ORIENTED ALN SINTERED BODY, AND PRODUCTION METHOD THEREFOR
In a first step of this production method for an oriented AlN sintered body, a mixture obtained by mixing a sintering aid with an AlN starting material powder including a plate-shaped AlN powder of which the plate surfaces are in the c plane, and which has an aspect ratio of 3 or higher, and an average thickness of 0.05-1.8 µm, is moulded to prepare a moulded body. The mixture is moulded such that the plate surfaces of the plate-shaped AlN powder extend along the surface of the moulded body. In a second step, the moulded body is subjected to hot-press firing under a non-oxidizing atmosphere while applying pressure to the surface of the moulded body, to obtain the oriented AlN sintered body.
Dans une première étape de ce procédé de production d'un corps fritté d'AlN orienté, un mélange obtenu par mélange d'un auxiliaire de frittage avec une poudre de matériau de départ d'AlN comprenant une poudre d'AlN en forme de plaque dont les surfaces de plaque sont dans le plan c, et qui présente un rapport de forme supérieur ou égal à 3, et une épaisseur moyenne allant de 0,05 à 1,8 µm, est moulé pour préparer un corps moulé. Le mélange est moulé de telle sorte que les surfaces de plaque de la poudre d'AlN en forme de plaque s'étendent le long de la surface du corps moulé. Dans une seconde étape, le corps moulé est soumis à une cuisson par compression à chaud sous atmosphère non oxydante tout en appliquant une pression sur la surface du corps moulé, pour obtenir le corps fritté d'AlN orienté.
配向ＡｌＮ焼結体の製法の第１工程では、板面がｃ面であり、アスペクト比が３以上、平均厚さが０．０５～１．８μｍの板状ＡｌＮ粉末を含むＡｌＮ原料粉末に焼結助剤を混合した混合物を成形して成形体を作製する工程であって、前記板状ＡｌＮ粉末の板面が前記成形体の表面に沿うように前記混合物を成形する。第２工程では、成形体の表面を加圧しながら非酸化雰囲気下、成形体をホットプレス焼成して配向ＡｌＮ焼結体を得る。
ORIENTED ALN SINTERED BODY, AND PRODUCTION METHOD THEREFOR
In a first step of this production method for an oriented AlN sintered body, a mixture obtained by mixing a sintering aid with an AlN starting material powder including a plate-shaped AlN powder of which the plate surfaces are in the c plane, and which has an aspect ratio of 3 or higher, and an average thickness of 0.05-1.8 µm, is moulded to prepare a moulded body. The mixture is moulded such that the plate surfaces of the plate-shaped AlN powder extend along the surface of the moulded body. In a second step, the moulded body is subjected to hot-press firing under a non-oxidizing atmosphere while applying pressure to the surface of the moulded body, to obtain the oriented AlN sintered body.
Dans une première étape de ce procédé de production d'un corps fritté d'AlN orienté, un mélange obtenu par mélange d'un auxiliaire de frittage avec une poudre de matériau de départ d'AlN comprenant une poudre d'AlN en forme de plaque dont les surfaces de plaque sont dans le plan c, et qui présente un rapport de forme supérieur ou égal à 3, et une épaisseur moyenne allant de 0,05 à 1,8 µm, est moulé pour préparer un corps moulé. Le mélange est moulé de telle sorte que les surfaces de plaque de la poudre d'AlN en forme de plaque s'étendent le long de la surface du corps moulé. Dans une seconde étape, le corps moulé est soumis à une cuisson par compression à chaud sous atmosphère non oxydante tout en appliquant une pression sur la surface du corps moulé, pour obtenir le corps fritté d'AlN orienté.
配向ＡｌＮ焼結体の製法の第１工程では、板面がｃ面であり、アスペクト比が３以上、平均厚さが０．０５～１．８μｍの板状ＡｌＮ粉末を含むＡｌＮ原料粉末に焼結助剤を混合した混合物を成形して成形体を作製する工程であって、前記板状ＡｌＮ粉末の板面が前記成形体の表面に沿うように前記混合物を成形する。第２工程では、成形体の表面を加圧しながら非酸化雰囲気下、成形体をホットプレス焼成して配向ＡｌＮ焼結体を得る。
ORIENTED ALN SINTERED BODY, AND PRODUCTION METHOD THEREFOR
CORPS FRITTÉ D'ALN ORIENTÉ ET SON PROCÉDÉ DE PRODUCTION
配向ＡｌＮ焼結体及びその製法
KOBAYASHI YOSHIMASA (author) / KOBAYASHI HIROHARU (author) / IIDA KAZUKI (author)
2018-06-28
Patent
Electronic Resource
Japanese