CERAMIC MASS FOR THE MANUFACTURE OF FACADE TILES
FIELD: construction.SUBSTANCE: invention relates to the production of wall building materials and can be used for the manufacture of facade tiles. Specified technical result is achieved by introducing into the ceramic mass, including clay, titanium dioxide and boric acid, in addition to lithium carbonate in the following ratio, wt. %: low plastic clay 80.0; titanium dioxide 10.0; lithium carbonate 5.0; boric acid 5.0. Samples of wall ceramics were obtained at a moisture content of a ceramic mass of 8 wt. %, pressing pressure of 15 MPa and firing temperature 1,000 °C. When firing, titanium dioxide interacts with silicon and lithium oxides in the presence of boric acid to form a vitreous phase containing lithium titanates and increases the strength of the material in the bulk of the product and on its surface, creating the effect of self-glazing.EFFECT: increased compressive strength and frost resistance while maintaining other performance characteristics of products.1 cl, 5 ex, 1 tbl
Изобретение относится к области производства стеновых строительных материалов и может быть использовано для изготовления фасадных плиток. Технический результат: повышение прочности на сжатие и морозостойкости при сохранении других эксплуатационных характеристик изделий. Указанный технический результат достигается за счет введения в керамическую массу, включающую глину, диоксид титана и борную кислоту, дополнительно карбоната лития при следующем соотношении компонентов, мас. %: малопластичная глина 80,0; диоксид титана 10,0; карбонат лития 5,0; борная кислота 5,0. Образцы стеновой керамики получали при влажности керамической массы 8 мас. %, давлении прессования 15 МПа и температуре обжига 1000°C. Диоксид титана при проведении обжига взаимодействует с оксидами кремния и лития в присутствии борной кислоты с образованием стекловидной фазы, содержащей титанаты лития и повышающей прочность материала в объеме изделия и на его поверхности, создавая эффект самоглазурования. 5 пр., 1 табл.
CERAMIC MASS FOR THE MANUFACTURE OF FACADE TILES
FIELD: construction.SUBSTANCE: invention relates to the production of wall building materials and can be used for the manufacture of facade tiles. Specified technical result is achieved by introducing into the ceramic mass, including clay, titanium dioxide and boric acid, in addition to lithium carbonate in the following ratio, wt. %: low plastic clay 80.0; titanium dioxide 10.0; lithium carbonate 5.0; boric acid 5.0. Samples of wall ceramics were obtained at a moisture content of a ceramic mass of 8 wt. %, pressing pressure of 15 MPa and firing temperature 1,000 °C. When firing, titanium dioxide interacts with silicon and lithium oxides in the presence of boric acid to form a vitreous phase containing lithium titanates and increases the strength of the material in the bulk of the product and on its surface, creating the effect of self-glazing.EFFECT: increased compressive strength and frost resistance while maintaining other performance characteristics of products.1 cl, 5 ex, 1 tbl
Изобретение относится к области производства стеновых строительных материалов и может быть использовано для изготовления фасадных плиток. Технический результат: повышение прочности на сжатие и морозостойкости при сохранении других эксплуатационных характеристик изделий. Указанный технический результат достигается за счет введения в керамическую массу, включающую глину, диоксид титана и борную кислоту, дополнительно карбоната лития при следующем соотношении компонентов, мас. %: малопластичная глина 80,0; диоксид титана 10,0; карбонат лития 5,0; борная кислота 5,0. Образцы стеновой керамики получали при влажности керамической массы 8 мас. %, давлении прессования 15 МПа и температуре обжига 1000°C. Диоксид титана при проведении обжига взаимодействует с оксидами кремния и лития в присутствии борной кислоты с образованием стекловидной фазы, содержащей титанаты лития и повышающей прочность материала в объеме изделия и на его поверхности, создавая эффект самоглазурования. 5 пр., 1 табл.
CERAMIC MASS FOR THE MANUFACTURE OF FACADE TILES
Керамическая масса для изготовления фасадных плиток
SHAKHOVA VALERIYA NIKOLAEVNA (author) / PIKALOV EVGENIJ SERGEEVICH (author) / SELIVANOV OLEG GRIGOREVICH (author) / CHUKHLANOV VLADIMIR YUREVICH (author)
2018-11-19
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME