупорного вяжущего за счет улучшения его физико-механических и эксплуатационных свойств. Вяжущее вещество содержит реакционно-активный компонент, ускоритель твердения и щелочной активатор; согласно изобретению в качестве реакционно-активного компонента используют каолинитовую глину, активированную до удельной поверхности 640 м/кг и обожженную при температуре 600-650°C, которую смешивают с вулканическим туфом, высушенным перед измельчением при температуре 105°C в течение 2-х часов и измельченным до удельной поверхности 520 м/кг в присутствии ускорителя твердения «кремнефтористого натрия» и щелочного активатора на основе гидроксида натрия и жидкого стекла натриевого с силикатным модулем 2,8 и плотностью 1,24 г/смпри следующем соотношении компонентов, мас. %: метакаолин 26,8-61,2, вулканический туф 21,4-51,2, кремнефтористый натрий NaSiF5,8-8,0, жидкое стекло NaSiO11,0-13,0, гидроксид натрия NaOH 0,6-1,0. 1 табл.
BINDER
FIELD: construction.SUBSTANCE: invention relates to the building materials industry and can be used in the manufacture of acid-resistant concrete and mortar based on the unfired binder. Binder contains a reactive component, a hardening accelerator and an alkaline activator; according to the invention, kaolinite clay activated to a specific surface of 640 m/kg is used as the reactive component and baked at a temperature of 600–650 °C, which is mixed with volcanic tuff, dried before grinding at a temperature of 105 °C for 2 hours and ground to a specific surface of 520 m/kg in the presence of a sodium silicofluoride hardening accelerator and an alkaline activator based on sodium hydroxide and sodium liquid glass with a silicate module of 2.8 and a density of 1.24 g/cmat the following component ratio, wt. %: metakaolin 26.8–61.2, volcanic tuff 21.4–51.2, sodium silicofluoride NaSiF5.8–8.0, liquid glass NaSiO11.0–13.0, sodium hydroxide NaOH 0.6–1.0.EFFECT: technical result is an increase in the effectiveness of acid-resistant binder due to the improvement of its physical and mechanical and operational properties.1 cl, 1 tbl
Изобретение относится к промышленности строительных материалов и может быть использовано при изготовлении кислотоупорных бетонов и растворов на основе безобжигового вяжущего.Техническим результатом является повышение эффективности кислотоупорного вяжущего за счет улучшения его физико-механических и эксплуатационных свойств. Вяжущее вещество содержит реакционно-активный компонент, ускоритель твердения и щелочной активатор; согласно изобретению в качестве реакционно-активного компонента используют каолинитовую глину, активированную до удельной поверхности 640 м/кг и обожженную при температуре 600-650°C, которую смешивают с вулканическим туфом, высушенным перед измельчением при температуре 105°C в течение 2-х часов и измельченным до удельной поверхности 520 м/кг в присутствии ускорителя твердения «кремнефтористого натрия» и щелочного активатора на основе гидроксида натрия и жидкого стекла натриевого с силикатным модулем 2,8 и плотностью 1,24 г/смпри следующем соотношении компонентов, мас. %: метакаолин 26,8-61,2, вулканический туф 21,4-51,2, кремнефтористый натрий NaSiF5,8-8,0, жидкое стекло NaSiO11,0-13,0, гидроксид натрия NaOH 0,6-1,0. 1 табл.
BINDER
ВЯЖУЩЕЕ ВЕЩЕСТВО
MURTAZAEV SAJD-ALVI YUSUPOVICH (author) / SALAMANOVA MADINA SHAKHIDOVNA (author) / BATAEV DENA KARIM-SULTANOVICH (author) / NAKHAEV MAGOMED RAMZANOVICH (author)
2018-10-29
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME