METHOD OF VORTEX MELTING, REDUCING, DEALKALIZATION, IRON EXTRACTION AND DIRECT CEMENT PRODUCTION OF HIGH-IRON RED MUD
A method of vortex melting, reducing, dealkalization, iron extraction and direct cement production of high-iron red mud, performed according to the following steps: (1) preparing raw material high-iron red mud; (2) drying the raw material, obtaining a dewatered raw material; mixing the dewatered raw material with a solid carbon reducing agent and a slagging agent, preparing a mixture, spraying into a vortex center of a vortex stirring high-temperature oven, performing vortex stirring and reducing; (3) layering molten iron and molten slag formed after reducing, continuing overflow separation; adding ferrochrome and ferromanganese to the molten iron, forming a wear-resistant cast iron product; (4) adjusting components of slag in a melting furnace, causing the slag to meet cement clinker requirements, air cooling, then crushing and grinding into cement clinker. The present invention can simultaneously realize extraction of sodium and iron from red mud, the process steps are simple, sodium base and iron extraction rates are relatively high, and a red mud utilization rate reaches 100%.
L'invention concerne un procédé de fusion tourbillonnaire, de réduction, de désalcalinisation, d'extraction de fer et de production directe de ciment à partir de boues rouges à forte teneur en fer, mis en œuvre selon les étapes suivantes consistant à : (1) préparer une matière première à base de boues rouges à forte teneur en fer ; (2) sécher la matière première, obtenir une matière première égouttée ; mélanger la matière première égouttée avec un agent réducteur carboné solide et un agent scorifiant, préparer un mélange, pulvériser au centre d'un tourbillon d'un four à haute température à agitation tourbillonnaire, mettre en œuvre une agitation tourbillonnaire et une réduction ; (3) superposer le fer fondu et les scories fondues formés après réduction, poursuivre la séparation par débordement ; ajouter du ferrochrome et du ferromanganèse au fer fondu, former un produit en fonte résistant à l'usure ; (4) ajuster les composants des scories dans un four de fusion, amener les scories à être conformes aux exigences d'un clinker, refroidir par air, puis concasser et broyer pour obtenir un clinker. La présente invention permet une mise en œuvre simultanée d'une extraction de sodium et de fer à partir de boues rouges, les étapes du procédé sont simples, les taux d'extraction de la base sodique et du fer sont relativement élevés et le taux d'utilisation des boues rouges atteint 100 %.
一种高铁赤泥涡流熔融还原脱碱提铁直接水泥化的方法，按以下步骤进行：(1)准备原料高铁赤泥；(2)原料干燥获得脱水原料；脱水原料与固态碳质还原剂和造渣剂混料制成混合料，喷吹到涡流搅拌高温炉的漩涡中心，进行涡流搅拌还原；(3)还原后形成的铁水与熔融渣分层，连续溢流分离；向铁水中加入铬铁和锰铁制成耐磨铸铁产品；(4)熔融渣在熔炼炉中调整组分使其符合水泥熟料要求，空冷后破碎和研磨制成水泥熟料。可同时实现赤泥中钠和铁的提取，工艺步骤简单，钠碱和铁的提取率较高，赤泥利用率达100％。
METHOD OF VORTEX MELTING, REDUCING, DEALKALIZATION, IRON EXTRACTION AND DIRECT CEMENT PRODUCTION OF HIGH-IRON RED MUD
A method of vortex melting, reducing, dealkalization, iron extraction and direct cement production of high-iron red mud, performed according to the following steps: (1) preparing raw material high-iron red mud; (2) drying the raw material, obtaining a dewatered raw material; mixing the dewatered raw material with a solid carbon reducing agent and a slagging agent, preparing a mixture, spraying into a vortex center of a vortex stirring high-temperature oven, performing vortex stirring and reducing; (3) layering molten iron and molten slag formed after reducing, continuing overflow separation; adding ferrochrome and ferromanganese to the molten iron, forming a wear-resistant cast iron product; (4) adjusting components of slag in a melting furnace, causing the slag to meet cement clinker requirements, air cooling, then crushing and grinding into cement clinker. The present invention can simultaneously realize extraction of sodium and iron from red mud, the process steps are simple, sodium base and iron extraction rates are relatively high, and a red mud utilization rate reaches 100%.
L'invention concerne un procédé de fusion tourbillonnaire, de réduction, de désalcalinisation, d'extraction de fer et de production directe de ciment à partir de boues rouges à forte teneur en fer, mis en œuvre selon les étapes suivantes consistant à : (1) préparer une matière première à base de boues rouges à forte teneur en fer ; (2) sécher la matière première, obtenir une matière première égouttée ; mélanger la matière première égouttée avec un agent réducteur carboné solide et un agent scorifiant, préparer un mélange, pulvériser au centre d'un tourbillon d'un four à haute température à agitation tourbillonnaire, mettre en œuvre une agitation tourbillonnaire et une réduction ; (3) superposer le fer fondu et les scories fondues formés après réduction, poursuivre la séparation par débordement ; ajouter du ferrochrome et du ferromanganèse au fer fondu, former un produit en fonte résistant à l'usure ; (4) ajuster les composants des scories dans un four de fusion, amener les scories à être conformes aux exigences d'un clinker, refroidir par air, puis concasser et broyer pour obtenir un clinker. La présente invention permet une mise en œuvre simultanée d'une extraction de sodium et de fer à partir de boues rouges, les étapes du procédé sont simples, les taux d'extraction de la base sodique et du fer sont relativement élevés et le taux d'utilisation des boues rouges atteint 100 %.
一种高铁赤泥涡流熔融还原脱碱提铁直接水泥化的方法，按以下步骤进行：(1)准备原料高铁赤泥；(2)原料干燥获得脱水原料；脱水原料与固态碳质还原剂和造渣剂混料制成混合料，喷吹到涡流搅拌高温炉的漩涡中心，进行涡流搅拌还原；(3)还原后形成的铁水与熔融渣分层，连续溢流分离；向铁水中加入铬铁和锰铁制成耐磨铸铁产品；(4)熔融渣在熔炼炉中调整组分使其符合水泥熟料要求，空冷后破碎和研磨制成水泥熟料。可同时实现赤泥中钠和铁的提取，工艺步骤简单，钠碱和铁的提取率较高，赤泥利用率达100％。
METHOD OF VORTEX MELTING, REDUCING, DEALKALIZATION, IRON EXTRACTION AND DIRECT CEMENT PRODUCTION OF HIGH-IRON RED MUD
PROCÉDÉ DE FUSION TOURBILLONNAIRE, DE RÉDUCTION, DE DÉSALCALINISATION, D'EXTRACTION DE FER ET DE PRODUCTION DIRECTE DE CIMENT À PARTIR DE BOUES ROUGES À FORTE TENEUR EN FER
一种高铁赤泥涡流熔融还原脱碱提铁直接水泥化的方法
ZHANG TINGAN (author) / DOU ZHIHE (author) / LIU YAN (author) / LV GUOZHI (author) / ZHANG ZIMU (author) / ZHAO QIUYUE (author) / FU DAXUE (author) / ZHANG WEIGUANG (author)
2020-10-15
Patent
Electronic Resource
Chinese
High-iron red mud dealkalization resource utilization process method and application thereof
| European Patent Office | 2024
Dealkalization of Red Mud by Carbide Slag and Flue Gas
| Wiley | 2018
Powdery lime slurrying system for Bayer process red mud dealkalization
| European Patent Office | 2024
Iron aluminate cement water reducing agent and preparation method thereof
| European Patent Office | 2024