HIGH-PURITY COMPACT CALCIUM HEXA-ALUMINATE-BASED REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
The present invention belongs to the technical field of refractory materials, and disclosed are a high-purity compact calcium hexa-aluminate-based refractory material, a preparation method therefor, and a working lining using same. The mixing ratio is adjusted according to the chemical composition of the final product to contain raw materials containing CaO, Al2O3 and ZrO2, the mixing ratio enabling the ratio of the chemical composition Al2O3:CaO:ZrO2 calculated according to parts by mass to be 45.5-95.5%:2.0-8.4%:0-50%; and the chemical composition are placed into a high-temperature furnace and a mold for hot-pressing, molding and sintering, wherein the temperature is increased while hot-pressing is carried out, the maximum temperature is 1550-1800°C, and the hot-pressing strength is 0.5-30 MPa. In the present invention, when no sintering agent is added, a hot-pressing sintering process is employed according to a proportion to obtain a high-purity compact calcium hexa-aluminate-based refractory material, and the refractory material has excellent resistance to molten steel erosion and thermal shock stability, and can be widely applied in metallurgy, building materials and petrochemical industries as well as other industries. The preparation method is scientific and reasonable, product purity is high, and the prepared refractory material product can increase a device operation period; in addition, production costs are reduced, and energy-saving and emission-reducing effects are achieved.
La présente invention appartient au domaine technique des matériaux réfractaires et concerne un matériau réfractaire compact de haute pureté à base d'hexa-aluminate de calcium, un procédé de préparation associé et un garnissage de travail l'utilisant. Le rapport de mélange est ajusté en fonction de la composition chimique du produit final pour contenir des matières premières contenant du CaO, de l'Al2O3 et du ZrO2, le rapport de mélange permettant au rapport de la composition chimique Al2O3:CaO:ZrO2, calculé selon des parties en masse, d'être de 45,5-95,5 %:2,0-8,4 %:0-50 % ; et la composition chimique étant placée dans un four à haute température et dans un moule pour le pressage à chaud, le moulage et le frittage, la température étant augmentée pendant que le pressage à chaud est effectué, la température maximale étant de 1550 à 1800°C et la force de pression à chaud étant de 0,5 à 30 MPa. Dans la présente invention, lorsqu'aucun agent de frittage n'est ajouté, un procédé de frittage par pressage à chaud est employé selon une proportion pour obtenir un matériau réfractaire compact de haute pureté à base d'hexa-aluminate de calcium et le matériau réfractaire présente une excellente résistance à l'érosion par l'acier fondu et une excellente stabilité aux chocs thermiques et peut être largement appliqué dans la métallurgie, les matériaux de construction et les industries pétrochimiques ainsi que dans d'autres industries. Le procédé de préparation est scientifique et raisonnable, la pureté du produit est élevée et le produit de matériau réfractaire préparé peut augmenter une période de fonctionnement du dispositif ; de plus, les coûts de production sont réduits et des effets d'économie d'énergie et de réduction d'émission sont obtenus.
本发明属于耐火材料技术领域，公开了一种高纯度致密六铝酸钙系耐火材料、其制备方法及使用其的工作衬，按照最终产品的化学成分调整好含CaO原料、含Al 2O 3原料、含ZrO 2原料的混合比例，所述混合比例使得按照质量份计算的化学成分Al 2O 3:CaO:ZrO 2的比例为45.5～95.5％：2.0～8.4％：0～50％，放入高温炉和模具中热压成型烧结，边升温边热压，最高温度为1550～1800℃、热压强度为0.5～30MPa。本发明在不添加烧结剂情况下，按照配比采用热压烧结工艺，获得高纯度致密六铝酸钙系耐火材料，该耐火材料具备出色的抵抗钢水侵蚀性能及热震稳定性，能广泛应用于冶金、建材和石化等行业。该制备方法科学合理、产品纯度高，并且所制得耐火材料制品能够增加设备运行周期，减少生产成本，达到节能减排效应。
HIGH-PURITY COMPACT CALCIUM HEXA-ALUMINATE-BASED REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
The present invention belongs to the technical field of refractory materials, and disclosed are a high-purity compact calcium hexa-aluminate-based refractory material, a preparation method therefor, and a working lining using same. The mixing ratio is adjusted according to the chemical composition of the final product to contain raw materials containing CaO, Al2O3 and ZrO2, the mixing ratio enabling the ratio of the chemical composition Al2O3:CaO:ZrO2 calculated according to parts by mass to be 45.5-95.5%:2.0-8.4%:0-50%; and the chemical composition are placed into a high-temperature furnace and a mold for hot-pressing, molding and sintering, wherein the temperature is increased while hot-pressing is carried out, the maximum temperature is 1550-1800°C, and the hot-pressing strength is 0.5-30 MPa. In the present invention, when no sintering agent is added, a hot-pressing sintering process is employed according to a proportion to obtain a high-purity compact calcium hexa-aluminate-based refractory material, and the refractory material has excellent resistance to molten steel erosion and thermal shock stability, and can be widely applied in metallurgy, building materials and petrochemical industries as well as other industries. The preparation method is scientific and reasonable, product purity is high, and the prepared refractory material product can increase a device operation period; in addition, production costs are reduced, and energy-saving and emission-reducing effects are achieved.
