Method for manufacturing plate-like alumina powder and plate-like alumina powder
96 parts by mass of a γ-alumina powder, 4 parts by mass of a an AlF3 powder, and 0.17 parts by mass of an α-alumina powder as a seed crystal were mixed by a pot mill. The purities of each raw material were evaluated, and it was found that the mass ratio of each impurity element other than Al, O, F, H, C, and S was 10 ppm or less. In a high-purity alumina-made sagger having a purity of 99.9 percent by mass, 300 g of the obtained mixed powder was received, and after a high-purity alumina-made lid having a purity of 99.9 percent by mass was placed on the sagger, a heat treatment was perforated at 900° C. for 3 hours in an electric furnace in an air flow atmosphere, so that an alumina powder was obtained. The value of AlF3 mass/container volume was 0.016 g/cm3.
Method for manufacturing plate-like alumina powder and plate-like alumina powder
96 parts by mass of a γ-alumina powder, 4 parts by mass of a an AlF3 powder, and 0.17 parts by mass of an α-alumina powder as a seed crystal were mixed by a pot mill. The purities of each raw material were evaluated, and it was found that the mass ratio of each impurity element other than Al, O, F, H, C, and S was 10 ppm or less. In a high-purity alumina-made sagger having a purity of 99.9 percent by mass, 300 g of the obtained mixed powder was received, and after a high-purity alumina-made lid having a purity of 99.9 percent by mass was placed on the sagger, a heat treatment was perforated at 900° C. for 3 hours in an electric furnace in an air flow atmosphere, so that an alumina powder was obtained. The value of AlF3 mass/container volume was 0.016 g/cm3.
Method for manufacturing plate-like alumina powder and plate-like alumina powder
WATANABE MORIMICHI (author) / FUKUI HIROSHI (author) / SATO KEI (author) / NANATAKI TSUTOMU (author)
2019-07-09
Patent
Electronic Resource
English
IPC:
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
/
C04B
Kalk
,
LIME
/
C30B
SINGLE-CRYSTAL GROWTH
,
Züchten von Einkristallen
PLATE-LIKE ALUMINA PARTICLE AND METHOD FOR MANUFACTURING PLATE-LIKE ALUMINA PARTICLE
| European Patent Office | 2024
PLATE-LIKE ALUMINA PARTICLE AND METHOD FOR MANUFACTURING PLATE-LIKE ALUMINA PARTICLE
| European Patent Office | 2023
PLATE-LIKE ALUMINA PARTICLE AND METHOD FOR MANUFACTURING PLATE-LIKE ALUMINA PARTICLE
| European Patent Office | 2023
PLATE-LIKE ALUMINA PARTICLE AND METHOD FOR MANUFACTURING PLATE-LIKE ALUMINA PARTICLE
| European Patent Office | 2021