PREPARATION METHOD FOR α-TYPE HEMIHYDRATE GYPSUM
A preparation method for an α-type hemihydrate gypsum, comprising the following steps: (1) enabling a desulfurized gypsum suspension and propionic acid to react at 120-140 °C for 3-5 hours; (2) carrying out solid-liquid separation, and carrying out vacuum drying at 40-80 °C to obtain an α-type high-strength hemihydrate gypsum. In the present preparation method for the α-type high-strength hemihydrate gypsum, propionic acid is used as a crystal transfer agent, only three carboxyl groups are contained, the distance between every two adjacent carboxyls is two C atoms, and no complex void groups are contained. Thus, the α-type high-strength gypsum tends to develop in the radial direction, a short-column-shaped α-type high-strength gypsum crystal is obtained, the strength of the α-type high-strength gypsum is improved, and resource utilization of the desulfurized gypsum is facilitated.
La présente invention concerne un procédé de préparation d'un gypse hémihydraté de type α, comprenant les étapes suivantes : (1) permettre à une suspension de gypse désulfuré et d'acide propionique de réagir à 120-140 °C pendant 3 à 5 heures ; (2) effectuer une séparation solide-liquide, et effectuer un séchage sous vide à 40-80 °C pour obtenir un gypse hémihydraté de haute résistance de type α. Dans le présent procédé de préparation du gypse hémihydraté de haute résistance de type α, de l'acide propionique est utilisé en tant qu'agent de transfert de cristaux, seuls trois groupes carboxyle sont contenus, la distance entre chaque paire de carboxyles adjacents est de deux atomes de C, et aucun groupe de vide complexe n'est contenu. Ainsi, le gypse à haute résistance de type α tend à se développer dans la direction radiale, un cristal de gypse à haute résistance de type α en forme de colonne courte est obtenu, la résistance du gypse à haute résistance de type α est améliorée, et l'utilisation des ressources du gypse désulfuré est facilitée.
α型半水石膏的制备方法包括下述步骤：（1）使脱硫石膏悬浮液和丙三酸在120-140℃下反应3-5h；（2）固液分离，40-80℃真空干燥，即得α型高强半水石膏。α型高强半水石膏的制备方法通过采用丙三酸作为转晶剂，其仅含有三个羧基基团，且每两个相邻的羧基间距均为两个C原子，不含有复杂的无效基团，可使α高强石膏趋于径向发展，得到短柱状的α高强石膏晶体，增加α高强石膏的强度，有助于脱硫石膏的资源化利用。
PREPARATION METHOD FOR α-TYPE HEMIHYDRATE GYPSUM
A preparation method for an α-type hemihydrate gypsum, comprising the following steps: (1) enabling a desulfurized gypsum suspension and propionic acid to react at 120-140 °C for 3-5 hours; (2) carrying out solid-liquid separation, and carrying out vacuum drying at 40-80 °C to obtain an α-type high-strength hemihydrate gypsum. In the present preparation method for the α-type high-strength hemihydrate gypsum, propionic acid is used as a crystal transfer agent, only three carboxyl groups are contained, the distance between every two adjacent carboxyls is two C atoms, and no complex void groups are contained. Thus, the α-type high-strength gypsum tends to develop in the radial direction, a short-column-shaped α-type high-strength gypsum crystal is obtained, the strength of the α-type high-strength gypsum is improved, and resource utilization of the desulfurized gypsum is facilitated.
La présente invention concerne un procédé de préparation d'un gypse hémihydraté de type α, comprenant les étapes suivantes : (1) permettre à une suspension de gypse désulfuré et d'acide propionique de réagir à 120-140 °C pendant 3 à 5 heures ; (2) effectuer une séparation solide-liquide, et effectuer un séchage sous vide à 40-80 °C pour obtenir un gypse hémihydraté de haute résistance de type α. Dans le présent procédé de préparation du gypse hémihydraté de haute résistance de type α, de l'acide propionique est utilisé en tant qu'agent de transfert de cristaux, seuls trois groupes carboxyle sont contenus, la distance entre chaque paire de carboxyles adjacents est de deux atomes de C, et aucun groupe de vide complexe n'est contenu. Ainsi, le gypse à haute résistance de type α tend à se développer dans la direction radiale, un cristal de gypse à haute résistance de type α en forme de colonne courte est obtenu, la résistance du gypse à haute résistance de type α est améliorée, et l'utilisation des ressources du gypse désulfuré est facilitée.
α型半水石膏的制备方法包括下述步骤：（1）使脱硫石膏悬浮液和丙三酸在120-140℃下反应3-5h；（2）固液分离，40-80℃真空干燥，即得α型高强半水石膏。α型高强半水石膏的制备方法通过采用丙三酸作为转晶剂，其仅含有三个羧基基团，且每两个相邻的羧基间距均为两个C原子，不含有复杂的无效基团，可使α高强石膏趋于径向发展，得到短柱状的α高强石膏晶体，增加α高强石膏的强度，有助于脱硫石膏的资源化利用。
PREPARATION METHOD FOR α-TYPE HEMIHYDRATE GYPSUM
PROCÉDÉ DE PRÉPARATION DE GYPSE HÉMIHYDRATÉ DE TYPE α
α型半水石膏的制备方法
ZHU JIANPING (author) / ZHANG CHEN (author) / FENG CHUNHUA (author) / LIU HUIJIE (author) / WANG QILIN (author) / GUAN XUEMAO (author) / ZHANG SUJUAN (author) / HUANG JINCHENG (author)
2023-06-29
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME