Method for manufacturing binders hardening by hydration and carbonation
Method for manufacturing a binder comprising a hydratable material and a building element from the binder comprising the steps: - providing a starting material from one or more raw materials convertible by tempering at 600 to 1200 °C into the hydratable material, wherein the starting material has a Ca/Si molar ratio from 0.5 to 1.8 and contains no or up to 30 % by weight of other elements than Ca and Si with regard to the total mass calculated as oxides, - tempering the starting material at a temperature in the range from 600 to 1200 °C during a residence time from 1 minutes to 5 hours to provide the hydratable material containing not more than 10 % by weight monocalcium silicate and at least 15 % by weight hydratable phases in the form of lime and dicalcium silicate, wherein at least 50 % of the hydratable phases are dicalcium silicate, wherein the residence time and the tempering temperature are adapted to obtain the said hydratable material by converting not more than 80 % by weight of the starting material, - cooling the hydratable material to provide the binder comprising the hydratable material. For manufacturing the building element the further steps of - mixing the binder with water and optionally one or more of aggregate, additves, admixtures to obtain a binder paste - placing the binder paste - hydrating the binder paste until the amount of bound water is at least 1 g/100 g dry binder and - carbonating the binder paste until until the amount of additionally bound carbon dioxide is at least 150 % of the initially bound water mass and/or the strength exceeds 2 MPa while still keeping the bound water at least 50 % of the initially bound water.
L'invention concerne un procédé de fabrication d'un liant comprenant un matériau hydratable et un élément de construction à partir du liant qui comprend les étapes consistant à : - utiliser un produit de départ à partir d'une ou plusieurs matières premières convertibles par trempe de 600 à 1 200 °C en matériau hydratable, le produit de départ ayant un rapport molaire Ca/Si de 0,5 à 1,8 et ne contenant pas ou contenant jusqu'à 30 % en poids d'éléments autres que Ca et Si par rapport à la masse totale calculée en tant qu'oxydes, - effectuer la trempe du produit de départ à une température comprise entre 600 et 1 200 °C pendant un temps de séjour de 1 minute à 5 heures pour fournir le matériau hydratable contenant au plus 10 % en poids de silicate de monocalcium et au moins 15 % en poids de phases hydratables sous la forme de chaux et de silicate dicalcique, au moins 50 % des phases hydratables étant du silicate dicalcique, le temps de séjour et la température de trempe étant adaptés pour obtenir ledit matériau hydratable en ne convertissant pas plus de 80 % en poids du produit de départ, - refroidir le matériau hydratable pour fournir le liant comprenant le matériau hydratable. Pour fabriquer l'élément de construction, les étapes supplémentaires consistant à - mélanger le liant avec de l'eau et éventuellement un ou plusieurs éléments parmi un agrégat, des additifs, des adjuvants pour obtenir une pâte de liant - placer la pâte de liant - hydrater la pâte de liant jusqu'à ce que la quantité d'eau liée soit d'au moins 1 g/100 g de liant sec et - carboniser la pâte de liant jusqu'à ce que la quantité de dioxyde de carbone supplémentaire liée représente au moins 150 % de la masse d'eau initialement liée et/ou que la résistance dépasse 2 MPa tout en maintenant l'eau liée à au moins 50 % de l'eau initialement liée.
Method for manufacturing binders hardening by hydration and carbonation
Method for manufacturing a binder comprising a hydratable material and a building element from the binder comprising the steps: - providing a starting material from one or more raw materials convertible by tempering at 600 to 1200 °C into the hydratable material, wherein the starting material has a Ca/Si molar ratio from 0.5 to 1.8 and contains no or up to 30 % by weight of other elements than Ca and Si with regard to the total mass calculated as oxides, - tempering the starting material at a temperature in the range from 600 to 1200 °C during a residence time from 1 minutes to 5 hours to provide the hydratable material containing not more than 10 % by weight monocalcium silicate and at least 15 % by weight hydratable phases in the form of lime and dicalcium silicate, wherein at least 50 % of the hydratable phases are dicalcium silicate, wherein the residence time and the tempering temperature are adapted to obtain the said hydratable material by converting not more than 80 % by weight of the starting material, - cooling the hydratable material to provide the binder comprising the hydratable material. For manufacturing the building element the further steps of - mixing the binder with water and optionally one or more of aggregate, additves, admixtures to obtain a binder paste - placing the binder paste - hydrating the binder paste until the amount of bound water is at least 1 g/100 g dry binder and - carbonating the binder paste until until the amount of additionally bound carbon dioxide is at least 150 % of the initially bound water mass and/or the strength exceeds 2 MPa while still keeping the bound water at least 50 % of the initially bound water.
L'invention concerne un procédé de fabrication d'un liant comprenant un matériau hydratable et un élément de construction à partir du liant qui comprend les étapes consistant à : - utiliser un produit de départ à partir d'une ou plusieurs matières premières convertibles par trempe de 600 à 1 200 °C en matériau hydratable, le produit de départ ayant un rapport molaire Ca/Si de 0,5 à 1,8 et ne contenant pas ou contenant jusqu'à 30 % en poids d'éléments autres que Ca et Si par rapport à la masse totale calculée en tant qu'oxydes, - effectuer la trempe du produit de départ à une température comprise entre 600 et 1 200 °C pendant un temps de séjour de 1 minute à 5 heures pour fournir le matériau hydratable contenant au plus 10 % en poids de silicate de monocalcium et au moins 15 % en poids de phases hydratables sous la forme de chaux et de silicate dicalcique, au moins 50 % des phases hydratables étant du silicate dicalcique, le temps de séjour et la température de trempe étant adaptés pour obtenir ledit matériau hydratable en ne convertissant pas plus de 80 % en poids du produit de départ, - refroidir le matériau hydratable pour fournir le liant comprenant le matériau hydratable. Pour fabriquer l'élément de construction, les étapes supplémentaires consistant à - mélanger le liant avec de l'eau et éventuellement un ou plusieurs éléments parmi un agrégat, des additifs, des adjuvants pour obtenir une pâte de liant - placer la pâte de liant - hydrater la pâte de liant jusqu'à ce que la quantité d'eau liée soit d'au moins 1 g/100 g de liant sec et - carboniser la pâte de liant jusqu'à ce que la quantité de dioxyde de carbone supplémentaire liée représente au moins 150 % de la masse d'eau initialement liée et/ou que la résistance dépasse 2 MPa tout en maintenant l'eau liée à au moins 50 % de l'eau initialement liée.
Method for manufacturing binders hardening by hydration and carbonation
PROCÉDÉ DE FABRICATION DE LIANTS DURCISSANT PAR HYDRATATION ET CARBONATATION
SKOCEK JAN (author) / ZAJAC MACIEJ (author) / BOLTE GERD (author) / BEN HAHA MOHSEN (author)
2019-04-18
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
METHOD FOR MANUFACTURING BINDERS HARDENING BY HYDRATION AND CARBONATION
| European Patent Office | 2019
Method for manufacturing binders hardening by hydration and carbonation
| European Patent Office | 2022
METHOD FOR MANUFACTURING BINDERS HARDENING BY HYDRATION AND CARBONATION
| European Patent Office | 2021
METHOD FOR MANUFACTURING BINDERS HARDENING BY HYDRATION AND CARBONATION
| European Patent Office | 2020
METHOD FOR MANUFACTURING BINDERS HARDENING BY HYDRATION AND CARBONATION
| European Patent Office | 2022