Provided is a MnZn ferrite having both the superior mechanical property of a fracture toughness value, in a flat plate-like core, of 1.10 MPa•m1/2 or greater as measured in accordance with JIS R1607, and the excellent magnetic property, of a loss value of 450 kW/m3 or less at 100ºC, 300 kHz, and 100 mT, in a toroidal core fabricated under the same conditions. The MnZn ferrite comprises basic components, auxiliary components, and unavoidable impurities. The respective contents of P, B, Na, Mg, Al and K in the unavoidable impurities are suppressed such that P is less than 10 ppm by mass, B is less than 10 ppm by mass, Na is less than 200 ppm by mass, Mg is less than 200 ppm by mass, Al is less than 250 ppm by mass, and K is less than 100 ppm by mass.
L'invention fournit une ferrite à base de ＭｎＺｎ qui combine d'excellentes caractéristiques mécaniques telles que la valeur de ténacité de noyaux de forme plate mesurée conformément à ＪＩＳ Ｒ１６０７ est supérieure ou égale à １,１０ＭＰａ・ｍ1/2, et des caractéristiques magnétiques satisfaisantes telles que la valeur de perte à １００℃, ３００ｋＨｚ et １００ｍＴ de noyaux de forme toroïdale fabriqués dans des conditions identiques, est inférieure ou égale à ４５０ｋＷ／ｍ3. Plus précisément, l'invention concerne une ferrite à base de ＭｎＺｎ qui est constituée de composants de base, de composants secondaires et des impuretés inévitables. La teneur en Ｐ, Ｂ, Ｎａ, Ｍｇ, Ａｌ et Ｋ dans les impuretés inévitables, est restreinte de sorte que respectivement Ｐ représente moins de １０ ｐｐｍ en masse, Ｂ représente moins de １０ｐｐｍ en masse, Ｎａ représente moins de ２００ ｐｐｍ en masse, Ｍｇ représente moins de ２００ ｐｐｍ en masse, Ａｌ représente moins de ２５０ｐｐｍ en masse et Ｋ représente moins de １００ ｐｐｍ en masse.
平板状コアのＪＩＳ Ｒ１６０７に準拠して測定した破壊靭性値が１．１０ＭＰａ・ｍ1/2以上という優れた機械特性と、同条件で作製したトロイダル形状コアの１００℃、３００ｋＨｚ、１００ｍＴにおける損失値が４５０ｋＷ／ｍ3以下という良好な磁気特性とを併せ持つ、ＭｎＺｎ系フェライトを提供すること。 基本成分、副成分および不可避的不純物からなるＭｎＺｎ系フェライトであって、不可避的不純物におけるＰ、Ｂ、Ｎａ、Ｍｇ、ＡｌおよびＫの含有量をそれぞれ、Ｐ：１０ｍａｓｓ ｐｐｍ未満、Ｂ：１０ｍａｓｓ ｐｐｍ未満、Ｎａ：２００ｍａｓｓ ｐｐｍ未満、Ｍｇ：２００ｍａｓｓ ｐｐｍ未満、Ａｌ：２５０ｍａｓｓ ｐｐｍ未満およびＫ：１００ｍａｓｓ ｐｐｍ未満に抑制する、ＭｎＺｎ系フェライト。
MANGANESE-ZINC FERRITE
Provided is a MnZn ferrite having both the superior mechanical property of a fracture toughness value, in a flat plate-like core, of 1.10 MPa•m1/2 or greater as measured in accordance with JIS R1607, and the excellent magnetic property, of a loss value of 450 kW/m3 or less at 100ºC, 300 kHz, and 100 mT, in a toroidal core fabricated under the same conditions. The MnZn ferrite comprises basic components, auxiliary components, and unavoidable impurities. The respective contents of P, B, Na, Mg, Al and K in the unavoidable impurities are suppressed such that P is less than 10 ppm by mass, B is less than 10 ppm by mass, Na is less than 200 ppm by mass, Mg is less than 200 ppm by mass, Al is less than 250 ppm by mass, and K is less than 100 ppm by mass.
L'invention fournit une ferrite à base de ＭｎＺｎ qui combine d'excellentes caractéristiques mécaniques telles que la valeur de ténacité de noyaux de forme plate mesurée conformément à ＪＩＳ Ｒ１６０７ est supérieure ou égale à １,１０ＭＰａ・ｍ1/2, et des caractéristiques magnétiques satisfaisantes telles que la valeur de perte à １００℃, ３００ｋＨｚ et １００ｍＴ de noyaux de forme toroïdale fabriqués dans des conditions identiques, est inférieure ou égale à ４５０ｋＷ／ｍ3. Plus précisément, l'invention concerne une ferrite à base de ＭｎＺｎ qui est constituée de composants de base, de composants secondaires et des impuretés inévitables. La teneur en Ｐ, Ｂ, Ｎａ, Ｍｇ, Ａｌ et Ｋ dans les impuretés inévitables, est restreinte de sorte que respectivement Ｐ représente moins de １０ ｐｐｍ en masse, Ｂ représente moins de １０ｐｐｍ en masse, Ｎａ représente moins de ２００ ｐｐｍ en masse, Ｍｇ représente moins de ２００ ｐｐｍ en masse, Ａｌ représente moins de ２５０ｐｐｍ en masse et Ｋ représente moins de １００ ｐｐｍ en masse.
平板状コアのＪＩＳ Ｒ１６０７に準拠して測定した破壊靭性値が１．１０ＭＰａ・ｍ1/2以上という優れた機械特性と、同条件で作製したトロイダル形状コアの１００℃、３００ｋＨｚ、１００ｍＴにおける損失値が４５０ｋＷ／ｍ3以下という良好な磁気特性とを併せ持つ、ＭｎＺｎ系フェライトを提供すること。 基本成分、副成分および不可避的不純物からなるＭｎＺｎ系フェライトであって、不可避的不純物におけるＰ、Ｂ、Ｎａ、Ｍｇ、ＡｌおよびＫの含有量をそれぞれ、Ｐ：１０ｍａｓｓ ｐｐｍ未満、Ｂ：１０ｍａｓｓ ｐｐｍ未満、Ｎａ：２００ｍａｓｓ ｐｐｍ未満、Ｍｇ：２００ｍａｓｓ ｐｐｍ未満、Ａｌ：２５０ｍａｓｓ ｐｐｍ未満およびＫ：１００ｍａｓｓ ｐｐｍ未満に抑制する、ＭｎＺｎ系フェライト。
MANGANESE-ZINC FERRITE
FERRITE À BASE DE ＭＮＺＮ
ＭｎＺｎ系フェライト
YOSHIDA HIROFUMI (author) / NAKAMURA YUKIKO (author) / HIRATANI TATSUHIKO (author) / TAGAWA TETSUYA (author)
2022-01-20
Patent
Electronic Resource
Japanese
| European Patent Office | 2024
| European Patent Office | 2016
| European Patent Office | 2015
Preparation method of manganese zinc ferrite nanoparticles
| European Patent Office | 2015