PROPAGABLE SELF-HEALING INORGANIC ADMIXTURE FOR CONCRETE AND PREPARATION METHOD THEREFOR
A propagable self-healing inorganic admixture for concrete and a preparation method therefor. The inorganic admixture comprises, in parts by weight, 50-70 parts of zeolite powder, 4-8 parts of a water reducer, 10-15 parts of silicate, 15-30 parts of water, 0.1-0.5 part of a reaction retarder, 0.05-0.1 part of a surfactant, and 0.05-0.1 part of a reducing agent. The preparation method comprises: (1) respectively weighing components; (2) adding silicate into water while stirring, and performing a pressurized reaction; (3) after pressure reduction, sequentially adding a reaction retarder, a surfactant, and a reducing agent, and performing stirring to obtain a mixed solution; (4) dropwise adding the mixed solution into zeolite powder; performing gradual heating and keeping the temperature for a period of time, and then cooling to the normal temperature to form a solid; and crushing and screening the solid; and (5) adding a water reducer into the screened material, and fully and uniformly stirring same to obtain an inorganic admixture. The prepared admixture can improve the compactness, strength, impermeability, and crack self-healing performance of concrete, thereby prolonging the service life of concrete.
L'invention concerne un mélange inorganique auto-cicatrisant apte à la propagation pour béton et un procédé de préparation s'y rapportant. Le mélange inorganique comprend, en parties en poids, 50 à 70 parties de poudre de zéolite, 4 à 8 parties d'un réducteur d'eau, 10 à 15 parties de silicate, 15 à 30 parties d'eau, 0,1 à 0,5 partie d'un retardateur de réaction, 0,05 à 0,1 partie d'un tensioactif et 0,05 à 0,1 partie d'un agent réducteur. Le procédé de préparation comprend : (1) la pesée des composants respectifs ; (2) l'addition de silicate dans de l'eau sous agitation et la mise en œuvre d'une réaction sous pression ; (3) après réduction de la pression, l'addition séquentielle d'un retardateur de réaction, d'un tensioactif et d'un agent réducteur, et la mise en œuvre d'une agitation pour obtenir une solution mélangée ; (4) l'addition goutte à goutte de la solution mélangée dans de la poudre de zéolite ; la mise en œuvre d'un chauffage progressif et le maintien de la température pendant une période de temps, puis le refroidissement jusqu'à la température normale pour former un solide ; et le concassage et le criblage du solide ; et (5) l'addition d'un réducteur d'eau dans le matériau criblé et l'agitation complète et uniforme de celui-ci pour obtenir un mélange inorganique. Le mélange préparé permet d'améliorer la compacité, la résistance, l'imperméabilité et la performance d'auto-cicatrisation de fissures du béton, ce qui permet de prolonger la durée de vie du béton.
一种混凝土用可繁殖自愈型无机内掺剂及其制备方法，其中，无机内掺剂按重量份计，包括沸石粉50-70份、减水剂4-8份、硅酸盐10-15份、水15-30份、反应迟缓剂0.1-0.5份、表面活性剂0.05-0.1份、还原剂0.05-0.1份。制备方法包括：(1)分别称取各组分；(2)在搅拌状态下将硅酸盐加入到水中，并加压反应；(3)降压后依次加入反应迟缓剂、表面活性剂、还原剂，搅拌后制得混合溶液；(4)将混合溶液以滴加的方式加入到沸石粉中，逐渐升温保持一段时间后冷却至常温形成固体；对固体进行破碎筛选；(5)在筛选后的材料中加入减水剂充分搅拌均匀后制得无机内掺剂。制备的内掺剂能够提高混凝土的密实性、强度、抗渗性及裂缝自愈性能，提升混凝土的使用寿命。
PROPAGABLE SELF-HEALING INORGANIC ADMIXTURE FOR CONCRETE AND PREPARATION METHOD THEREFOR
A propagable self-healing inorganic admixture for concrete and a preparation method therefor. The inorganic admixture comprises, in parts by weight, 50-70 parts of zeolite powder, 4-8 parts of a water reducer, 10-15 parts of silicate, 15-30 parts of water, 0.1-0.5 part of a reaction retarder, 0.05-0.1 part of a surfactant, and 0.05-0.1 part of a reducing agent. The preparation method comprises: (1) respectively weighing components; (2) adding silicate into water while stirring, and performing a pressurized reaction; (3) after pressure reduction, sequentially adding a reaction retarder, a surfactant, and a reducing agent, and performing stirring to obtain a mixed solution; (4) dropwise adding the mixed solution into zeolite powder; performing gradual heating and keeping the temperature for a period of time, and then cooling to the normal temperature to form a solid; and crushing and screening the solid; and (5) adding a water reducer into the screened material, and fully and uniformly stirring same to obtain an inorganic admixture. The prepared admixture can improve the compactness, strength, impermeability, and crack self-healing performance of concrete, thereby prolonging the service life of concrete.
