BOEHMITE STRUCTURE AND METHOD FOR PRODUCING SAME
The boehmite structure 1 comprises a plurality of boehmite particles 2, wherein adjacent boehmite particles 2 are bonded to each other. The boehmite structure 1 has a crystallite size of 10 nm or less and a porosity of 15% or less. A method for producing the boehmite structure 1 comprises: a mixing step for mixing mechanochemically treated hydraulic alumina with a water-containing solvent to give a mixture; and a pressurizing and heating step for pressurizing and heating the mixture under the conditions of a pressure of 10-600 MPa and a temperature of 50-300°C.
L'invention concerne une structure de boehmite (1), qui comprend une pluralité de particules de boehmite (2), des particules de boehmite (2) adjacentes étant liées les unes aux autres. La structure de boehmite (1) a une taille des cristallites inférieure ou égale à 10 nm et une porosité inférieure ou égale à 15 %. L'invention concerne également un procédé pour la production de la structure de bœhmite (1), qui comprend : une étape de mélange consistant à mélanger de l'alumine hydraulique traitée par voie mécano-chimique avec un solvant contenant de l'eau pour donner un mélange ; et une étape de mise sous pression et de chauffage consistant à mettre sous pression et chauffer le mélange dans les conditions de pression de 10 à 600 MPa et de température de 50 à 300 °C.
ベーマイト構造体１は、複数のベーマイト粒子２を含み、隣接するベーマイト粒子２が結合している。当該ベーマイト構造体１は、ベーマイトの結晶子サイズが１０ｎｍ以下であり、気孔率が１５％以下である。ベーマイト構造体１の製造方法は、メカノケミカル処理された水硬性アルミナと、水を含む溶媒とを混合することにより混合物を得る混合工程と、当該混合物を、圧力が１０～６００ＭＰａであり、かつ、温度が５０～３００℃である条件下で加圧及び加熱する加圧加熱工程と、を有する。
BOEHMITE STRUCTURE AND METHOD FOR PRODUCING SAME
The boehmite structure 1 comprises a plurality of boehmite particles 2, wherein adjacent boehmite particles 2 are bonded to each other. The boehmite structure 1 has a crystallite size of 10 nm or less and a porosity of 15% or less. A method for producing the boehmite structure 1 comprises: a mixing step for mixing mechanochemically treated hydraulic alumina with a water-containing solvent to give a mixture; and a pressurizing and heating step for pressurizing and heating the mixture under the conditions of a pressure of 10-600 MPa and a temperature of 50-300°C.
L'invention concerne une structure de boehmite (1), qui comprend une pluralité de particules de boehmite (2), des particules de boehmite (2) adjacentes étant liées les unes aux autres. La structure de boehmite (1) a une taille des cristallites inférieure ou égale à 10 nm et une porosité inférieure ou égale à 15 %. L'invention concerne également un procédé pour la production de la structure de bœhmite (1), qui comprend : une étape de mélange consistant à mélanger de l'alumine hydraulique traitée par voie mécano-chimique avec un solvant contenant de l'eau pour donner un mélange ; et une étape de mise sous pression et de chauffage consistant à mettre sous pression et chauffer le mélange dans les conditions de pression de 10 à 600 MPa et de température de 50 à 300 °C.
ベーマイト構造体１は、複数のベーマイト粒子２を含み、隣接するベーマイト粒子２が結合している。当該ベーマイト構造体１は、ベーマイトの結晶子サイズが１０ｎｍ以下であり、気孔率が１５％以下である。ベーマイト構造体１の製造方法は、メカノケミカル処理された水硬性アルミナと、水を含む溶媒とを混合することにより混合物を得る混合工程と、当該混合物を、圧力が１０～６００ＭＰａであり、かつ、温度が５０～３００℃である条件下で加圧及び加熱する加圧加熱工程と、を有する。
BOEHMITE STRUCTURE AND METHOD FOR PRODUCING SAME
STRUCTURE DE BOEHMITE ET PROCÉDÉ POUR LA PRODUCTION DE CELLE-CI
ベーマイト構造体及びその製造方法
KURIZOE NAOKI (author) / SAWA RYOSUKE (author) / SATO NATSUKI (author) / YOSHIOKA TATSURO (author) / SEKINO TOHRU (author) / GOTO TOMOYO (author) / CHO SUNGHUN (author)
2023-04-27
Patent
Electronic Resource
Japanese
Hollow alumina microspheres from boehmite sols
| British Library Online Contents | 1998