HARD WEAR-RESISTANT POLISHED GLAZED CERAMIC TILE AND PREPARATION METHOD THEREFOR
Hard wear-resistant polished glazed ceramic tile and preparation method therefor The preparation method comprises the following steps: step (1), pressing powder to form a green body and then drying to form a green tile; step (2), applying ground coat enamel on a surface of the green tile; step (3), ink-jet printing a pattern on the green tile surface having the ground coat enamel, and applying isolation enamel; step (4), applying a polished glazed finish on the green tile surface having the isolation enamel; step (5), drying, firing, and polishing the green tile having the polished glazed finish, thereby acquiring a hard wear-resistant polished glazed ceramic tile, wherein the phase composition of the polished glazed finish comprises the following components in percentage by mass: 10-20% of corundum, 20-30% of hyalophane, 0.5-1% of hematite, and 50-68% of amorphous phase. The adjusted formula of the polished glazed finish and the enamel application method improves wear-resistance of the polished glazed finish.
L'invention concerne une tuile de céramique émaillée polie dure, résistant à l'usure et un procédé de préparation associé. Le procédé de préparation comprend les étapes suivantes : étape (1), presser de la poudre pour former un corps cru, puis sécher pour former une tuile crue; étape (2), appliquer de l'émail de fond sur une surface de la tuile crue; étape (3), imprimer par jet d'encre un motif sur la surface de le tuile crue présentant l'émail de fond et appliquer de l'émail isolant; étape (4), appliquer une finition émaillée polie sur la surface de la tuile crue présentant l'émail isolant; étape (5), sécher, cuire et polir la tuile crue présentant la finition émaillée polie, ce qui permet d'obtenir une tuile de céramique émaillée polie dure, résistant à l'usure, la composition de phase de la finition émaillée polie comprenant les constituants suivants, en pourcentage en masse : 10-20 % de corindon, 20-30 % d'hyalophane, 0,5-1 % d'hématite et 50-68 % de phase amorphe. La formule ajustée de la finition émaillée polie et le procédé d'application d'émail améliorent la résistance à l'usure de la finition émaillée polie.
一种高硬度高耐磨全抛釉陶瓷砖及其制备方法。所述制备方法包括以下步骤：步骤(1)，将坯体粉料压制成型后干燥，形成砖坯；步骤(2)，在砖坯表面施底釉；步骤(3)，在施底釉后的砖坯表面喷墨打印图案，并施隔离釉；步骤(4)，在施隔离釉后的砖坯表面施全抛釉；步骤(5)，将施全抛釉后的砖坯干燥，烧成，抛光，获得高硬度高耐磨全抛釉陶瓷砖；所述全抛釉烧成后物相组成为：以质量百分比计，刚玉10～20％、钡冰长石20～30％、赤铁矿0.5～1％和非晶相50～68％。通过调整全抛釉配方和施釉方式等很好地改善了全抛釉的耐磨性。
HARD WEAR-RESISTANT POLISHED GLAZED CERAMIC TILE AND PREPARATION METHOD THEREFOR
Hard wear-resistant polished glazed ceramic tile and preparation method therefor The preparation method comprises the following steps: step (1), pressing powder to form a green body and then drying to form a green tile; step (2), applying ground coat enamel on a surface of the green tile; step (3), ink-jet printing a pattern on the green tile surface having the ground coat enamel, and applying isolation enamel; step (4), applying a polished glazed finish on the green tile surface having the isolation enamel; step (5), drying, firing, and polishing the green tile having the polished glazed finish, thereby acquiring a hard wear-resistant polished glazed ceramic tile, wherein the phase composition of the polished glazed finish comprises the following components in percentage by mass: 10-20% of corundum, 20-30% of hyalophane, 0.5-1% of hematite, and 50-68% of amorphous phase. The adjusted formula of the polished glazed finish and the enamel application method improves wear-resistance of the polished glazed finish.
L'invention concerne une tuile de céramique émaillée polie dure, résistant à l'usure et un procédé de préparation associé. Le procédé de préparation comprend les étapes suivantes : étape (1), presser de la poudre pour former un corps cru, puis sécher pour former une tuile crue; étape (2), appliquer de l'émail de fond sur une surface de la tuile crue; étape (3), imprimer par jet d'encre un motif sur la surface de le tuile crue présentant l'émail de fond et appliquer de l'émail isolant; étape (4), appliquer une finition émaillée polie sur la surface de la tuile crue présentant l'émail isolant; étape (5), sécher, cuire et polir la tuile crue présentant la finition émaillée polie, ce qui permet d'obtenir une tuile de céramique émaillée polie dure, résistant à l'usure, la composition de phase de la finition émaillée polie comprenant les constituants suivants, en pourcentage en masse : 10-20 % de corindon, 20-30 % d'hyalophane, 0,5-1 % d'hématite et 50-68 % de phase amorphe. La formule ajustée de la finition émaillée polie et le procédé d'application d'émail améliorent la résistance à l'usure de la finition émaillée polie.
一种高硬度高耐磨全抛釉陶瓷砖及其制备方法。所述制备方法包括以下步骤：步骤(1)，将坯体粉料压制成型后干燥，形成砖坯；步骤(2)，在砖坯表面施底釉；步骤(3)，在施底釉后的砖坯表面喷墨打印图案，并施隔离釉；步骤(4)，在施隔离釉后的砖坯表面施全抛釉；步骤(5)，将施全抛釉后的砖坯干燥，烧成，抛光，获得高硬度高耐磨全抛釉陶瓷砖；所述全抛釉烧成后物相组成为：以质量百分比计，刚玉10～20％、钡冰长石20～30％、赤铁矿0.5～1％和非晶相50～68％。通过调整全抛釉配方和施釉方式等很好地改善了全抛釉的耐磨性。
HARD WEAR-RESISTANT POLISHED GLAZED CERAMIC TILE AND PREPARATION METHOD THEREFOR
TUILE DE CÉRAMIQUE ÉMAILLÉE POLIE DURE RÉSISTANT À L'USURE ET PROCÉDÉ DE PRÉPARATION ASSOCIÉ
一种高硬度高耐磨全抛釉陶瓷砖及其制备方法
LIU YIJUN (author) / DENG LAIFU (author) / YANG YUANDONG (author) / WANG XIANCHAO (author) / ZHANG KELIN (author)
2021-12-30
Patent
Electronic Resource
Chinese
HARD WEAR-RESISTANT POLISHED GLAZED CERAMIC TILE AND PREPARATION METHOD THEREFOR
| European Patent Office | 2024
HARD WEAR-RESISTANT POLISHED GLAZED CERAMIC TILE AND PREPARATION METHOD THEREOF
| European Patent Office | 2023
HIGH-WEAR-RESISTANCE FAR-INFRARED CERAMIC POLISHED GLAZED TILE AND PREPARATION METHOD THEREFOR
| European Patent Office | 2021
HIGH-WEAR-RESISTANCE FAR-INFRARED CERAMIC POLISHED GLAZED TILE AND PREPARATION METHOD THEREFOR
| European Patent Office | 2024
HIGH-WEAR-RESISTANCE FAR-INFRARED CERAMIC POLISHED GLAZED TILE AND PREPARATION METHOD THEREFOR
| European Patent Office | 2023