L'invention concerne un mélange inorganique auto-cicatrisant apte à la propagation pour béton et un procédé de préparation s'y rapportant. Le mélange inorganique comprend, en parties en poids, 50 à 70 parties de poudre de zéolite, 4 à 8 parties d'un réducteur d'eau, 10 à 15 parties de silicate, 15 à 30 parties d'eau, 0,1 à 0,5 partie d'un retardateur de réaction, 0,05 à 0,1 partie d'un tensioactif et 0,05 à 0,1 partie d'un agent réducteur. Le procédé de préparation comprend : (1) la pesée des composants respectifs ; (2) l'addition de silicate dans de l'eau sous agitation et la mise en œuvre d'une réaction sous pression ; (3) après réduction de la pression, l'addition séquentielle d'un retardateur de réaction, d'un tensioactif et d'un agent réducteur, et la mise en œuvre d'une agitation pour obtenir une solution mélangée ; (4) l'addition goutte à goutte de la solution mélangée dans de la poudre de zéolite ; la mise en œuvre d'un chauffage progressif et le maintien de la température pendant une période de temps, puis le refroidissement jusqu'à la température normale pour former un solide ; et le concassage et le criblage du solide ; et (5) l'addition d'un réducteur d'eau dans le matériau criblé et l'agitation complète et uniforme de celui-ci pour obtenir un mélange inorganique. Le mélange préparé permet d'améliorer la compacité, la résistance, l'imperméabilité et la performance d'auto-cicatrisation de fissures du béton, ce qui permet de prolonger la durée de vie du béton.
一种混凝土用可繁殖自愈型无机内掺剂及其制备方法，其中，无机内掺剂按重量份计，包括沸石粉50-70份、减水剂4-8份、硅酸盐10-15份、水15-30份、反应迟缓剂0.1-0.5份、表面活性剂0.05-0.1份、还原剂0.05-0.1份。制备方法包括：(1)分别称取各组分；(2)在搅拌状态下将硅酸盐加入到水中，并加压反应；(3)降压后依次加入反应迟缓剂、表面活性剂、还原剂，搅拌后制得混合溶液；(4)将混合溶液以滴加的方式加入到沸石粉中，逐渐升温保持一段时间后冷却至常温形成固体；对固体进行破碎筛选；(5)在筛选后的材料中加入减水剂充分搅拌均匀后制得无机内掺剂。制备的内掺剂能够提高混凝土的密实性、强度、抗渗性及裂缝自愈性能，提升混凝土的使用寿命。
PROPAGABLE SELF-HEALING INORGANIC ADMIXTURE FOR CONCRETE AND PREPARATION METHOD THEREFOR
MÉLANGE INORGANIQUE AUTO-CICATRISANT APTE A LA PROPAGATION POUR BÉTON ET PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT
混凝土用可繁殖自愈型无机内掺剂及其制备方法
YAO GUOYOU (author) / SHI XIAOCHENG (author) / YU JINZHU (author) / JIN XIN (author)
2023-08-24
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Reproducible self-healing inorganic internal admixture for concrete and preparation method thereof
| European Patent Office | 2022
| European Patent Office | 2022
Preparation method of intelligent self-healing admixture
| European Patent Office | 2021