LOW-SHRINKAGE ALKALI-ACTIVATED DRY MIX REPAIR MORTAR
A dry-mix, OPC-free,alkali-activated repair mortar includes a base material selected from ground granulated blast furnace slag, fly ash, or a mixture thereof in an amount from approximately 32 weight percent to approximately 37 weight percent. Metakaolin is provided in an amount from approximately 3 weight percent to approximately 8 weight percent. As an alkali activator, modulated potassium silicate is used, the potassium silicate having been modified (by KOH) such that a molar ratio of K 2O to SiO 2 ranges from approximately 1.8 to 2.2. A filler is used in an amount from approximately 50 weight percent to approximately 54 weight percent. The drying shrinkage of the repair mortar is less than or equal to approximately 0.06% and the bond strength of the repair mortar is greater than or equal to approximately 0.5 MPa, the acid resistance measured by a weight loss after 28 days of acid exposure is less than or equal to approximately 3.4 %, and the setting time of the repair mortar is greater than or equal to approximately 60 minutes.
L'invention concerne un mortier de réparation sous forme de mélange sec sans ciment Portland ordinaire (OPC) activé en milieu alcalin, comprenant un matériau de base choisi parmi des scories de haut fourneau granulées broyées, des cendres volantes ou un mélange de celles-ci en une quantité d'environ 32 pour cent en poids à environ 37 pour cent en poids. Du métakaolin est présent en une quantité d'environ 3 pour cent en poids à environ 8 pour cent en poids. En tant qu'activateur alcalin, du silicate de potassium modulé est utilisé, le silicate de potassium ayant été modifié (par du KOH) de façon telle qu'un rapport molaire de K2O à SiO2 est compris entre environ 1,8 et 2,2. Une charge est utilisée en une quantité d'environ 50 pour cent en poids à environ 54 pour cent en poids. Le retrait au séchage du mortier de réparation est inférieur ou égal à environ 0,06 % et la force de liaison du mortier de réparation est supérieure ou égale à environ 0,5 MPa, la résistance à l'acide mesurée par une perte de poids après 28 jours d'exposition à de l'acide est inférieure ou égale à environ 3,4 % et le temps de prise du mortier de réparation est supérieur ou égal à environ 60 minutes.
LOW-SHRINKAGE ALKALI-ACTIVATED DRY MIX REPAIR MORTAR
A dry-mix, OPC-free,alkali-activated repair mortar includes a base material selected from ground granulated blast furnace slag, fly ash, or a mixture thereof in an amount from approximately 32 weight percent to approximately 37 weight percent. Metakaolin is provided in an amount from approximately 3 weight percent to approximately 8 weight percent. As an alkali activator, modulated potassium silicate is used, the potassium silicate having been modified (by KOH) such that a molar ratio of K 2O to SiO 2 ranges from approximately 1.8 to 2.2. A filler is used in an amount from approximately 50 weight percent to approximately 54 weight percent. The drying shrinkage of the repair mortar is less than or equal to approximately 0.06% and the bond strength of the repair mortar is greater than or equal to approximately 0.5 MPa, the acid resistance measured by a weight loss after 28 days of acid exposure is less than or equal to approximately 3.4 %, and the setting time of the repair mortar is greater than or equal to approximately 60 minutes.
L'invention concerne un mortier de réparation sous forme de mélange sec sans ciment Portland ordinaire (OPC) activé en milieu alcalin, comprenant un matériau de base choisi parmi des scories de haut fourneau granulées broyées, des cendres volantes ou un mélange de celles-ci en une quantité d'environ 32 pour cent en poids à environ 37 pour cent en poids. Du métakaolin est présent en une quantité d'environ 3 pour cent en poids à environ 8 pour cent en poids. En tant qu'activateur alcalin, du silicate de potassium modulé est utilisé, le silicate de potassium ayant été modifié (par du KOH) de façon telle qu'un rapport molaire de K2O à SiO2 est compris entre environ 1,8 et 2,2. Une charge est utilisée en une quantité d'environ 50 pour cent en poids à environ 54 pour cent en poids. Le retrait au séchage du mortier de réparation est inférieur ou égal à environ 0,06 % et la force de liaison du mortier de réparation est supérieure ou égale à environ 0,5 MPa, la résistance à l'acide mesurée par une perte de poids après 28 jours d'exposition à de l'acide est inférieure ou égale à environ 3,4 % et le temps de prise du mortier de réparation est supérieur ou égal à environ 60 minutes.
LOW-SHRINKAGE ALKALI-ACTIVATED DRY MIX REPAIR MORTAR
MORTIER DE RÉPARATION SOUS FORME DE MÉLANGE SEC ACTIVÉ EN MILIEU ALCALIN À FAIBLE RETRAIT
CHAU CHUNG KONG (author) / GUAN XIWEN (author) / LIU SHIYIN (author) / SHAM MAN LUNG (author) / CHAN WAI PONG (author)
2020-10-08
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
Shrinkage Characteristics of Alkali-Activated Slag Mortar with SAP
| Springer Verlag | 2016
Alkali activated slag mortar. Mechanical strengths, shrinkage and structure
| UB Braunschweig | 1990