SURFACE-COATED BORON NITRIDE SINTERED COMPACT TOOL
In a surface-coated boron nitride sintered compact tool according to the present invention, at least a cutting blade portion includes a compound sintered compact and a coating layer provided on a surface of the compound sintered compact. The compound sintered compact includes cubic boron nitride particles and binder particles. The compound sintered compact includes the cubic boron nitride particles in a ratio of 45 vol% to 80 vol%. A first particle size distribution curve of the cubic boron nitride particles has one or more peaks in the particle diameter range of 0.1 µm to 0.7 µm. A second particle size distribution curve of the cubic boron nitride particles has a first peak having a maximum peak height in the particle diameter range of 2.0 µm to 7.0 µm. In the second particle size distribution curve, the integral value ratio (Io/It × 100) is 1 to 20, where Io represents the integral value in the particle diameter range of 0.1 µm to 0.7 µm, and It represents the integral value for the entire range.
La présente invention porte sur un outil compact fritté en nitrure de bore à surface revêtue, dans lequel outil au moins une partie de lame de coupe comprend un corps compact fritté composite et une couche de revêtement disposée sur une surface du corps compact fritté composite. Le corps compact fritté composite comprend des particules de nitrure de bore cubiques et des particules de liant. Le corps compact fritté composite comprend les particules de nitrure de bore cubiques sous un rapport de 45 % en volume à 80 % en volume. Une première courbe de répartition de tailles de particules des particules en nitrure de bore cubiques a un ou plusieurs pics dans la plage de diamètre de particules de 0,1 µm à 0,7 µm. Une seconde courbe de répartition de tailles de particules des particules en nitrure de bore cubiques a un premier pic ayant une hauteur de pic maximale dans la plage de diamètre de particules de 2,0 µm à 7,0 µm. Dans la seconde courbe de répartition de tailles de particules, le rapport de valeur intégrée (Io/It × 100) est de 1 à 20, Io représentant la valeur intégrée dans la plage de diamètre de particules de 0,1 µm à 0,7 µm, et It représentant la valeur intégrée pour la totalité de la plage.
表面被覆窒化硼素焼結体工具は、少なくとも切れ刃部分が複合焼結体と複合焼結体の表面上に設けられた被覆層とを含む。複合焼結体は、立方晶窒化硼素粒子と結合材粒子とを含む。立方晶窒化硼素粒子は、複合焼結体に４５体積％以上８０体積％以下含まれている。立方晶窒化硼素粒子の第１粒度分布曲線は、粒径が０．１μｍ以上０．７μｍ以下である範囲に１つ以上のピークを有する。立方晶窒化硼素粒子の第２粒度分布曲線は、粒径が２．０μｍ以上７．０μｍ以下である範囲にピーク高さが最大である第１ピークを有する。第２粒度分布曲線において、粒径が０．１μｍ以上０．７μｍ以下である範囲の積分値をＩoと表し、全範囲の積分値をＩtと表した場合、積分値比（Ｉo／Ｉt×１００）は、１以上２０以下である。
SURFACE-COATED BORON NITRIDE SINTERED COMPACT TOOL
In a surface-coated boron nitride sintered compact tool according to the present invention, at least a cutting blade portion includes a compound sintered compact and a coating layer provided on a surface of the compound sintered compact. The compound sintered compact includes cubic boron nitride particles and binder particles. The compound sintered compact includes the cubic boron nitride particles in a ratio of 45 vol% to 80 vol%. A first particle size distribution curve of the cubic boron nitride particles has one or more peaks in the particle diameter range of 0.1 µm to 0.7 µm. A second particle size distribution curve of the cubic boron nitride particles has a first peak having a maximum peak height in the particle diameter range of 2.0 µm to 7.0 µm. In the second particle size distribution curve, the integral value ratio (Io/It × 100) is 1 to 20, where Io represents the integral value in the particle diameter range of 0.1 µm to 0.7 µm, and It represents the integral value for the entire range.
La présente invention porte sur un outil compact fritté en nitrure de bore à surface revêtue, dans lequel outil au moins une partie de lame de coupe comprend un corps compact fritté composite et une couche de revêtement disposée sur une surface du corps compact fritté composite. Le corps compact fritté composite comprend des particules de nitrure de bore cubiques et des particules de liant. Le corps compact fritté composite comprend les particules de nitrure de bore cubiques sous un rapport de 45 % en volume à 80 % en volume. Une première courbe de répartition de tailles de particules des particules en nitrure de bore cubiques a un ou plusieurs pics dans la plage de diamètre de particules de 0,1 µm à 0,7 µm. Une seconde courbe de répartition de tailles de particules des particules en nitrure de bore cubiques a un premier pic ayant une hauteur de pic maximale dans la plage de diamètre de particules de 2,0 µm à 7,0 µm. Dans la seconde courbe de répartition de tailles de particules, le rapport de valeur intégrée (Io/It × 100) est de 1 à 20, Io représentant la valeur intégrée dans la plage de diamètre de particules de 0,1 µm à 0,7 µm, et It représentant la valeur intégrée pour la totalité de la plage.
表面被覆窒化硼素焼結体工具は、少なくとも切れ刃部分が複合焼結体と複合焼結体の表面上に設けられた被覆層とを含む。複合焼結体は、立方晶窒化硼素粒子と結合材粒子とを含む。立方晶窒化硼素粒子は、複合焼結体に４５体積％以上８０体積％以下含まれている。立方晶窒化硼素粒子の第１粒度分布曲線は、粒径が０．１μｍ以上０．７μｍ以下である範囲に１つ以上のピークを有する。立方晶窒化硼素粒子の第２粒度分布曲線は、粒径が２．０μｍ以上７．０μｍ以下である範囲にピーク高さが最大である第１ピークを有する。第２粒度分布曲線において、粒径が０．１μｍ以上０．７μｍ以下である範囲の積分値をＩoと表し、全範囲の積分値をＩtと表した場合、積分値比（Ｉo／Ｉt×１００）は、１以上２０以下である。
SURFACE-COATED BORON NITRIDE SINTERED COMPACT TOOL
OUTIL COMPACT FRITTÉ EN NITRURE DE BORE À SURFACE REVÊTUE
表面被覆窒化硼素焼結体工具
MATSUDA YUSUKE (author) / OKAMURA KATSUMI (author) / SANO KENTA (author) / TSUKIHARA NOZOMI (author) / SETOYAMA MAKOTO (author)
2015-10-29
Patent
Electronic Resource
Japanese
COMPOSITE SINTERED COMPACT AND SURFACE-COATED BORON NITRIDE SINTERED COMPACT TOOL
| European Patent Office | 2016