HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
The present invention relates to the technical field of high-entropy ceramics, and specifically disclosed is a high-entropy rare earth-toughened tantalate ceramic. The ceramic is prepared by sintering Ta2O5 powder and x types of different RE2O3 powder, wherein 4≤x≤9, and the molar ratio of the RE2O3 powder is 1. RE2O3 powder and Ta2O5 powder having the molar ratio of RE to Ta being 1:1 are weighed, a solvent is added for mixing, and ball milling is performed by a ball mill to obtain mixed powder M; the powder M is dried at a temperature of 650-850°C for 1.5-2 h to obtain dried powder; the powder is sieved to obtain powder N, the powder N is put in a mold for first pressing to obtain a rough blank, and the rough blank is then pressed for the second time to obtain a compact blank; the compact blank is sintered to obtain the high-entropy rare earth-toughened tantalate ceramic. The high-entropy ceramic has higher hardness and toughness.
La présente invention relève du domaine technique des céramiques à entropie élevée, et concerne spécifiquement une céramique de tantalate à entropie élevée durcie par des terres rares. Le procédé de préparation de la céramique consiste à : fritter une poudre de Ta2O5 et x types différents de poudre de RE2O3, 4 ≤ x ≤ 9, et le rapport molaire de la poudre de RE2O3 étant de 1 ; peser la poudre de RE2O3 et la poudre de Ta2O5 présentant le rapport molaire RE sur Ta de 1:1, ajouter un solvant en vue d'un mélange, et mettre en oeuvre un broyage à boulets par un broyeur à boulets afin d'obtenir une poudre mélangée M ; sécher la poudre M à une température comprise entre 650 et 850°C pendant 1,5 à 2 h afin d'obtenir une poudre séchée ; tamiser la poudre pour obtenir une poudre N, placer la poudre N dans un moule pour un premier pressage afin d'obtenir une ébauche crue, et presser ensuite l'ébauche crue pendant une seconde durée afin d'obtenir une ébauche compacte ; fritter l'ébauche compacte pour obtenir la céramique de tantalate à entropie élevée durcie par des terres rares. Cette céramique à entropie élevée présente une dureté et une ténacité supérieures.
高熵陶瓷技术领域，具体公开了一种高熵稀土增韧钽酸盐陶瓷，该陶瓷由Ta2O5粉体和x种不同RE2O3粉体烧结而成，其中4≤x≤9，各RE2O3粉体的摩尔比为1。称取RE∶Ta的摩尔比为1∶1的RE2O3粉末和Ta2O5粉末，加入溶剂混合，采用球磨机进行球磨，得到混合粉末M；将粉末M进行干燥处理，干燥温度为650～850℃，干燥时间为1.5～2h，得到干燥的粉末；将粉末进行过筛处理，得到粉末N，将粉末N置于模具内进行第一次压制，得粗坯，后将粗坯进行第二次压制，得致密胚体；将致密胚体进行烧结得到一种高熵稀土增韧钽酸盐陶瓷；该高熵陶瓷具有较高的硬度和韧性。
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
The present invention relates to the technical field of high-entropy ceramics, and specifically disclosed is a high-entropy rare earth-toughened tantalate ceramic. The ceramic is prepared by sintering Ta2O5 powder and x types of different RE2O3 powder, wherein 4≤x≤9, and the molar ratio of the RE2O3 powder is 1. RE2O3 powder and Ta2O5 powder having the molar ratio of RE to Ta being 1:1 are weighed, a solvent is added for mixing, and ball milling is performed by a ball mill to obtain mixed powder M; the powder M is dried at a temperature of 650-850°C for 1.5-2 h to obtain dried powder; the powder is sieved to obtain powder N, the powder N is put in a mold for first pressing to obtain a rough blank, and the rough blank is then pressed for the second time to obtain a compact blank; the compact blank is sintered to obtain the high-entropy rare earth-toughened tantalate ceramic. The high-entropy ceramic has higher hardness and toughness.
La présente invention relève du domaine technique des céramiques à entropie élevée, et concerne spécifiquement une céramique de tantalate à entropie élevée durcie par des terres rares. Le procédé de préparation de la céramique consiste à : fritter une poudre de Ta2O5 et x types différents de poudre de RE2O3, 4 ≤ x ≤ 9, et le rapport molaire de la poudre de RE2O3 étant de 1 ; peser la poudre de RE2O3 et la poudre de Ta2O5 présentant le rapport molaire RE sur Ta de 1:1, ajouter un solvant en vue d'un mélange, et mettre en oeuvre un broyage à boulets par un broyeur à boulets afin d'obtenir une poudre mélangée M ; sécher la poudre M à une température comprise entre 650 et 850°C pendant 1,5 à 2 h afin d'obtenir une poudre séchée ; tamiser la poudre pour obtenir une poudre N, placer la poudre N dans un moule pour un premier pressage afin d'obtenir une ébauche crue, et presser ensuite l'ébauche crue pendant une seconde durée afin d'obtenir une ébauche compacte ; fritter l'ébauche compacte pour obtenir la céramique de tantalate à entropie élevée durcie par des terres rares. Cette céramique à entropie élevée présente une dureté et une ténacité supérieures.
高熵陶瓷技术领域，具体公开了一种高熵稀土增韧钽酸盐陶瓷，该陶瓷由Ta2O5粉体和x种不同RE2O3粉体烧结而成，其中4≤x≤9，各RE2O3粉体的摩尔比为1。称取RE∶Ta的摩尔比为1∶1的RE2O3粉末和Ta2O5粉末，加入溶剂混合，采用球磨机进行球磨，得到混合粉末M；将粉末M进行干燥处理，干燥温度为650～850℃，干燥时间为1.5～2h，得到干燥的粉末；将粉末进行过筛处理，得到粉末N，将粉末N置于模具内进行第一次压制，得粗坯，后将粗坯进行第二次压制，得致密胚体；将致密胚体进行烧结得到一种高熵稀土增韧钽酸盐陶瓷；该高熵陶瓷具有较高的硬度和韧性。
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
CÉRAMIQUE DE TANTALATE À ENTROPIE ÉLEVÉE DURCIE PAR DES TERRES RARES ET SON PROCÉDÉ DE PRÉPARATION
一种高熵稀土增韧钽酸盐陶瓷及其制备方法
FENG JING (author) / ZHOU YUNXUAN (author) / CHONG XIAOYU (author) / WU PENG (author) / CHEN LIN (author) / WANG JUN (author)
2020-12-24
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
| European Patent Office | 2022
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
| European Patent Office | 2022
High-entropy rare earth tantalate ceramic material and preparation method thereof
| European Patent Office | 2022
Preparation method of fine-grain high-entropy rare earth tantalate ceramic
| European Patent Office | 2022
High-entropy rare earth tantalate ceramic coating material and preparation method thereof
| European Patent Office | 2024