Provided are a concrete admixture anti-seepage and anti-cracking shrinkage-reducing agent and preparation method thereof. The anti-seepage and anti-cracking shrinkage-reducing agent contains the following components: 35–45 parts by weight of alkali-modified diatomaceous earth, 15–22 parts by weight of magnesium oxide, 13–20 parts by weight of vermiculite, 8–11 parts by weight of borax, 3–9 parts by weight of sodium hexametaphosphate, and 7–13 parts by weight of citric-acid modified starch. The anti-seepage and anti-cracking shrinkage-reducing agent is used as an internal admixture when mixed with cement and is used in concrete, can fully improve the working performance of fresh concrete, reduce the shrinkage of concrete during the hardening process, and also significantly improve the compressive strength, tensile strength, hardness, and impermeability of hardened concrete, thereby greatly improving the durability of a concrete workpiece. In addition, the method for preparing the concrete admixture anti-seepage and anti-cracking shrinkage-reducing agent is simple and quick, and is suitable for large-scale industrial applications.
L'invention concerne un agent de réduction de retrait anti-suintement et anti-fissuration d'adjuvant de béton et son procédé de préparation. L'agent de réduction de retrait anti-suintement et anti-fissuration contient les composants suivants: 35 à 45 parties en poids de terre de diatomées modifiée par un alcali, 15 à 22 parties en poids d'oxyde de magnésium, 13 à 20 parties en poids de vermiculite, 8 à 11 parties en poids de borax, 3 à 9 parties en poids d'hexamétaphosphate de sodium et 7 à 13 parties en poids d'amidon modifié par de l'acide citrique. L'agent de réduction de retrait anti-suintement et anti-fissuration est utilisé en tant qu'adjuvant interne lorsqu'il est mélangé avec du ciment et est utilisé dans du béton, peut améliorer complètement les performances de travail du béton frais, réduire le retrait du béton pendant le processus de durcissement, et améliorer également significativement la résistance à la compression, la résistance à la traction, la dureté et l'imperméabilité du béton durci, ce qui permet d'améliorer considérablement la durabilité d'une pièce à travailler en béton. De plus, le procédé de préparation de l'agent de réduction de retrait anti-suintement et anti-fissuration d'adjuvant de béton est simple et rapide, et est approprié pour des applications industrielles à grande échelle.
一种混凝土内掺型防渗抗裂减缩剂及其制备方法。所述防渗抗裂减缩剂包含以下组分：碱改性硅藻土35～45重量份，氧化镁15～22重量份，蛭石13～20重量份，硼砂8～11重量份，六偏磷酸钠3～9重量份，柠檬酸改性淀粉7～13重量份。所述的防渗抗裂减缩剂作为内掺剂掺入水泥应用于混凝土中，可以充分改善新拌混凝土的工作性能，降低混凝土在硬化过程中的收缩程度，同时还极大地提高了硬化混凝土的抗压强度、抗拉强度、硬度、抗渗性等，从而大大提高混凝土工件的耐久性。此外，所述混凝土内掺型防渗抗裂减缩剂的制备方法简单快捷，适于工业上大规模应用。
Provided are a concrete admixture anti-seepage and anti-cracking shrinkage-reducing agent and preparation method thereof. The anti-seepage and anti-cracking shrinkage-reducing agent contains the following components: 35–45 parts by weight of alkali-modified diatomaceous earth, 15–22 parts by weight of magnesium oxide, 13–20 parts by weight of vermiculite, 8–11 parts by weight of borax, 3–9 parts by weight of sodium hexametaphosphate, and 7–13 parts by weight of citric-acid modified starch. The anti-seepage and anti-cracking shrinkage-reducing agent is used as an internal admixture when mixed with cement and is used in concrete, can fully improve the working performance of fresh concrete, reduce the shrinkage of concrete during the hardening process, and also significantly improve the compressive strength, tensile strength, hardness, and impermeability of hardened concrete, thereby greatly improving the durability of a concrete workpiece. In addition, the method for preparing the concrete admixture anti-seepage and anti-cracking shrinkage-reducing agent is simple and quick, and is suitable for large-scale industrial applications.
L'invention concerne un agent de réduction de retrait anti-suintement et anti-fissuration d'adjuvant de béton et son procédé de préparation. L'agent de réduction de retrait anti-suintement et anti-fissuration contient les composants suivants: 35 à 45 parties en poids de terre de diatomées modifiée par un alcali, 15 à 22 parties en poids d'oxyde de magnésium, 13 à 20 parties en poids de vermiculite, 8 à 11 parties en poids de borax, 3 à 9 parties en poids d'hexamétaphosphate de sodium et 7 à 13 parties en poids d'amidon modifié par de l'acide citrique. L'agent de réduction de retrait anti-suintement et anti-fissuration est utilisé en tant qu'adjuvant interne lorsqu'il est mélangé avec du ciment et est utilisé dans du béton, peut améliorer complètement les performances de travail du béton frais, réduire le retrait du béton pendant le processus de durcissement, et améliorer également significativement la résistance à la compression, la résistance à la traction, la dureté et l'imperméabilité du béton durci, ce qui permet d'améliorer considérablement la durabilité d'une pièce à travailler en béton. De plus, le procédé de préparation de l'agent de réduction de retrait anti-suintement et anti-fissuration d'adjuvant de béton est simple et rapide, et est approprié pour des applications industrielles à grande échelle.
一种混凝土内掺型防渗抗裂减缩剂及其制备方法。所述防渗抗裂减缩剂包含以下组分：碱改性硅藻土35～45重量份，氧化镁15～22重量份，蛭石13～20重量份，硼砂8～11重量份，六偏磷酸钠3～9重量份，柠檬酸改性淀粉7～13重量份。所述的防渗抗裂减缩剂作为内掺剂掺入水泥应用于混凝土中，可以充分改善新拌混凝土的工作性能，降低混凝土在硬化过程中的收缩程度，同时还极大地提高了硬化混凝土的抗压强度、抗拉强度、硬度、抗渗性等，从而大大提高混凝土工件的耐久性。此外，所述混凝土内掺型防渗抗裂减缩剂的制备方法简单快捷，适于工业上大规模应用。
CONCRETE ADMIXTURE ANTI-SEEPAGE AND ANTI-CRACKING SHRINKAGE-REDUCING AGENT AND PREPARATION METHOD THEREOF
AGENT DE RÉDUCTION DE RETRAIT ANTI-SUINTEMENT ET ANTI-FISSURATION D'ADJUVANT DE BÉTON ET SON PROCÉDÉ DE PRÉPARATION
一种混凝土内掺型防渗抗裂减缩剂及其制备方法
YANG FEI (author)
2021-09-10
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Anti-cracking shrinkage-reducing concrete admixture and preparation method thereof
| European Patent Office | 2021
Concrete anti-cracking and anti-seepage admixture and preparation method thereof
| European Patent Office | 2021
Concrete anti-cracking and anti-seepage reinforcing agent and preparation method thereof
| European Patent Office | 2024
| European Patent Office | 2022
Efficient concrete anti-cracking and anti-seepage agent and preparation method thereof
| European Patent Office | 2021