CERAMIC MIXTURE FOR MAKING PORCELAIN STONEWARE
FIELD: industry of ceramic materials.SUBSTANCE: ceramic mixture for making porcelain stoneware contains, wt. %: kaolin clay 30–50; feldspar concentrate 40–50; alumino-alkaline sludge obtained during treatment of effluents from production of ethyl- and isopropylbenzene, 10–20. Used kaolin clay has chemical composition, wt. %: SiO259.10; Al2O324.70; Fe2O31.80; CaO 1.90; MgO 0.86; R2O 1.30; p.o.i. (percentage of other impurities) 10.34. Feldspar concentrate has chemical composition, wt. %: SiO269.82; Al2O317.24; Fe2O30.18; CaO 0.54; MgO 0.44; R2O 11.41; p.o.i. 0.37. Said alumino-alkaline sludge has chemical composition, wt. %: SiO25.2; Al2O360.1; Fe2O31.0; CaO 4.4; MgO 4.2; R2O 19.8; p.o.i. 5.3.EFFECT: increased ultimate bending strength, recycling of industrial wastes, wider raw material base for ceramic materials.1 cl, 3 tbl
Изобретение относится к промышленности керамических материалов. Технический результат - повышение предела прочности при изгибе, утилизация промышленных отходов, расширение сырьевой базы для керамических материалов. Керамическая масса для изготовления керамогранита включает, мас.%: каолиновую глину 30-50; полевошпатовый концентрат 40-50; алюмощелочной шлам, получаемый при очистке стоков производств этил- и изопропилбензола, 10-20. Используемая каолиновая глина имеет химический состав, мас.%: SiO259,10; Al2O324,70; Fe2O31,80; CaO 1,90; MgO 0,86 R2O 1,30; п.п.п. 10,34. Полевошпатовый концентрат имеет химический состав, мас.%: SiO269,82; Al2O317,24; Fe2O30,18; CaO 0,54; MgO 0,44; R2O 11,41; п.п.п. 0,37. Указанный алюмощелочной шлам имеет химический состав, мас.%: SiO25,2, Al2O360,1; Fe2O31,0; CaO 4,4; MgO 4,2; R2O 19,8; п.п.п. 5,3. 3 табл.
CERAMIC MIXTURE FOR MAKING PORCELAIN STONEWARE
FIELD: industry of ceramic materials.SUBSTANCE: ceramic mixture for making porcelain stoneware contains, wt. %: kaolin clay 30–50; feldspar concentrate 40–50; alumino-alkaline sludge obtained during treatment of effluents from production of ethyl- and isopropylbenzene, 10–20. Used kaolin clay has chemical composition, wt. %: SiO259.10; Al2O324.70; Fe2O31.80; CaO 1.90; MgO 0.86; R2O 1.30; p.o.i. (percentage of other impurities) 10.34. Feldspar concentrate has chemical composition, wt. %: SiO269.82; Al2O317.24; Fe2O30.18; CaO 0.54; MgO 0.44; R2O 11.41; p.o.i. 0.37. Said alumino-alkaline sludge has chemical composition, wt. %: SiO25.2; Al2O360.1; Fe2O31.0; CaO 4.4; MgO 4.2; R2O 19.8; p.o.i. 5.3.EFFECT: increased ultimate bending strength, recycling of industrial wastes, wider raw material base for ceramic materials.1 cl, 3 tbl
Изобретение относится к промышленности керамических материалов. Технический результат - повышение предела прочности при изгибе, утилизация промышленных отходов, расширение сырьевой базы для керамических материалов. Керамическая масса для изготовления керамогранита включает, мас.%: каолиновую глину 30-50; полевошпатовый концентрат 40-50; алюмощелочной шлам, получаемый при очистке стоков производств этил- и изопропилбензола, 10-20. Используемая каолиновая глина имеет химический состав, мас.%: SiO259,10; Al2O324,70; Fe2O31,80; CaO 1,90; MgO 0,86 R2O 1,30; п.п.п. 10,34. Полевошпатовый концентрат имеет химический состав, мас.%: SiO269,82; Al2O317,24; Fe2O30,18; CaO 0,54; MgO 0,44; R2O 11,41; п.п.п. 0,37. Указанный алюмощелочной шлам имеет химический состав, мас.%: SiO25,2, Al2O360,1; Fe2O31,0; CaO 4,4; MgO 4,2; R2O 19,8; п.п.п. 5,3. 3 табл.
CERAMIC MIXTURE FOR MAKING PORCELAIN STONEWARE
КЕРАМИЧЕСКАЯ МАССА ДЛЯ ИЗГОТОВЛЕНИЯ КЕРАМОГРАНИТА
ABDRAKHIMOV VLADIMIR ZAKIROVICH (author)
2022-03-25
Patent
Electronic Resource
Russian