DIELECTRIC CERAMIC MATERIAL, METHOD FOR MANUFACTURING SAME, AND COMPOSITE DIELECTRIC MATERIAL
Provided is a dielectric ceramic material which is characterized in that: the dielectric ceramic material comprises perovskite (ABO3) composite oxide particles; the value of ((D90-D10)/D50) is 1.2 or less, where D10 is the particle size at which an accumulated value in a volume frequency particle size distribution measurement by a laser diffraction scattering method is 10%, D50 is the particle size at which the accumulated value therein is 50%, and D90 is the particle size at which the accumulated value therein is 90%; the average particle size D50 is 3 to 15 μm; and the relationship between the theoretical specific surface area (m2/g) calculated by the average particle size D50 and the BET specific surface area (m2/g) measured by the BET method is 0.5≤ ((BET specific surface area-theoretical specific surface area)/theoretical specific surface area) ≤9.0.
L'invention concerne un matériau céramique diélectrique qui est caractérisé en ce que : le matériau céramique diélectrique comprend des particules d'oxyde composite de pérovskite (ABO3) ; la valeur de ((D90-D10)/D50) vaut 1,2 ou moins, où D10 représente la grosseur de particule à laquelle une valeur cumulée dans une mesure de distribution granulométrique en fréquence volumique par un procédé de diffraction/diffusion au laser est de 10 %, D50 représente la grosseur de particule à laquelle la valeur cumulée dans celle-ci est de 50 % et D90 représente la grosseur de particule à laquelle la valeur cumulée dans celle-ci est de 90 % ; la grosseur moyenne D50 des particules est de 3 à 15 μm ; et la relation entre l'aire de surface spécifique théorique (m2/g), calculée par la grosseur moyenne D50 de particule, et l'aire de surface spécifique BET (m2/g), mesurée par le procédé BET, est de 0,5≤((aire de surface spécifique BET-aire de surface spécifique théorique)/aire de surface spécifique théorique)≤9,0.
ペロブスカイト（ＡＢＯ３）型複合酸化物粒子からなり、レーザー回折散乱法による体積頻度粒度分布測定における累積値が１０％となる粒子径をＤ１０、５０％となる粒子径をＤ５０、９０％となる粒子径をＤ９０としたときに、（（Ｄ９０－Ｄ１０）／Ｄ５０）の値が１．２以下であり、平均粒子径Ｄ５０が３～１５μｍであり、平均粒子径Ｄ５０より算出される理論比表面積（ｍ２／ｇ）とＢＥＴ法により測定されるＢＥＴ比表面積（ｍ２／ｇ）との関係が、０．５≦（（ＢＥＴ比表面積－理論比表面積）／理論比表面積）≦９．０であること、を特徴とする誘電体セラミック材料を提供する。
DIELECTRIC CERAMIC MATERIAL, METHOD FOR MANUFACTURING SAME, AND COMPOSITE DIELECTRIC MATERIAL
Provided is a dielectric ceramic material which is characterized in that: the dielectric ceramic material comprises perovskite (ABO3) composite oxide particles; the value of ((D90-D10)/D50) is 1.2 or less, where D10 is the particle size at which an accumulated value in a volume frequency particle size distribution measurement by a laser diffraction scattering method is 10%, D50 is the particle size at which the accumulated value therein is 50%, and D90 is the particle size at which the accumulated value therein is 90%; the average particle size D50 is 3 to 15 μm; and the relationship between the theoretical specific surface area (m2/g) calculated by the average particle size D50 and the BET specific surface area (m2/g) measured by the BET method is 0.5≤ ((BET specific surface area-theoretical specific surface area)/theoretical specific surface area) ≤9.0.
L'invention concerne un matériau céramique diélectrique qui est caractérisé en ce que : le matériau céramique diélectrique comprend des particules d'oxyde composite de pérovskite (ABO3) ; la valeur de ((D90-D10)/D50) vaut 1,2 ou moins, où D10 représente la grosseur de particule à laquelle une valeur cumulée dans une mesure de distribution granulométrique en fréquence volumique par un procédé de diffraction/diffusion au laser est de 10 %, D50 représente la grosseur de particule à laquelle la valeur cumulée dans celle-ci est de 50 % et D90 représente la grosseur de particule à laquelle la valeur cumulée dans celle-ci est de 90 % ; la grosseur moyenne D50 des particules est de 3 à 15 μm ; et la relation entre l'aire de surface spécifique théorique (m2/g), calculée par la grosseur moyenne D50 de particule, et l'aire de surface spécifique BET (m2/g), mesurée par le procédé BET, est de 0,5≤((aire de surface spécifique BET-aire de surface spécifique théorique)/aire de surface spécifique théorique)≤9,0.
ペロブスカイト（ＡＢＯ３）型複合酸化物粒子からなり、レーザー回折散乱法による体積頻度粒度分布測定における累積値が１０％となる粒子径をＤ１０、５０％となる粒子径をＤ５０、９０％となる粒子径をＤ９０としたときに、（（Ｄ９０－Ｄ１０）／Ｄ５０）の値が１．２以下であり、平均粒子径Ｄ５０が３～１５μｍであり、平均粒子径Ｄ５０より算出される理論比表面積（ｍ２／ｇ）とＢＥＴ法により測定されるＢＥＴ比表面積（ｍ２／ｇ）との関係が、０．５≦（（ＢＥＴ比表面積－理論比表面積）／理論比表面積）≦９．０であること、を特徴とする誘電体セラミック材料を提供する。
DIELECTRIC CERAMIC MATERIAL, METHOD FOR MANUFACTURING SAME, AND COMPOSITE DIELECTRIC MATERIAL
MATÉRIAU CÉRAMIQUE DIÉLECTRIQUE, SON PROCÉDÉ DE FABRICATION ET MATÉRIAU COMPOSITE DIÉLECTRIQUE
誘電体セラミック材料、その製造方法及び複合誘電体材料
TANABE SHINJI (author)
2016-10-13
Patent
Electronic Resource
Japanese
| European Patent Office | 2015
| European Patent Office | 2022