METHOD FOR DECOMPOSING AND CALCINING CALCIUM OXIDE OUTSIDE POWDER MULTI-STAGE SUSPENSION PREHEATING KILN
A method for decomposing and calcining calcium oxide outside of a powder multi-stage suspension preheating kiln, comprising the following steps: feeding limestone powder into a multi-stage suspension preheating kiln (3) and preheating to 800-900°C; feeding the preheated material into a decomposition furnace (4) and calcining at 900-1100°C for 25-35s; and feeding the calcined material into a rotary kiln (6), calcining at 1100-1300°C for 25-35 min, then cooling to obtain calcium oxide. The described method transforms the traditional method of directly firing lump limestone into grinding limestone to a powder and using suspension preheating; a decomposition furnace performs calcining and decomposition, and a rotary kiln performs calcining and curing to obtain powdered calcium oxide; and the single-line production capacity of the described method is greater than that of the traditional method.
L'invention concerne un procédé de décomposition et de calcination d'oxyde de calcium à l'extérieur d'un four à préchauffage de suspension à étages multiples pour poudre, comprenant les étapes suivantes : introduction de poudre de calcaire dans un four à préchauffage de suspension à étages multiples (3) et préchauffage à 800 à 900 °C ; introduction du matériau préchauffé dans un four de décomposition (4) et calcination à 900 à 1100 °C pendant 25 à 35 s ; et introduction du matériau calciné dans un four rotatif (6), calcination à 1100 à 1300 °C pendant 25 à 35 min, puis refroidissement pour obtenir de l'oxyde de calcium. Le procédé décrit transforme le procédé traditionnel consistant à directement cuire le calcaire en morceaux en un procédé consistant à broyer le calcaire en une poudre et utiliser un préchauffage de suspension ; un four de décomposition effectue une calcination et une décomposition, et un four rotatif effectue une calcination et un durcissement pour obtenir de l'oxyde de calcium en poudre ; et la capacité de production en ligne unique du procédé décrit est supérieure à celle du procédé traditionnel.
一种粉体多级悬浮预热窑外分解煅烧氧化钙的方法，包括以下步骤：将石灰石粉末送至多级悬浮预热窑（3）中预热至800～900℃；将预热后的物料送至分解炉（4），在900～1100℃下煅烧25～35s；将煅烧后的物料送至回转窑（6）中，在1100～1300℃下煅烧25～35min，冷却，得氧化钙。该方法将传统块状石灰石直接烧制改为将石灰石粉磨成粉体状采用悬浮预热，分解炉煅烧分解以及回转窑煅烧熟化制得粉状氧化钙，单线生产能力高于传统方法。
METHOD FOR DECOMPOSING AND CALCINING CALCIUM OXIDE OUTSIDE POWDER MULTI-STAGE SUSPENSION PREHEATING KILN
A method for decomposing and calcining calcium oxide outside of a powder multi-stage suspension preheating kiln, comprising the following steps: feeding limestone powder into a multi-stage suspension preheating kiln (3) and preheating to 800-900°C; feeding the preheated material into a decomposition furnace (4) and calcining at 900-1100°C for 25-35s; and feeding the calcined material into a rotary kiln (6), calcining at 1100-1300°C for 25-35 min, then cooling to obtain calcium oxide. The described method transforms the traditional method of directly firing lump limestone into grinding limestone to a powder and using suspension preheating; a decomposition furnace performs calcining and decomposition, and a rotary kiln performs calcining and curing to obtain powdered calcium oxide; and the single-line production capacity of the described method is greater than that of the traditional method.
L'invention concerne un procédé de décomposition et de calcination d'oxyde de calcium à l'extérieur d'un four à préchauffage de suspension à étages multiples pour poudre, comprenant les étapes suivantes : introduction de poudre de calcaire dans un four à préchauffage de suspension à étages multiples (3) et préchauffage à 800 à 900 °C ; introduction du matériau préchauffé dans un four de décomposition (4) et calcination à 900 à 1100 °C pendant 25 à 35 s ; et introduction du matériau calciné dans un four rotatif (6), calcination à 1100 à 1300 °C pendant 25 à 35 min, puis refroidissement pour obtenir de l'oxyde de calcium. Le procédé décrit transforme le procédé traditionnel consistant à directement cuire le calcaire en morceaux en un procédé consistant à broyer le calcaire en une poudre et utiliser un préchauffage de suspension ; un four de décomposition effectue une calcination et une décomposition, et un four rotatif effectue une calcination et un durcissement pour obtenir de l'oxyde de calcium en poudre ; et la capacité de production en ligne unique du procédé décrit est supérieure à celle du procédé traditionnel.
一种粉体多级悬浮预热窑外分解煅烧氧化钙的方法，包括以下步骤：将石灰石粉末送至多级悬浮预热窑（3）中预热至800～900℃；将预热后的物料送至分解炉（4），在900～1100℃下煅烧25～35s；将煅烧后的物料送至回转窑（6）中，在1100～1300℃下煅烧25～35min，冷却，得氧化钙。该方法将传统块状石灰石直接烧制改为将石灰石粉磨成粉体状采用悬浮预热，分解炉煅烧分解以及回转窑煅烧熟化制得粉状氧化钙，单线生产能力高于传统方法。
METHOD FOR DECOMPOSING AND CALCINING CALCIUM OXIDE OUTSIDE POWDER MULTI-STAGE SUSPENSION PREHEATING KILN
PROCÉDÉ DE DÉCOMPOSITION ET DE CALCINATION D'OXYDE DE CALCIUM À L'EXTÉRIEUR D'UN FOUR À PRÉCHAUFFAGE DE SUSPENSION À ÉTAGES MULTIPLES POUR POUDRE
一种粉体多级悬浮预热窑外分解煅烧氧化钙的方法
ZHUANG YAN (author) / ZHUANG LICHENG (author) / ZHUANG QIANCHENG (author)
2021-03-18
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2023
MULTI-STAGE SUSPENSION PREHEATING CEMENT KILN SYSTEM AND CONTROL METHOD THEREFOR
| European Patent Office | 2020
Lime kiln calcining process for active calcium oxide production
| European Patent Office | 2020
Multi-stage suspension preheating cement kiln system and control method thereof
| European Patent Office | 2020