ALUMINA-ZIRCONIA-SILICA FUSED-CAST REFRACTORY MATERIAL, GLASS FURNACE, AND METHOD FOR PRODUCING SHEET GLASS
Provided are: an alumina-zirconia-silica fused-cast refractory material suitable as a refractory material for glass production apparatuses, and which suppresses the exudation of glass components from the refractory material; and a glass furnace using same. An alumina-zirconia-silica fused-cast refractory material containing, as essential components, Al2O3, ZrO2, SiO2 and Na2O, in mass percentage in oxide equivalent, 20.0% ≤ Al2O3 ≤ 70.0%, 10.0% ≤ ZrO2 < 41.5%, 3.8% ≤ SiO2 ≤ 18.0%, 1.3% ≤ Na2O ≤ 15.0%, where Al2O3/SiO2 < 6.5, 0.20 ≤ Na2O/SiO2, and the total amount of the abovementioned essential components is at least 85%.
L'invention concerne : un matériau réfractaire, coulé par fusion, à base d'alumine-zircone-silice approprié en tant que matériau réfractaire pour des appareils de production de verre et qui supprime l'exsudation de constituants de verre du matériau réfractaire ; et un four de verrerie l'utilisant. L'invention concerne un matériau réfractaire, coulé par fusion, à base d'alumine-zircone-silice, contenant, en tant que constituants essentiels, Al2O3, ZrO2, SiO2 et Na2O, en des pourcentages en masse, en équivalent d'oxyde, 20,0 % ≤ Al2O3 ≤ 70,0 %, 10,0 % ≤ ZrO2 < 41,5 %, 3,8 % ≤ SiO2 ≤ 18,0 %, 1,3 % ≤ Na2O ≤ 15,0 %, où Al2O3/SiO2 < 6,5, 0,20 ≤ Na2O/SiO2, et la quantité totale des constituants essentiels mentionnés ci-dessus étant d'au moins 85 %.
耐火物からのガラス質成分の滲出を抑制し、ガラス製造装置用の耐火物として好適なアルミナ・ジルコニア・シリカ質溶融鋳造耐火物およびそれを用いたガラス溶融窯を提供する。必須成分としてＡｌ２Ｏ３、ＺｒＯ２、ＳｉＯ２およびＮａ２Ｏを含むアルミナ・ジルコニア・シリカ質溶融鋳造耐火物であって、酸化物基準の質量パーセンテージで、２０．０％≦Ａｌ２Ｏ３≦７０．０％、１０．０％≦ＺｒＯ２＜４１．５％、３．８％≦ＳｉＯ２≦１８．０％、１．３％≦Ｎａ２Ｏ≦１５．０％を含有し、かつＡｌ２Ｏ３／ＳｉＯ２＜６．５、０．２０≦Ｎａ２Ｏ／ＳｉＯ２であり、上記必須成分の合量が８５％以上であるアルミナ・ジルコニア・シリカ質溶融鋳造耐火物。
ALUMINA-ZIRCONIA-SILICA FUSED-CAST REFRACTORY MATERIAL, GLASS FURNACE, AND METHOD FOR PRODUCING SHEET GLASS
Provided are: an alumina-zirconia-silica fused-cast refractory material suitable as a refractory material for glass production apparatuses, and which suppresses the exudation of glass components from the refractory material; and a glass furnace using same. An alumina-zirconia-silica fused-cast refractory material containing, as essential components, Al2O3, ZrO2, SiO2 and Na2O, in mass percentage in oxide equivalent, 20.0% ≤ Al2O3 ≤ 70.0%, 10.0% ≤ ZrO2 < 41.5%, 3.8% ≤ SiO2 ≤ 18.0%, 1.3% ≤ Na2O ≤ 15.0%, where Al2O3/SiO2 < 6.5, 0.20 ≤ Na2O/SiO2, and the total amount of the abovementioned essential components is at least 85%.
L'invention concerne : un matériau réfractaire, coulé par fusion, à base d'alumine-zircone-silice approprié en tant que matériau réfractaire pour des appareils de production de verre et qui supprime l'exsudation de constituants de verre du matériau réfractaire ; et un four de verrerie l'utilisant. L'invention concerne un matériau réfractaire, coulé par fusion, à base d'alumine-zircone-silice, contenant, en tant que constituants essentiels, Al2O3, ZrO2, SiO2 et Na2O, en des pourcentages en masse, en équivalent d'oxyde, 20,0 % ≤ Al2O3 ≤ 70,0 %, 10,0 % ≤ ZrO2 < 41,5 %, 3,8 % ≤ SiO2 ≤ 18,0 %, 1,3 % ≤ Na2O ≤ 15,0 %, où Al2O3/SiO2 < 6,5, 0,20 ≤ Na2O/SiO2, et la quantité totale des constituants essentiels mentionnés ci-dessus étant d'au moins 85 %.
耐火物からのガラス質成分の滲出を抑制し、ガラス製造装置用の耐火物として好適なアルミナ・ジルコニア・シリカ質溶融鋳造耐火物およびそれを用いたガラス溶融窯を提供する。必須成分としてＡｌ２Ｏ３、ＺｒＯ２、ＳｉＯ２およびＮａ２Ｏを含むアルミナ・ジルコニア・シリカ質溶融鋳造耐火物であって、酸化物基準の質量パーセンテージで、２０．０％≦Ａｌ２Ｏ３≦７０．０％、１０．０％≦ＺｒＯ２＜４１．５％、３．８％≦ＳｉＯ２≦１８．０％、１．３％≦Ｎａ２Ｏ≦１５．０％を含有し、かつＡｌ２Ｏ３／ＳｉＯ２＜６．５、０．２０≦Ｎａ２Ｏ／ＳｉＯ２であり、上記必須成分の合量が８５％以上であるアルミナ・ジルコニア・シリカ質溶融鋳造耐火物。
ALUMINA-ZIRCONIA-SILICA FUSED-CAST REFRACTORY MATERIAL, GLASS FURNACE, AND METHOD FOR PRODUCING SHEET GLASS
MATÉRIAU RÉFRACTAIRE, COULÉ PAR FUSION, À BASE D'ALUMINE-ZIRCONE-SILICE, FOUR DE VERRERIE ET PROCÉDÉ DE PRODUCTION DE VERRE À VITRES
アルミナ・ジルコニア・シリカ質溶融鋳造耐火物、ガラス溶融窯、およびガラス板の製造方法
OGAWA SHUHEI (author) / TOMURA NOBUO (author) / SHINOZAKI YASUO (author)
2016-05-06
Patent
Electronic Resource
Japanese
ALUMINA-ZIRCONIA-SILICA FUSED CAST REFRACTORY AND GLASS MELTING FURNACE
| European Patent Office | 2024
ALUMINA-ZIRCONIA-SILICA FUSED CAST REFRACTORY AND GLASS MELTING FURNACE
| European Patent Office | 2019
| European Patent Office | 2016
| European Patent Office | 2016
ALUMINA-ZIRCONIA-SILICA REFRACTORY, GLASS MELTING FURNACE, AND METHOD FOR MANUFACTURING PLATE GLASS
| European Patent Office | 2017