METHOD OF MAKING GLASS-CERAMIC ARTICLES OF LITHIUM ALUMINOSILICATE COMPOSITION
FIELD: manufacturing technology.SUBSTANCE: invention relates to production of large-size ceramic articles for radio engineering purposes. Method of making articles from glass-ceramic lithium-aluminosilicate composition involves grinding of pre-crystallized lithium-aluminosilicate glass by wet method to obtain a slurry with given parameters, preliminary molding in gypsum molds of workpieces of arbitrary shape, their repeated processing into a slurry, molding of articles and thermal treatment. Preliminary crystallization of lithium-aluminosilicate glass is carried out in containers of glass-ceramic lithium-aluminosilicate composition at rate of temperature rise of 200–300 °C/h first at nucleation temperature of 630–670 °C, and then at crystallization temperature of 1,170–1,250 °C for 6–12 hours, wherein glass layer in vessel does not exceed 200 mm.EFFECT: high efficiency of crystallization of the initial lithium aluminosilicate glass and high quality of the material.1 cl, 5 ex
Изобретение относится к производству крупногабаритных керамических изделий радиотехнического назначения. Технический результат - повышение производительности при кристаллизации исходного литийалюмосиликатного стекла и повышение качества материала. Способ изготовления изделий из стеклокерамики литийалюмосиликатного состава включает измельчение предварительно закристаллизованного литийалюмосиликатного стекла мокрым способом до получения шликера с заданными параметрами, предварительное формование в гипсовых формах заготовок произвольной формы, их повторную переработку в шликер, формование изделий и термообработку. Предварительную кристаллизацию литийалюмосиликатного стекла проводят в емкости из стеклокерамики литийалюмосиликатного состава при скорости подъема температуры 200-300°С/час сначала при температуре зародышеобразования 630-670°С, а затем при температуре кристаллизации 1170-1250°С в течение 6-12 ч, при этом слой стекла в емкости не превышает 200 мм. 5 пр.
METHOD OF MAKING GLASS-CERAMIC ARTICLES OF LITHIUM ALUMINOSILICATE COMPOSITION
FIELD: manufacturing technology.SUBSTANCE: invention relates to production of large-size ceramic articles for radio engineering purposes. Method of making articles from glass-ceramic lithium-aluminosilicate composition involves grinding of pre-crystallized lithium-aluminosilicate glass by wet method to obtain a slurry with given parameters, preliminary molding in gypsum molds of workpieces of arbitrary shape, their repeated processing into a slurry, molding of articles and thermal treatment. Preliminary crystallization of lithium-aluminosilicate glass is carried out in containers of glass-ceramic lithium-aluminosilicate composition at rate of temperature rise of 200–300 °C/h first at nucleation temperature of 630–670 °C, and then at crystallization temperature of 1,170–1,250 °C for 6–12 hours, wherein glass layer in vessel does not exceed 200 mm.EFFECT: high efficiency of crystallization of the initial lithium aluminosilicate glass and high quality of the material.1 cl, 5 ex
Изобретение относится к производству крупногабаритных керамических изделий радиотехнического назначения. Технический результат - повышение производительности при кристаллизации исходного литийалюмосиликатного стекла и повышение качества материала. Способ изготовления изделий из стеклокерамики литийалюмосиликатного состава включает измельчение предварительно закристаллизованного литийалюмосиликатного стекла мокрым способом до получения шликера с заданными параметрами, предварительное формование в гипсовых формах заготовок произвольной формы, их повторную переработку в шликер, формование изделий и термообработку. Предварительную кристаллизацию литийалюмосиликатного стекла проводят в емкости из стеклокерамики литийалюмосиликатного состава при скорости подъема температуры 200-300°С/час сначала при температуре зародышеобразования 630-670°С, а затем при температуре кристаллизации 1170-1250°С в течение 6-12 ч, при этом слой стекла в емкости не превышает 200 мм. 5 пр.
METHOD OF MAKING GLASS-CERAMIC ARTICLES OF LITHIUM ALUMINOSILICATE COMPOSITION
Способ изготовления изделий из стеклокерамики литийалюмосиликатного состава
KHARITONOV DMITRIJ VIKTOROVICH (author) / ANASHKINA ANTONINA ALEKSANDROVNA (author) / ANISIMOVA SVETLANA ANATOLEVNA (author) / RUSIN MIKHAIL YUREVICH (author) / KHAMITSAEV ANATOLIJ STEPANOVICH (author)
2019-11-28
Patent
Electronic Resource
Russian
METHOD FOR PRODUCING ARTICLES FROM GLASS-CERAMIC MATERIAL OF LITHIUM ALUMINOSILICATE COMPOSITION
| European Patent Office | 2022
| European Patent Office | 2015
Toughening mechanisms for a zirconia-lithium aluminosilicate glass-ceramic
| British Library Online Contents | 1995
Selective laser densification of lithium aluminosilicate glass ceramic tapes
| British Library Online Contents | 2013
| British Library Online Contents | 2010