GRAPHITE-CONTAINING REFRACTORY MATERIAL AND METHOD OF PRODUCING GRAPHITE-CONTAINING REFRACTORY MATERIAL
FIELD: chemistry.SUBSTANCE: graphite-containing refractory material contains magnesia refractory filler or refractory filler based on aluminium oxide and silicon carbide, as well as graphite in amount from 1 % to 80 % by weight and multiple bundles of carbon fibres. Each bundle consists of 1000 to 300,000 carbon fibres with diameter in range of 1 to 45 mcm/fibre bonded with binder. Carbon fibre bundle has length of 100 mm or more. End surface of each bundle of carbon fibres has flattened shape, at which width of end surface of bundle of carbon fibres is more than its width. Fibre bundles are located inside graphite-containing fire-resistant material so that longitudinal direction of end surfaces of bundles is identical, and angle between compression surface and longitudinal direction of each end surface makes 45 to 135°.EFFECT: disclosed is graphite-containing refractory material having high bending strength and breaking energy compared to known refractory materials, and a method of producing said refractory material.19 cl, 85 ex, 16 tbl, 13 dwg
Предложен графитсодержащий огнеупорный материал, обладающий повышенной прочностью при изгибе и энергией разрушения по сравнению с известными огнеупорными материалами, и способ получения этого огнеупорного материала. Графитсодержащий огнеупорный материал содержит магнезиальный огнеупорный наполнитель или огнеупорный наполнитель на основе оксида алюминия и карбида кремния, а также графит в количестве от 1% до 80% по массе и множество пучков углеродных волокон. Каждый пучок состоит из от 1000 до 300000 углеродных волокон с диаметром в диапазоне от 1 до 45 мкм/волокно, скреплённых связующим. Пучок углеродных волокон имеет длину 100 мм или больше. Торцевая поверхность каждого пучка углеродных волокон имеет уплощённую форму, при которой ширина торцевой поверхности пучка углеродных волокон больше её ширины. Пучки волокон расположены внутри графитсодержащего огнеупорного материала так, что продольное направление торцевых поверхностей пучков является одинаковым, а угол между поверхностью сжатия и продольным направлением каждой торцевой поверхности составляет от 45 до 135°. 4 н. и 15 з.п. ф-лы, 85 пр., 16 табл. и 13 ил.
GRAPHITE-CONTAINING REFRACTORY MATERIAL AND METHOD OF PRODUCING GRAPHITE-CONTAINING REFRACTORY MATERIAL
FIELD: chemistry.SUBSTANCE: graphite-containing refractory material contains magnesia refractory filler or refractory filler based on aluminium oxide and silicon carbide, as well as graphite in amount from 1 % to 80 % by weight and multiple bundles of carbon fibres. Each bundle consists of 1000 to 300,000 carbon fibres with diameter in range of 1 to 45 mcm/fibre bonded with binder. Carbon fibre bundle has length of 100 mm or more. End surface of each bundle of carbon fibres has flattened shape, at which width of end surface of bundle of carbon fibres is more than its width. Fibre bundles are located inside graphite-containing fire-resistant material so that longitudinal direction of end surfaces of bundles is identical, and angle between compression surface and longitudinal direction of each end surface makes 45 to 135°.EFFECT: disclosed is graphite-containing refractory material having high bending strength and breaking energy compared to known refractory materials, and a method of producing said refractory material.19 cl, 85 ex, 16 tbl, 13 dwg
Предложен графитсодержащий огнеупорный материал, обладающий повышенной прочностью при изгибе и энергией разрушения по сравнению с известными огнеупорными материалами, и способ получения этого огнеупорного материала. Графитсодержащий огнеупорный материал содержит магнезиальный огнеупорный наполнитель или огнеупорный наполнитель на основе оксида алюминия и карбида кремния, а также графит в количестве от 1% до 80% по массе и множество пучков углеродных волокон. Каждый пучок состоит из от 1000 до 300000 углеродных волокон с диаметром в диапазоне от 1 до 45 мкм/волокно, скреплённых связующим. Пучок углеродных волокон имеет длину 100 мм или больше. Торцевая поверхность каждого пучка углеродных волокон имеет уплощённую форму, при которой ширина торцевой поверхности пучка углеродных волокон больше её ширины. Пучки волокон расположены внутри графитсодержащего огнеупорного материала так, что продольное направление торцевых поверхностей пучков является одинаковым, а угол между поверхностью сжатия и продольным направлением каждой торцевой поверхности составляет от 45 до 135°. 4 н. и 15 з.п. ф-лы, 85 пр., 16 табл. и 13 ил.
GRAPHITE-CONTAINING REFRACTORY MATERIAL AND METHOD OF PRODUCING GRAPHITE-CONTAINING REFRACTORY MATERIAL
ГРАФИТСОДЕРЖАЩИЙ ОГНЕУПОРНЫЙ МАТЕРИАЛ И СПОСОБ ПОЛУЧЕНИЯ ГРАФИТСОДЕРЖАЩЕГО ОГНЕУПОРНОГО МАТЕРИАЛА
YOSHIDA KEISUKE (author) / MATSUNAGA HISAHIRO (author) / HAMA YOICHIRO (author)
2020-08-25
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
Graphite-containing refractory and method of producing graphite-containing refractory
| European Patent Office | 2021
GRAPHITE-CONTAINING REFRACTORY AND METHOD OF PRODUCING GRAPHITE-CONTAINING REFRACTORY
| European Patent Office | 2021
GRAPHITE-CONTAINING REFRACTORY AND METHOD OF PRODUCING GRAPHITE-CONTAINING REFRACTORY
| European Patent Office | 2019
Graphite-containing refractory and method of producing graphite-containing refractory
| European Patent Office | 2023