SHAPED JOINT MATERIAL FOR HEATED INSTALLATION
The objective of the present invention is to retain the hot sealing properties of a shaped joint material while suppressing igniting or smoke generation from the combustible material in the shaped joint material. The shaped joint material is obtained by adding a ratio of 26-50% by mass of an organic material additive into 100% by mass of a mixture including 50-90% by mass of a gibbsite aluminum hydroxide raw material, 1-9% by mass of clay, 9-23% by mass of graphite, and the balance mostly other refractory raw material, and kneading, shaping, and drying the result.
La présente invention a pour objectif de conserver les propriétés d'étanchéité à chaud d'un matériau pour joint façonné tout en supprimant l'allumage ou la génération de fumée provenant du matériau combustible dans le matériau pour joint façonné. Le matériau pour joint façonné est obtenu par ajout d'un rapport de 26 à 50 % en masse d'un additif de type matière organique à 100 % en masse d'un mélange comprenant de 50 à 90 % en masse d'une matière première d'hydroxyde d'aluminium de type gibbsite, de 1 à 9 % en masse d'argile, de 9 à 23 % en masse de graphite, et le reste étant principalement constitué d'autres matières premières réfractaires, et par malaxage, façonnage et séchage du résultat.
本発明は定形目地材の熱間シール性は維持した上で，定形目地材中の可燃物の燃焼による発炎及び発煙を抑制することを目的とする。すなわち本発明の熱間設置用定形目地材は，ギブサイトである水酸化アルミニウム原料を５０質量％以上９０質量％以下，粘土を１質量％以上９質量％以下，黒鉛を９質量％以上２３質量％以下含み，残部が主としてその他耐火原料からなる配合物１００質量％に対して，有機質添加剤の合量を外掛けで２６質量％以上５０質量％以下添加して混練し，成形及び乾燥して得られるものである。
SHAPED JOINT MATERIAL FOR HEATED INSTALLATION
The objective of the present invention is to retain the hot sealing properties of a shaped joint material while suppressing igniting or smoke generation from the combustible material in the shaped joint material. The shaped joint material is obtained by adding a ratio of 26-50% by mass of an organic material additive into 100% by mass of a mixture including 50-90% by mass of a gibbsite aluminum hydroxide raw material, 1-9% by mass of clay, 9-23% by mass of graphite, and the balance mostly other refractory raw material, and kneading, shaping, and drying the result.
La présente invention a pour objectif de conserver les propriétés d'étanchéité à chaud d'un matériau pour joint façonné tout en supprimant l'allumage ou la génération de fumée provenant du matériau combustible dans le matériau pour joint façonné. Le matériau pour joint façonné est obtenu par ajout d'un rapport de 26 à 50 % en masse d'un additif de type matière organique à 100 % en masse d'un mélange comprenant de 50 à 90 % en masse d'une matière première d'hydroxyde d'aluminium de type gibbsite, de 1 à 9 % en masse d'argile, de 9 à 23 % en masse de graphite, et le reste étant principalement constitué d'autres matières premières réfractaires, et par malaxage, façonnage et séchage du résultat.
本発明は定形目地材の熱間シール性は維持した上で，定形目地材中の可燃物の燃焼による発炎及び発煙を抑制することを目的とする。すなわち本発明の熱間設置用定形目地材は，ギブサイトである水酸化アルミニウム原料を５０質量％以上９０質量％以下，粘土を１質量％以上９質量％以下，黒鉛を９質量％以上２３質量％以下含み，残部が主としてその他耐火原料からなる配合物１００質量％に対して，有機質添加剤の合量を外掛けで２６質量％以上５０質量％以下添加して混練し，成形及び乾燥して得られるものである。
SHAPED JOINT MATERIAL FOR HEATED INSTALLATION
MATÉRIAU DE JOINT FAÇONNÉ POUR INSTALLATION CHAUFFÉE
熱間設置用定形目地材
OOUCHI TATSUYA (author) / YAMAMOTO MASAKI (author)
2020-04-09
Patent
Electronic Resource
Japanese