CUBIC BORON NITRIDE SINTERED BODY CUTTING TOOL
In a cBN sintered body cutting tool having a sintered body including cBN grains and a binder phase as the tool base body therefor, the sintered body contains at least 40 capacity% but less than 60 capacity% cBN grains, a minimum of 2% by mass of Al, and a maximum within a range that fulfils the relationship Y = -0.1 X + 10, when Y is the Al content ratio (capacity %) and X is the cBN content ratio (% by mass). The binder phase contains at least a Ti-based compound, Al2O3, and unavoidable impurities. Al2O3 that has a diameter of 10-100 nm, among said Al2O3, is dispersed and generated within the binder phase and at least 30 Al2O3 being generated within a 1 µm × 1µm cross-sectional area of the binder phase.
La présente invention concerne un outil de coupe à corps fritté en cBN possédant un corps fritté comprenant des grains de cBN et une phase liante, utilisé comme corps de base d'outil associé, le corps fritté contenant au moins 40 % en capacité mais moins de 60 % en capacité de grains de cBN, un minimum de 2 % en masse d'Al et un maximum situé d'une plage qui satisfait à la relation Y = - 0,1 X + 10, Y représentant la proportion en Al (% en capacité) et X représentant la proportion en cBN (% en masse). La phase liante contient au moins un composé à base de Ti, de l'Al2O3 et des impuretés inévitables. L'Al2O3 présentant un diamètre de 10 à 100 nm, parmi ledit Al2O3 est dispersé et généré à l'intérieur de la phase liante et au moins 30 Al2O3 sont générés à l'intérieur d'une section transversale de 1 µm × 1 µm de la phase liante.
ｃＢＮ粒子と結合相とを含む焼結体を工具基体とするｃＢＮ焼結体切削工具において、前記焼結体は、ｃＢＮ粒子を４０容量％以上６０容量％未満およびＡｌが下限値で２質量％、上限値でＹをＡｌ含有割合（容量％）、ＸをｃＢＮ含有割合（質量％）としたとき、Ｙ＝－０．１Ｘ＋１０の関係を満足する範囲となるように含有し、前記結合相は、少なくともＴｉ系化合物とＡｌ２Ｏ３と不可避不純物を含有し、前記Ａｌ２Ｏ３のうち、直径１０ｎｍ～１００ｎｍの微粒Ａｌ２Ｏ３が結合相中に分散、生成しており、前記結合相の断面１μｍ×１μｍの領域において、前記微粒Ａｌ２Ｏ３が３０個以上生成している。
CUBIC BORON NITRIDE SINTERED BODY CUTTING TOOL
In a cBN sintered body cutting tool having a sintered body including cBN grains and a binder phase as the tool base body therefor, the sintered body contains at least 40 capacity% but less than 60 capacity% cBN grains, a minimum of 2% by mass of Al, and a maximum within a range that fulfils the relationship Y = -0.1 X + 10, when Y is the Al content ratio (capacity %) and X is the cBN content ratio (% by mass). The binder phase contains at least a Ti-based compound, Al2O3, and unavoidable impurities. Al2O3 that has a diameter of 10-100 nm, among said Al2O3, is dispersed and generated within the binder phase and at least 30 Al2O3 being generated within a 1 µm × 1µm cross-sectional area of the binder phase.
La présente invention concerne un outil de coupe à corps fritté en cBN possédant un corps fritté comprenant des grains de cBN et une phase liante, utilisé comme corps de base d'outil associé, le corps fritté contenant au moins 40 % en capacité mais moins de 60 % en capacité de grains de cBN, un minimum de 2 % en masse d'Al et un maximum situé d'une plage qui satisfait à la relation Y = - 0,1 X + 10, Y représentant la proportion en Al (% en capacité) et X représentant la proportion en cBN (% en masse). La phase liante contient au moins un composé à base de Ti, de l'Al2O3 et des impuretés inévitables. L'Al2O3 présentant un diamètre de 10 à 100 nm, parmi ledit Al2O3 est dispersé et généré à l'intérieur de la phase liante et au moins 30 Al2O3 sont générés à l'intérieur d'une section transversale de 1 µm × 1 µm de la phase liante.
ｃＢＮ粒子と結合相とを含む焼結体を工具基体とするｃＢＮ焼結体切削工具において、前記焼結体は、ｃＢＮ粒子を４０容量％以上６０容量％未満およびＡｌが下限値で２質量％、上限値でＹをＡｌ含有割合（容量％）、ＸをｃＢＮ含有割合（質量％）としたとき、Ｙ＝－０．１Ｘ＋１０の関係を満足する範囲となるように含有し、前記結合相は、少なくともＴｉ系化合物とＡｌ２Ｏ３と不可避不純物を含有し、前記Ａｌ２Ｏ３のうち、直径１０ｎｍ～１００ｎｍの微粒Ａｌ２Ｏ３が結合相中に分散、生成しており、前記結合相の断面１μｍ×１μｍの領域において、前記微粒Ａｌ２Ｏ３が３０個以上生成している。
CUBIC BORON NITRIDE SINTERED BODY CUTTING TOOL
OUTIL DE COUPE À CORPS FRITTÉ EN NITRURE DE BORE CUBIQUE
立方晶窒化硼素焼結体切削工具
YUMOTO KENJI (author) / MIYASHITA YOSUKE (author)
2015-10-01
Patent
Electronic Resource
Japanese
| European Patent Office | 2017