Ceria-zirconia composite oxide, method for producing the same, and catalyst for purifying exhaust gas using the ceria-zirconia composite oxide
A ceria-zirconia composite oxide includes at least one of lanthanum, yttrium, and praseodymium. A rate of a total content of the at least one rare earth element to a total content of cerium and zirconium is 0.1 at % to 4.0 at %. A content of the rare earth element present in near-surface regions, which are at a distance of less than 50 nm from surfaces of primary particles of the ceria-zirconia composite oxide, accounts for 90 at % or more of the total content of the rare earth element. An average particle size of the primary particles of the ceria-zirconia composite oxide is 2.2 μm to 4.5 μm. After a predetermined durability test, the intensity ratio I(14/29) of a diffraction line at 2θ=14.5° to a diffraction line at 2θ=29° and the intensity ratio I(28/29) of a diffraction line at 2θ=28.5° to the diffraction line at 2θ=29° respectively satisfy the following conditions: I(14/29)≧0.02, and I(28/29)≦0.08.
Ceria-zirconia composite oxide, method for producing the same, and catalyst for purifying exhaust gas using the ceria-zirconia composite oxide
A ceria-zirconia composite oxide includes at least one of lanthanum, yttrium, and praseodymium. A rate of a total content of the at least one rare earth element to a total content of cerium and zirconium is 0.1 at % to 4.0 at %. A content of the rare earth element present in near-surface regions, which are at a distance of less than 50 nm from surfaces of primary particles of the ceria-zirconia composite oxide, accounts for 90 at % or more of the total content of the rare earth element. An average particle size of the primary particles of the ceria-zirconia composite oxide is 2.2 μm to 4.5 μm. After a predetermined durability test, the intensity ratio I(14/29) of a diffraction line at 2θ=14.5° to a diffraction line at 2θ=29° and the intensity ratio I(28/29) of a diffraction line at 2θ=28.5° to the diffraction line at 2θ=29° respectively satisfy the following conditions: I(14/29)≧0.02, and I(28/29)≦0.08.
Ceria-zirconia composite oxide, method for producing the same, and catalyst for purifying exhaust gas using the ceria-zirconia composite oxide
MORIKAWA AKIRA (author) / KONISHI KAE (author) / TANABE TOSHITAKA (author) / SUDA AKIHIKO (author) / MIURA MASAHIDE (author) / CHINZEI ISAO (author) / SUZUKI HIROMASA (author) / CHIBA AKIYA (author) / IIZUKA KOSUKE (author)
2018-10-30
Patent
Electronic Resource
English
IPC:
B01J
Chemische oder physikalische Verfahren, z.B. Katalyse oder Kolloidchemie
,
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY
/
B01D
SEPARATION
,
Trennen
/
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
/
C01G
Verbindungen der von den Unterklassen C01D oder C01F nicht umfassten Metalle
,
COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
/
C04B
Kalk
,
LIME
| European Patent Office | 2021
| European Patent Office | 2022
| European Patent Office | 2018
| European Patent Office | 2018
| European Patent Office | 2016