HIGH-ENTROPY ALLOY BORIDE CERAMIC, AND PREPARATION METHOD THEREFOR AND APPLICATION THEREOF
A high-entropy alloy boride ceramic and a preparation method therefor. The molecular formula of the high-entropy alloy boride ceramic is Aly(FeNiCoCr)1-x-yBx, wherein 0≤x≤1 and 0≤y≤1.The high-entropy alloy boride is prepared by the following steps: carrying out ball milling on Al, Fe, Ni, Co, Cr, and B to prepare Aly(FeNiCoCr)1-x-yBx powder; then carrying out spark plasma sintering at a heating rate of 50-200 °C/min, a temperature of 800-1500 °C, and a constant pressure of 10-50 Mpa; carrying out furnace cooling. The Aly(FeNiCoCr)1-x-yBx high-entropy alloy boride powder prepared by the method is approximately spherical and is small in particle size, the ceramic main phase is an FCC solid solution in which Fe and Cr metal borides are dispersed, and high density, high hardness and wear resistance are achieved.
L'invention concerne une céramique de borure d'alliage à entropie élevée et un procédé de préparation associé. La formule moléculaire de la céramique de borure d'alliage à entropie élevée est Aly(FeNiCoCr)1-x-yBx, dans laquelle 0 ≤ x ≤ 1 et 0 ≤ y ≤ 1. Le borure d'alliage à entropie élevée est préparé par les étapes suivantes : réalisation d'un broyage à billes sur des Al, Fe, Ni, Co, Cr, et B pour préparer une poudre de Aly(FeNiCoCr)1-x-yBx ; puis réalisation d'un frittage par plasma d'étincelles à une vitesse de chauffage de 50 à 200 °C/min, une température de 800-1500 °C, et une pression constante de 10 à 50 Mpa ; la réalisation d'un refroidissement de four. La poudre de borure d'alliage à entropie élevée Aly(FeNiCoCr)1-x-yBx préparée par le procédé est approximativement sphérique et est de petite taille de particule, la phase principale de céramique est une solution solide de FCC dans laquelle des borures métalliques de Fe et Cr sont dispersés, et une densité élevée, une dureté élevée et une résistance à l'usure sont obtenues.
一种高熵合金硼化物陶瓷及其制备方法。所述高熵合金硼化物陶瓷的分子式为Aly(FeNiCoCr)1-x-yBx，其中0≤x≤1，0≤y≤1，所述高熵合金硼化物是将Al、Fe、Ni、Co、Cr和B经球磨制得Aly(FeNiCoCr)1-x-yBx粉体；再通过放电等离子烧结，以加热速率50～200℃/min、在800～1500℃、恒定压力10～50Mpa下烧结，随炉冷却制得。该方法制备的Aly(FeNiCoCr)1-x-yBx高熵合金硼化物粉末为类球形且粒径小，该陶瓷主相为FCC固溶体中弥散分布着Fe、Cr金属硼化物，具有高致密度、较高的硬度和耐磨性能。
HIGH-ENTROPY ALLOY BORIDE CERAMIC, AND PREPARATION METHOD THEREFOR AND APPLICATION THEREOF
A high-entropy alloy boride ceramic and a preparation method therefor. The molecular formula of the high-entropy alloy boride ceramic is Aly(FeNiCoCr)1-x-yBx, wherein 0≤x≤1 and 0≤y≤1.The high-entropy alloy boride is prepared by the following steps: carrying out ball milling on Al, Fe, Ni, Co, Cr, and B to prepare Aly(FeNiCoCr)1-x-yBx powder; then carrying out spark plasma sintering at a heating rate of 50-200 °C/min, a temperature of 800-1500 °C, and a constant pressure of 10-50 Mpa; carrying out furnace cooling. The Aly(FeNiCoCr)1-x-yBx high-entropy alloy boride powder prepared by the method is approximately spherical and is small in particle size, the ceramic main phase is an FCC solid solution in which Fe and Cr metal borides are dispersed, and high density, high hardness and wear resistance are achieved.
L'invention concerne une céramique de borure d'alliage à entropie élevée et un procédé de préparation associé. La formule moléculaire de la céramique de borure d'alliage à entropie élevée est Aly(FeNiCoCr)1-x-yBx, dans laquelle 0 ≤ x ≤ 1 et 0 ≤ y ≤ 1. Le borure d'alliage à entropie élevée est préparé par les étapes suivantes : réalisation d'un broyage à billes sur des Al, Fe, Ni, Co, Cr, et B pour préparer une poudre de Aly(FeNiCoCr)1-x-yBx ; puis réalisation d'un frittage par plasma d'étincelles à une vitesse de chauffage de 50 à 200 °C/min, une température de 800-1500 °C, et une pression constante de 10 à 50 Mpa ; la réalisation d'un refroidissement de four. La poudre de borure d'alliage à entropie élevée Aly(FeNiCoCr)1-x-yBx préparée par le procédé est approximativement sphérique et est de petite taille de particule, la phase principale de céramique est une solution solide de FCC dans laquelle des borures métalliques de Fe et Cr sont dispersés, et une densité élevée, une dureté élevée et une résistance à l'usure sont obtenues.
一种高熵合金硼化物陶瓷及其制备方法。所述高熵合金硼化物陶瓷的分子式为Aly(FeNiCoCr)1-x-yBx，其中0≤x≤1，0≤y≤1，所述高熵合金硼化物是将Al、Fe、Ni、Co、Cr和B经球磨制得Aly(FeNiCoCr)1-x-yBx粉体；再通过放电等离子烧结，以加热速率50～200℃/min、在800～1500℃、恒定压力10～50Mpa下烧结，随炉冷却制得。该方法制备的Aly(FeNiCoCr)1-x-yBx高熵合金硼化物粉末为类球形且粒径小，该陶瓷主相为FCC固溶体中弥散分布着Fe、Cr金属硼化物，具有高致密度、较高的硬度和耐磨性能。
HIGH-ENTROPY ALLOY BORIDE CERAMIC, AND PREPARATION METHOD THEREFOR AND APPLICATION THEREOF
CÉRAMIQUE DE BORURE D'ALLIAGE À ENTROPIE ÉLEVÉE, PROCÉDÉ DE PRÉPARATION ET SON APPLICATION
一种高熵合金硼化物陶瓷及其制备方法和应用
LONG YING (author) / CHE JINTAO (author) / HUANG LUJIANG (author) / LIN HUATAY (author)
2020-08-06
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2023
Quaternary boride high-entropy ceramic and preparation method thereof
| European Patent Office | 2024
High-entropy boride ceramic pellet as well as preparation method and application thereof
| European Patent Office | 2024
High-entropy boride ceramic material as well as preparation method and application thereof
| European Patent Office | 2023
Medium-entropy boride ceramic as well as preparation method and application thereof
| European Patent Office | 2024