PHASE CHANGE HEAT STORAGE SELF-FLOWING REFRACTORY CASTABLE AND PREPARATION METHOD THEREFOR
Disclosed are a phase change heat storage self-flowing refractory castable and a preparation method therefor. The method comprises: mixing 55-75 parts by mass of bauxite particles, 10-30 parts by mass of a fine bauxite powder, 6-10 parts by mass of α-alumina powder, 1-3 parts by mass of a silicon micropowder and 4-6 parts by mass of a calcium aluminate cement as raw materials to obtain a mixed material; adding 0.1-0.3 parts by mass of a water reducing agent and 6-7 parts by mass of water to the mixed material, and stirring same until uniform to obtain a bauxite-based self-flowing castable; then stacking 55-75 parts by mass of alloy @ ceramic large capsule particles in a mold to obtain a castable framework; and then pouring the bauxite-based self-flowing castable into the castable framework to prepare a phase change heat storage self-flowing refractory castable. The process thereof is simple, and the castable has a large heat storage density, a high strength, a good thermal shock resistance, a high thermal efficiency in high-temperature applications, and a stable temperature.
L'invention concerne un matériau coulable réfractaire à auto-écoulement à stockage thermique à changement de phase et un procédé de préparation s'y rapportant. Le procédé comprend : le mélange de 55 à 75 parties en masse de particules de bauxite, de 10 à 30 parties en masse d'une fine poudre de bauxite, de 6 à 10 parties en masse de poudre d'alumine α, de 1 à 3 parties en masse d'une micropoudre de silicium et de 4 à 6 parties en masse d'un ciment d'aluminate de calcium en tant que matières premières pour obtenir une matière mélangée ; l'addition de 0,1 à 0,3 partie en masse d'un agent réducteur d'eau et de 6 à 7 parties en masse d'eau dans la matière mélangée et l'agitation de ceux-ci jusqu'à l'homogénéité pour obtenir un matériau coulable à auto-écoulement à base de bauxite ; puis l'empilement de 55 à 75 parties en masse de particules de grosses capsules d'alliage dans de la céramique dans un moule pour obtenir une structure de matériau coulable ; puis le versement du matériau coulable à auto-écoulement à base de bauxite dans la structure de matériau coulable pour préparer un matériau coulable réfractaire à auto-écoulement à stockage thermique à changement de phase. Le procédé selon l'invention est simple et le matériau coulable a une grande densité de stockage thermique, une haute résistance, une bonne résistance aux chocs thermiques, un haut rendement thermique dans des applications à haute température et une température stable.
一种相变蓄热自流式耐火浇注料及其制备方法。以55～75质量份的矾土颗粒、10～30质量份的矾土细粉、6～10质量份的α-氧化铝粉、1～3质量份的硅微粉和4～6质量份的铝酸钙水泥为原料，混合得混合料。向混合料中加入0.1～0.3质量份的减水剂和6～7质量份的水，搅拌均匀，即得矾土基自流式浇注料；再将55～75质量份的合金@陶瓷大胶囊颗粒堆积于模具中，得到浇注料骨架；然后将所述矾土基自流式浇注料浇注到所述浇注料骨架中，制得相变蓄热自流式耐火浇注料。其工艺简单，浇注料蓄热密度大、强度高、抗热震性能好、高温应用时热效率高、温度稳定。
PHASE CHANGE HEAT STORAGE SELF-FLOWING REFRACTORY CASTABLE AND PREPARATION METHOD THEREFOR
Disclosed are a phase change heat storage self-flowing refractory castable and a preparation method therefor. The method comprises: mixing 55-75 parts by mass of bauxite particles, 10-30 parts by mass of a fine bauxite powder, 6-10 parts by mass of α-alumina powder, 1-3 parts by mass of a silicon micropowder and 4-6 parts by mass of a calcium aluminate cement as raw materials to obtain a mixed material; adding 0.1-0.3 parts by mass of a water reducing agent and 6-7 parts by mass of water to the mixed material, and stirring same until uniform to obtain a bauxite-based self-flowing castable; then stacking 55-75 parts by mass of alloy @ ceramic large capsule particles in a mold to obtain a castable framework; and then pouring the bauxite-based self-flowing castable into the castable framework to prepare a phase change heat storage self-flowing refractory castable. The process thereof is simple, and the castable has a large heat storage density, a high strength, a good thermal shock resistance, a high thermal efficiency in high-temperature applications, and a stable temperature.
L'invention concerne un matériau coulable réfractaire à auto-écoulement à stockage thermique à changement de phase et un procédé de préparation s'y rapportant. Le procédé comprend : le mélange de 55 à 75 parties en masse de particules de bauxite, de 10 à 30 parties en masse d'une fine poudre de bauxite, de 6 à 10 parties en masse de poudre d'alumine α, de 1 à 3 parties en masse d'une micropoudre de silicium et de 4 à 6 parties en masse d'un ciment d'aluminate de calcium en tant que matières premières pour obtenir une matière mélangée ; l'addition de 0,1 à 0,3 partie en masse d'un agent réducteur d'eau et de 6 à 7 parties en masse d'eau dans la matière mélangée et l'agitation de ceux-ci jusqu'à l'homogénéité pour obtenir un matériau coulable à auto-écoulement à base de bauxite ; puis l'empilement de 55 à 75 parties en masse de particules de grosses capsules d'alliage dans de la céramique dans un moule pour obtenir une structure de matériau coulable ; puis le versement du matériau coulable à auto-écoulement à base de bauxite dans la structure de matériau coulable pour préparer un matériau coulable réfractaire à auto-écoulement à stockage thermique à changement de phase. Le procédé selon l'invention est simple et le matériau coulable a une grande densité de stockage thermique, une haute résistance, une bonne résistance aux chocs thermiques, un haut rendement thermique dans des applications à haute température et une température stable.
一种相变蓄热自流式耐火浇注料及其制备方法。以55～75质量份的矾土颗粒、10～30质量份的矾土细粉、6～10质量份的α-氧化铝粉、1～3质量份的硅微粉和4～6质量份的铝酸钙水泥为原料，混合得混合料。向混合料中加入0.1～0.3质量份的减水剂和6～7质量份的水，搅拌均匀，即得矾土基自流式浇注料；再将55～75质量份的合金@陶瓷大胶囊颗粒堆积于模具中，得到浇注料骨架；然后将所述矾土基自流式浇注料浇注到所述浇注料骨架中，制得相变蓄热自流式耐火浇注料。其工艺简单，浇注料蓄热密度大、强度高、抗热震性能好、高温应用时热效率高、温度稳定。
PHASE CHANGE HEAT STORAGE SELF-FLOWING REFRACTORY CASTABLE AND PREPARATION METHOD THEREFOR
MATÉRIAU COULABLE RÉFRACTAIRE À AUTO-ÉCOULEMENT À STOCKAGE THERMIQUE À CHANGEMENT DE PHASE ET PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT
一种相变蓄热自流式耐火浇注料及其制备方法
ZHANG MEIJIE (author) / XIA QIULIN (author) / GU HUAZHI (author) / HUANG AO (author) / FU LVPING (author) / YANG SHUANG (author)
2021-07-29
Patent
Electronic Resource
Chinese