HIGH-STRENGTH CONCRETE
FIELD: construction.SUBSTANCE: invention relates to construction materials and can be used for making articles from concrete in civil and industrial construction, as well as in production of special-purpose structures. Set task is achieved due to that high-strength concrete obtained from a mixture comprising Portland cement, sand, crushed stone, an additive and water, according to the invention sand contains sand with a fineness modulus of 2.2–3.2, as crushed stone granite or gravel fractions of 3–25 mm, additionally contains blast-furnace slag with specific surface area of at least 280 m/kg and pH value of pH=7–13, and also contains reactive filler consisting of metakaolin, finely-dispersed polymer based on allyl ether and maleic acid anhydrite and potassium nitrate in following ratio of components, wt%: metakaolin 43.0–49.0, finely dispersed polymer 43.0–47.0, potassium nitrate 8.0–10.0, with the following ratio of components, wt%: Portland cement 8.0–15.0, blast-furnace slag 3.0–6.0, sand 33.9–36.0, crushed stone 40.0–46.0, additive 0.6–1.0, reactive filler 0.5–0.8, water 2.0–5.0. As an additive, concrete contains a solution of polycarboxylate polymers modified with organic and inorganic substances, as well as nanodispersions of hydrated silicon dioxide.EFFECT: high crack resistance and high corrosion resistance of high-strength concrete with respect to sulphate and magnesia corrosion.1 cl, 2 tbl
Изобретение относится к строительным материалам и может быть использовано для изготовления изделий из бетона в гражданском и промышленном строительстве, а также при изготовлении сооружений специального назначения. Технический результат - повышение трещиностойкости и повышение коррозионной стойкости высокопрочного бетона относительно сульфатной и магнезиальной коррозии. Поставленная задача достигается тем, что высокопрочный бетон, полученный из смеси, включающей портландцемент, песок, щебень, добавку и воду, согласно изобретению в качестве песка содержит песок с модулем крупности 2,2-3,2, в качестве щебня содержит щебень гранитный или гравийный фракции 3-25 мм, дополнительно содержит доменный шлак с удельной поверхностью не менее 280 м/кг и значением водородного показателя рН=7-13, а также содержит реакционно-активный наполнитель, состоящий из метакаолина, тонкодисперсного полимера на основе эфира аллила и ангидрита малеиновой кислоты и нитрата калия при следующем соотношении компонентов, мас. %: метакаолин 43,0-49,0, тонкодисперсный полимер 43,0-47,0, нитрат калия 8,0-10,0, при следующем соотношении компонентов смеси, мас. %: портландцемент 8,0-15,0, доменный шлак 3,0-6,0, песок 33,9-36,0, щебень 40,0-46,0, добавка 0,6-1,0, реакционно-активный наполнитель 0,5-0,8, вода 2,0-5,0, В качестве добавки бетон содержит раствор поликарбоксилатных полимеров, модифицированных органическими и неорганическими веществами, а также нанодисперсиями гидратного диоксида кремния. 1 з.п. ф-лы, 2 табл.
HIGH-STRENGTH CONCRETE
FIELD: construction.SUBSTANCE: invention relates to construction materials and can be used for making articles from concrete in civil and industrial construction, as well as in production of special-purpose structures. Set task is achieved due to that high-strength concrete obtained from a mixture comprising Portland cement, sand, crushed stone, an additive and water, according to the invention sand contains sand with a fineness modulus of 2.2–3.2, as crushed stone granite or gravel fractions of 3–25 mm, additionally contains blast-furnace slag with specific surface area of at least 280 m/kg and pH value of pH=7–13, and also contains reactive filler consisting of metakaolin, finely-dispersed polymer based on allyl ether and maleic acid anhydrite and potassium nitrate in following ratio of components, wt%: metakaolin 43.0–49.0, finely dispersed polymer 43.0–47.0, potassium nitrate 8.0–10.0, with the following ratio of components, wt%: Portland cement 8.0–15.0, blast-furnace slag 3.0–6.0, sand 33.9–36.0, crushed stone 40.0–46.0, additive 0.6–1.0, reactive filler 0.5–0.8, water 2.0–5.0. As an additive, concrete contains a solution of polycarboxylate polymers modified with organic and inorganic substances, as well as nanodispersions of hydrated silicon dioxide.EFFECT: high crack resistance and high corrosion resistance of high-strength concrete with respect to sulphate and magnesia corrosion.1 cl, 2 tbl
Изобретение относится к строительным материалам и может быть использовано для изготовления изделий из бетона в гражданском и промышленном строительстве, а также при изготовлении сооружений специального назначения. Технический результат - повышение трещиностойкости и повышение коррозионной стойкости высокопрочного бетона относительно сульфатной и магнезиальной коррозии. Поставленная задача достигается тем, что высокопрочный бетон, полученный из смеси, включающей портландцемент, песок, щебень, добавку и воду, согласно изобретению в качестве песка содержит песок с модулем крупности 2,2-3,2, в качестве щебня содержит щебень гранитный или гравийный фракции 3-25 мм, дополнительно содержит доменный шлак с удельной поверхностью не менее 280 м/кг и значением водородного показателя рН=7-13, а также содержит реакционно-активный наполнитель, состоящий из метакаолина, тонкодисперсного полимера на основе эфира аллила и ангидрита малеиновой кислоты и нитрата калия при следующем соотношении компонентов, мас. %: метакаолин 43,0-49,0, тонкодисперсный полимер 43,0-47,0, нитрат калия 8,0-10,0, при следующем соотношении компонентов смеси, мас. %: портландцемент 8,0-15,0, доменный шлак 3,0-6,0, песок 33,9-36,0, щебень 40,0-46,0, добавка 0,6-1,0, реакционно-активный наполнитель 0,5-0,8, вода 2,0-5,0, В качестве добавки бетон содержит раствор поликарбоксилатных полимеров, модифицированных органическими и неорганическими веществами, а также нанодисперсиями гидратного диоксида кремния. 1 з.п. ф-лы, 2 табл.
HIGH-STRENGTH CONCRETE
Высокопрочный бетон
MITYUKOVA ELENA VALENTINOVNA (author) / VOLOKHOV SERGEJ VADIMOVICH (author) / SOLOVEVA VALENTINA YAKOVLEVNA (author) / GUNIN SERGEJ OLIMPIEVICH (author)
2020-07-28
Patent