SINTERED BODY, POWDER, AND METHOD FOR PRODUCING SAME
Provided are at least any one of a raw material for obtaining a zirconia sintered body which is obtained by pressureless sintering and has a high fracture toughness value measured by the SEPB method, a sintered body obtained by the raw material, and a method for producing the same. The sintered body is characterized by comprising zirconia which contains a stabilizer and having a monoclinic ratio of 0.5% or more. Such a sintered body is preferably obtained by a production method which is characterized by using a powder characterized by comprising a stabilizer and containing zirconia having a monoclinic ratio of over 70%, and in that the monoclinic zirconia has a crystallite diameter of over 23 nm and 80 nm or less.
L'invention concerne au moins l'une quelconque d'une matière première pour obtenir un corps fritté de zircone qui est obtenu par frittage sans pression et présente une valeur de ténacité à la rupture élevée mesurée par le procédé SEPB, un corps fritté obtenu par la matière première, et un procédé de production de celui-ci. Le corps fritté est caractérisé en ce qu'il comprend de la zircone qui contient un stabilisant et a un rapport monoclinique de 0,5 % ou plus. Un tel corps fritté est de préférence obtenu par un procédé de production qui est caractérisé par l'utilisation d'une poudre caractérisée en ce qu'elle comprend un stabilisant et contenant de la zircone ayant un rapport monoclinique supérieur à 70 %, et en ce que la zircone monoclinique a un diamètre de cristallite supérieur à 23 nm et inférieur ou égal à 80 nm.
常圧焼結によって得られるジルコニア焼結体であって、ＳＥＰＢ法により測定される破壊靭性値が高いジルコニア焼結体を得るための原料、当該原料から得られる焼結体、及びこれらの製造方法の少なくともいずれかを提供する。 安定化剤を含有するジルコニアを含み、単斜晶率が０．５％以上であることを特徴とする焼結体。このような焼結体は、安定化剤を含有し、単斜晶率が７０％を超えるジルコニアを含み、単斜晶ジルコニアの結晶子径が２３ｎｍを超え８０ｎｍ以下であることを特徴とする粉末を使用することを特徴とする製造方法により得られることが好ましい。
SINTERED BODY, POWDER, AND METHOD FOR PRODUCING SAME
Provided are at least any one of a raw material for obtaining a zirconia sintered body which is obtained by pressureless sintering and has a high fracture toughness value measured by the SEPB method, a sintered body obtained by the raw material, and a method for producing the same. The sintered body is characterized by comprising zirconia which contains a stabilizer and having a monoclinic ratio of 0.5% or more. Such a sintered body is preferably obtained by a production method which is characterized by using a powder characterized by comprising a stabilizer and containing zirconia having a monoclinic ratio of over 70%, and in that the monoclinic zirconia has a crystallite diameter of over 23 nm and 80 nm or less.
L'invention concerne au moins l'une quelconque d'une matière première pour obtenir un corps fritté de zircone qui est obtenu par frittage sans pression et présente une valeur de ténacité à la rupture élevée mesurée par le procédé SEPB, un corps fritté obtenu par la matière première, et un procédé de production de celui-ci. Le corps fritté est caractérisé en ce qu'il comprend de la zircone qui contient un stabilisant et a un rapport monoclinique de 0,5 % ou plus. Un tel corps fritté est de préférence obtenu par un procédé de production qui est caractérisé par l'utilisation d'une poudre caractérisée en ce qu'elle comprend un stabilisant et contenant de la zircone ayant un rapport monoclinique supérieur à 70 %, et en ce que la zircone monoclinique a un diamètre de cristallite supérieur à 23 nm et inférieur ou égal à 80 nm.
常圧焼結によって得られるジルコニア焼結体であって、ＳＥＰＢ法により測定される破壊靭性値が高いジルコニア焼結体を得るための原料、当該原料から得られる焼結体、及びこれらの製造方法の少なくともいずれかを提供する。 安定化剤を含有するジルコニアを含み、単斜晶率が０．５％以上であることを特徴とする焼結体。このような焼結体は、安定化剤を含有し、単斜晶率が７０％を超えるジルコニアを含み、単斜晶ジルコニアの結晶子径が２３ｎｍを超え８０ｎｍ以下であることを特徴とする粉末を使用することを特徴とする製造方法により得られることが好ましい。
SINTERED BODY, POWDER, AND METHOD FOR PRODUCING SAME
CORPS FRITTÉ, POUDRE ET PROCÉDÉ DE PRODUCTION ASSOCIÉ
焼結体、粉末及びその製造方法
MATSUI KOJI (author) / HOSOI KOHEI (author)
2020-10-29
Patent
Electronic Resource
Japanese
Sintered body, method for producing sintered body, powder, and sintered body
| European Patent Office | 2024
Powder composition, pre-sintered body, sintered body, and method for producing same
| European Patent Office | 2024
SINTERED BODY, POWDER, AND METHOD FOR PRODUCING THE SAME
| European Patent Office | 2021