MnZn-BASED FERRITE SINTERED BODY
A MnZn-based ferrite sintered body which contains a main component and an auxiliary component and has an average crystal grain diameter of 3 μm or more and less than 8 μm and a sintered body density of 4.65 g/cm3 or more, wherein the main component is composed of Fe in an amount of 53.30 to 53.80 mol% in terms of Fe2O3 content, Zn in an amount of 6.90 to 9.50 mol% in terms of ZnO content and a remainder made up by Mn in terms of MnO content, and the auxiliary component is composed of Si, Ca, Co, Zr and Ta in amounts of 0.003 to 0.020 part by mass in terms of SiO2 content, more than 0 part by mass and 0.35 part by mass or less in term of CaCO3 content, 0.30 to 0.50 part by mass in terms of Co3O4 content, 0.03 to 0.10 part by mass in terms of ZrO2 content and 0 to 0.05 part by mass in terms of Ta2O5 content, respectively, relative to the total amount, i.e., 100 parts by mass, of the main component in the above-mentioned terms.
L'invention concerne un corps fritté en ferrite à base de MnZn qui contient un composant principal et un composant auxiliaire et présente un diamètre de grain cristallin moyen égal ou supérieur à 3 µm et inférieur à 8 µm et une densité de corps fritté égale ou supérieure à 4,65 g/cm3, le composant principal étant composé de Fe à raison de 53,30 à 53,80 % en moles en termes de teneur en Fe2O3, de Zn à raison de 6,90 à 9,50 % en moles en termes de teneur en ZnO et le reste étant constitué de Mn en termes de teneur en MnO, et le composant auxiliaire étant composé de Si, Ca, Co, Zr et Ta à raison de 0,003 à 0,020 partie en masse en termes de teneur en SiO2, plus de 0 partie en masse et 0,35 partie en masse ou moins en termes de teneur en CaCO3, 0,30 à 0,50 partie en masse en termes de teneur en Co3O4, 0,03 à 0,10 partie en masse en termes de teneur en ZrO2 et 0 à 0,05 partie en masse en termes de teneur en Ta2O5, respectivement, par rapport à la quantité totale, c'est-à-dire à 100 parties en masse, du composant principal comme mentionné ci-dessus.
Fe2O3換算で53.30～53.80モル％のFe、ZnO換算で6.90～9.50モル％のZn、及びMnO換算で残部のMnからなる主成分と、前記換算での前記主成分の合計100質量部に対して、SiO2換算で0.003～0.020質量部のSi、CaCO3換算で0質量部超0.35質量部以下のCa、Co3O4換算で0.30～0.50質量部のCo、ZrO2換算で0.03～0.10質量部のZr、及びTa2O5換算で0～0.05質量部のTaからなる副成分とを含有し、平均結晶粒径が3μm以上8μm未満であり、焼結体密度が4.65 g/cm3以上であるMnZn系フェライト焼結体。
MnZn-BASED FERRITE SINTERED BODY
A MnZn-based ferrite sintered body which contains a main component and an auxiliary component and has an average crystal grain diameter of 3 μm or more and less than 8 μm and a sintered body density of 4.65 g/cm3 or more, wherein the main component is composed of Fe in an amount of 53.30 to 53.80 mol% in terms of Fe2O3 content, Zn in an amount of 6.90 to 9.50 mol% in terms of ZnO content and a remainder made up by Mn in terms of MnO content, and the auxiliary component is composed of Si, Ca, Co, Zr and Ta in amounts of 0.003 to 0.020 part by mass in terms of SiO2 content, more than 0 part by mass and 0.35 part by mass or less in term of CaCO3 content, 0.30 to 0.50 part by mass in terms of Co3O4 content, 0.03 to 0.10 part by mass in terms of ZrO2 content and 0 to 0.05 part by mass in terms of Ta2O5 content, respectively, relative to the total amount, i.e., 100 parts by mass, of the main component in the above-mentioned terms.
L'invention concerne un corps fritté en ferrite à base de MnZn qui contient un composant principal et un composant auxiliaire et présente un diamètre de grain cristallin moyen égal ou supérieur à 3 µm et inférieur à 8 µm et une densité de corps fritté égale ou supérieure à 4,65 g/cm3, le composant principal étant composé de Fe à raison de 53,30 à 53,80 % en moles en termes de teneur en Fe2O3, de Zn à raison de 6,90 à 9,50 % en moles en termes de teneur en ZnO et le reste étant constitué de Mn en termes de teneur en MnO, et le composant auxiliaire étant composé de Si, Ca, Co, Zr et Ta à raison de 0,003 à 0,020 partie en masse en termes de teneur en SiO2, plus de 0 partie en masse et 0,35 partie en masse ou moins en termes de teneur en CaCO3, 0,30 à 0,50 partie en masse en termes de teneur en Co3O4, 0,03 à 0,10 partie en masse en termes de teneur en ZrO2 et 0 à 0,05 partie en masse en termes de teneur en Ta2O5, respectivement, par rapport à la quantité totale, c'est-à-dire à 100 parties en masse, du composant principal comme mentionné ci-dessus.
Fe2O3換算で53.30～53.80モル％のFe、ZnO換算で6.90～9.50モル％のZn、及びMnO換算で残部のMnからなる主成分と、前記換算での前記主成分の合計100質量部に対して、SiO2換算で0.003～0.020質量部のSi、CaCO3換算で0質量部超0.35質量部以下のCa、Co3O4換算で0.30～0.50質量部のCo、ZrO2換算で0.03～0.10質量部のZr、及びTa2O5換算で0～0.05質量部のTaからなる副成分とを含有し、平均結晶粒径が3μm以上8μm未満であり、焼結体密度が4.65 g/cm3以上であるMnZn系フェライト焼結体。
MnZn-BASED FERRITE SINTERED BODY
CORPS FRITTÉ EN FERRITE À BASE DE MnZn
ＭｎＺｎ系フェライト焼結体
MIYOSHI YASUHARU (author) / TADA TOMOYUKI (author) / KOYUHARA NORIKAZU (author)
2018-10-04
Patent
Electronic Resource
Japanese
MNZN FERRITE SINTERED BODY AND METHOD FOR MANUFACTURING MNZN FERRITE
| European Patent Office | 2023
MnZn-based ferrite sintered body and method for producing MnZn-based ferrite
| European Patent Office | 2023