METHODS OF MAKING SUSTAINABLE DUCTILE CAST CEMENTITIOUS STRUCTURE FOR CARBON DIOXIDE SEQUESTRATION
Methods of preparing a cementitious structure for carbon dioxide (CO2) sequestration are provided. The cementitious structure may be a cast in a mold. First, a cementitious composite material comprising binder and water is conditioned, for example, in a mold by exposing the cementitious composite material to ≥ about 50 % to ≤ about 80% relative humidity for ≥ about 3 hours to ≤ about 24 hours. The cementitious composite material is then dried to remove ≥ about 10% by weight of initial water in the cementitious composite material. The cementitious structure formed is capable of a carbon dioxide uptake level of greater than or equal to about 6% by weight binder. The cementitious structure has a tensile strain capacity of ≥ about 1% and a uniaxial tensile strength of ≥ about 1 MPa. The method may also include carbonating the cementitious structure, following by an optional further hydration process.
L'invention concerne des procédés de préparation d'une structure cimentaire pour la séquestration de dioxyde de carbone (CO2). La structure cimentaire peut être coulée dans un moule. Un matériau composite cimentaire comprenant un liant et de l'eau est tout d'abord conditionné, par exemple, dans un moule par exposition du matériau composite cimentaire à ≥ environ 50 % à ≤ environ 80 % d'humidité relative pendant ≥ environ 3 heures à ≤ environ 24 heures. Le matériau composite cimentaire est ensuite séché pour éliminer ≥ environ 10 % en poids d'eau initiale dans le matériau composite cimentaire. La structure cimentaire formée peut présenter un taux d'absorption de dioxyde de carbone supérieur ou égal à environ 6 % en poids de liant. La structure cimentaire possède une capacité de résistance à la traction ≥ environ 1 % et une résistance à la traction uniaxiale ≥ environ 1 MPa. Le procédé peut également comprendre la carbonatation de la structure cimentaire, suivie d'un éventuel processus d'hydratation supplémentaire.
METHODS OF MAKING SUSTAINABLE DUCTILE CAST CEMENTITIOUS STRUCTURE FOR CARBON DIOXIDE SEQUESTRATION
Methods of preparing a cementitious structure for carbon dioxide (CO2) sequestration are provided. The cementitious structure may be a cast in a mold. First, a cementitious composite material comprising binder and water is conditioned, for example, in a mold by exposing the cementitious composite material to ≥ about 50 % to ≤ about 80% relative humidity for ≥ about 3 hours to ≤ about 24 hours. The cementitious composite material is then dried to remove ≥ about 10% by weight of initial water in the cementitious composite material. The cementitious structure formed is capable of a carbon dioxide uptake level of greater than or equal to about 6% by weight binder. The cementitious structure has a tensile strain capacity of ≥ about 1% and a uniaxial tensile strength of ≥ about 1 MPa. The method may also include carbonating the cementitious structure, following by an optional further hydration process.
L'invention concerne des procédés de préparation d'une structure cimentaire pour la séquestration de dioxyde de carbone (CO2). La structure cimentaire peut être coulée dans un moule. Un matériau composite cimentaire comprenant un liant et de l'eau est tout d'abord conditionné, par exemple, dans un moule par exposition du matériau composite cimentaire à ≥ environ 50 % à ≤ environ 80 % d'humidité relative pendant ≥ environ 3 heures à ≤ environ 24 heures. Le matériau composite cimentaire est ensuite séché pour éliminer ≥ environ 10 % en poids d'eau initiale dans le matériau composite cimentaire. La structure cimentaire formée peut présenter un taux d'absorption de dioxyde de carbone supérieur ou égal à environ 6 % en poids de liant. La structure cimentaire possède une capacité de résistance à la traction ≥ environ 1 % et une résistance à la traction uniaxiale ≥ environ 1 MPa. Le procédé peut également comprendre la carbonatation de la structure cimentaire, suivie d'un éventuel processus d'hydratation supplémentaire.
METHODS OF MAKING SUSTAINABLE DUCTILE CAST CEMENTITIOUS STRUCTURE FOR CARBON DIOXIDE SEQUESTRATION
PROCÉDÉS DE FABRICATION D'UNE STRUCTURE CIMENTAIRE COULÉE DUCTILE DURABLE POUR LA SÉQUESTRATION DE DIOXYDE DE CARBONE
LI VICTOR C (author) / ELLIS BRIAN R (author) / ZHANG DUO (author)
2021-02-04
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
METHODS OF MAKING SUSTAINABLE DUCTILE CAST CEMENTITIOUS STRUCTURE FOR CARBON DIOXIDE SEQUESTRATION
| European Patent Office | 2022
Carbon Dioxide Sequestration in Cementitious Construction Materials
| UB Braunschweig | 2018
ENHANCED CARBONATION AND CARBON SEQUESTRATION IN CEMENTITIOUS BINDERS
| European Patent Office | 2016
ENHANCED CARBONATION AND CARBON SEQUESTRATION IN CEMENTITIOUS BINDERS
| European Patent Office | 2017