HEAT-RESISTANT SLAG-LINTERING CONCRETE
FIELD: construction.SUBSTANCE: invention relates to production of construction materials and can be used in making lining of units operating under high temperatures and high cyclicity. Heat-resistant slag-alkaline concrete produced from concrete mixture, containing chamotte of 5–10 mm fraction, chamotte of less than 5 mm fraction, self-breaking ferrochrome slag, sodium hydroxide, portland cement and water, where the mixture additionally contains slag of metal chromium of 5–10 mm fraction, slag of metal chromium of fraction less than 5 mm and metakaolin in following ratio of components, wt%: chamotte of fraction 5–10 mm - 15.0, chamotte of fraction less than 5 mm - 16.0, slag of metal chromium of fraction 5–10 mm - 15.0, slag of metal chromium of fraction less than 5 mm - 15.5, self-breaking ferrochrome slag - 23.5, caustic soda - 2.5, portland cement - 1.0, metakaolin - 0.5, water - 11.0.EFFECT: technical result is provision of application temperature of more than 1400 °C with preservation of strength characteristics.1 cl, 3 tbl
Изобретение относится к производству строительных материалов и может быть использовано при изготовлении футеровок агрегатов, работающих в условиях высоких температур и повышенной цикличности. Технический результат - обеспечение температуры применения более 1400 град С при сохранении прочностных характеристик. Жаростойкий шлакощелочной бетон, полученный из бетонной смеси, содержащей шамот фракции 5-10 мм, шамот фракции менее 5 мм, самораспадающийся феррохромовый шлак, едкий натр, портландцемент и воду, где смесь дополнительно содержит шлак металлического хрома фракции 5-10 мм, шлак металлического хрома фракции менее 5 мм и метакаолин в следующем соотношении компонентов, мас.%: шамот фракции 5-10 мм – 15,0, шамот фракции менее 5 мм - 16,0, шлак металлического хрома фракции 5-10 мм - 15,0, шлак металлического хрома фракции менее 5 мм - 15,5, самораспадающийся феррохромовый шлак - 23,5, едкий натр - 2,5, портландцемент - 1,0, метакаолин - 0,5, вода - 11,0. 3 табл.
HEAT-RESISTANT SLAG-LINTERING CONCRETE
FIELD: construction.SUBSTANCE: invention relates to production of construction materials and can be used in making lining of units operating under high temperatures and high cyclicity. Heat-resistant slag-alkaline concrete produced from concrete mixture, containing chamotte of 5–10 mm fraction, chamotte of less than 5 mm fraction, self-breaking ferrochrome slag, sodium hydroxide, portland cement and water, where the mixture additionally contains slag of metal chromium of 5–10 mm fraction, slag of metal chromium of fraction less than 5 mm and metakaolin in following ratio of components, wt%: chamotte of fraction 5–10 mm - 15.0, chamotte of fraction less than 5 mm - 16.0, slag of metal chromium of fraction 5–10 mm - 15.0, slag of metal chromium of fraction less than 5 mm - 15.5, self-breaking ferrochrome slag - 23.5, caustic soda - 2.5, portland cement - 1.0, metakaolin - 0.5, water - 11.0.EFFECT: technical result is provision of application temperature of more than 1400 °C with preservation of strength characteristics.1 cl, 3 tbl
Изобретение относится к производству строительных материалов и может быть использовано при изготовлении футеровок агрегатов, работающих в условиях высоких температур и повышенной цикличности. Технический результат - обеспечение температуры применения более 1400 град С при сохранении прочностных характеристик. Жаростойкий шлакощелочной бетон, полученный из бетонной смеси, содержащей шамот фракции 5-10 мм, шамот фракции менее 5 мм, самораспадающийся феррохромовый шлак, едкий натр, портландцемент и воду, где смесь дополнительно содержит шлак металлического хрома фракции 5-10 мм, шлак металлического хрома фракции менее 5 мм и метакаолин в следующем соотношении компонентов, мас.%: шамот фракции 5-10 мм – 15,0, шамот фракции менее 5 мм - 16,0, шлак металлического хрома фракции 5-10 мм - 15,0, шлак металлического хрома фракции менее 5 мм - 15,5, самораспадающийся феррохромовый шлак - 23,5, едкий натр - 2,5, портландцемент - 1,0, метакаолин - 0,5, вода - 11,0. 3 табл.
HEAT-RESISTANT SLAG-LINTERING CONCRETE
Жаростойкий шлакощелочной бетон
AKHTYAMOV RUSLAN RASHIDOVICH (author) / BOGUSEVICH DMITRIJ VLADIMIROVICH (author)
2020-09-08
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
Development of Heat-resistant Concrete with Ferro-nickel Slag
| British Library Conference Proceedings | 1998
Manufacture technology for heat-resistant mineral-slag aerated concrete brick
| European Patent Office | 2015
| European Patent Office | 2024