La présente invention appartient au domaine technique des matériaux réfractaires et concerne un matériau réfractaire compact de haute pureté à base d'hexa-aluminate de calcium, un procédé de préparation associé et un garnissage de travail l'utilisant. Le rapport de mélange est ajusté en fonction de la composition chimique du produit final pour contenir des matières premières contenant du CaO, de l'Al2O3 et du ZrO2, le rapport de mélange permettant au rapport de la composition chimique Al2O3:CaO:ZrO2, calculé selon des parties en masse, d'être de 45,5-95,5 %:2,0-8,4 %:0-50 % ; et la composition chimique étant placée dans un four à haute température et dans un moule pour le pressage à chaud, le moulage et le frittage, la température étant augmentée pendant que le pressage à chaud est effectué, la température maximale étant de 1550 à 1800°C et la force de pression à chaud étant de 0,5 à 30 MPa. Dans la présente invention, lorsqu'aucun agent de frittage n'est ajouté, un procédé de frittage par pressage à chaud est employé selon une proportion pour obtenir un matériau réfractaire compact de haute pureté à base d'hexa-aluminate de calcium et le matériau réfractaire présente une excellente résistance à l'érosion par l'acier fondu et une excellente stabilité aux chocs thermiques et peut être largement appliqué dans la métallurgie, les matériaux de construction et les industries pétrochimiques ainsi que dans d'autres industries. Le procédé de préparation est scientifique et raisonnable, la pureté du produit est élevée et le produit de matériau réfractaire préparé peut augmenter une période de fonctionnement du dispositif ; de plus, les coûts de production sont réduits et des effets d'économie d'énergie et de réduction d'émission sont obtenus.
本发明属于耐火材料技术领域，公开了一种高纯度致密六铝酸钙系耐火材料、其制备方法及使用其的工作衬，按照最终产品的化学成分调整好含CaO原料、含Al 2O 3原料、含ZrO 2原料的混合比例，所述混合比例使得按照质量份计算的化学成分Al 2O 3:CaO:ZrO 2的比例为45.5～95.5％：2.0～8.4％：0～50％，放入高温炉和模具中热压成型烧结，边升温边热压，最高温度为1550～1800℃、热压强度为0.5～30MPa。本发明在不添加烧结剂情况下，按照配比采用热压烧结工艺，获得高纯度致密六铝酸钙系耐火材料，该耐火材料具备出色的抵抗钢水侵蚀性能及热震稳定性，能广泛应用于冶金、建材和石化等行业。该制备方法科学合理、产品纯度高，并且所制得耐火材料制品能够增加设备运行周期，减少生产成本，达到节能减排效应。
HIGH-PURITY COMPACT CALCIUM HEXA-ALUMINATE-BASED REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
MATÉRIAU RÉFRACTAIRE COMPACT DE HAUTE PURETÉ À BASE D'HEXA-ALUMINATE DE CALCIUM ET PROCÉDÉ DE PRÉPARATION ASSOCIÉ
一种高纯度致密六铝酸钙系耐火材料及其制备方法
CHEN JUNHONG (author) / FENG JISHENG (author) / JIA YUANPING (author) / LI BIN (author) / ZHU BO (author) / LI GUANGQI (author) / GUO YUTAO (author)
2022-11-17
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
HIGH-PURITY COMPACT CALCIUM HEXA-ALUMINATE-BASED REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
| European Patent Office | 2024
HIGH-PURITY COMPACT CALCIUM HEXA-ALUMINATE-BASED REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
| European Patent Office | 2024
High-purity compact calcium hexaluminate series refractory material and preparation method thereof
| European Patent Office | 2022
| European Patent Office | 2024
Preparation of barium hexa-aluminate aerogel
| British Library Online Contents | 1994