USE OF GRAPHENE OXIDE/BUTYL ACRYLATE/SILANE COMPOSITE EMULSION AS SHRINKAGE REDUCING AGENT
Provided is the use of a graphene oxide/butyl acrylate/silane composite emulsion as a shrinkage reducing agent for cement-based materials, which belongs to the technical field of cement-based materials. Active groups on isobutyltriethoxysilane molecules react with hydroxyl groups on the surface of mortar to form a layered hydrophobic structure, such that the loss of water in the mortar of a cement-based material is slowed down and cracking caused by drying shrinkage is avoided. Butyl acrylate can be dehydrated to form spatial network polymer fibers, which fill the pores of cement paste and consequently restrict the shrinkage of the mortar. Graphene oxide, with a large specific surface area and oxygen-containing functional groups on the surface, can provide growth sites for a hydration product and promote the formation of a regular and dense structure from the hydration product in the manner of a template, thereby ensuring the strength of the cement-based material. When blended into the cement-based material, sodium silicate can be hydrolyzed to form a silica gel, and the silica gel can react with calcium ions to form a C-S-H gel that fills the pores of a matrix, such that the early strength of the cement-based material is improved.
L'invention concerne l'utilisation d'une émulsion composite d'oxyde de graphène/acrylate de butyle/silane en tant qu'agent de réduction du retrait dans des matériaux à base de ciment, qui relève du domaine technique des matériaux à base de ciment. Les groupes actifs présents sur les molécules d'isobutyltriéthoxysilane réagissent avec les groupes hydroxyle présents sur la surface du mortier pour former une structure hydrophobe en couches, de telle sorte que la perte d'eau dans le mortier d'un matériau à base de ciment est ralentie et que la fissuration provoquée par le retrait au séchage est évitée. L'acrylate de butyle peut être déshydraté pour former des fibres de polymère à réseau spatial, qui remplissent les pores de la pâte de ciment et limitent par conséquent le retrait du mortier. L'oxyde de graphène, doté d'une surface spécifique importante et de groupes fonctionnels contenant de l'oxygène sur la surface, peut fournir des sites de croissance pour un produit d'hydratation et favoriser la formation d'une structure régulière et dense à partir du produit d'hydratation à la manière d'une matrice, ce qui permet d'assurer la résistance du matériau à base de ciment. Lorsqu'il est mélangé dans le matériau à base de ciment, le silicate de sodium peut être hydrolysé pour former un gel de silice et le gel de silice peut réagir avec des ions calcium pour former un gel C-S-H qui remplit les pores d'une matrice, de telle sorte que la résistance initiale du matériau à base de ciment est améliorée.
提供了氧化石墨烯/丙烯酸丁酯/硅烷复合乳液作为水泥基材料抗收缩剂的应用，属于水泥基材料技术领域。异丁基三乙氧基硅烷分子上的活性基团通过与砂浆表面的羟基反应，形成了层状憎水结构，减缓水泥基材料砂浆内部水分的散失，避免干燥收缩导致的开裂；丙烯酸丁酯可脱水形成空间网络状的聚合物纤维，填充在水泥浆体孔隙内，进而限制砂浆的收缩；氧化石墨烯具有较大的比表面积和表面含氧官能团，可以为水化产物提供生长位点，并以模板的方式促进水化产物形成规整致密的结构，保证水泥基材料的强度；硅酸钠掺入水泥基材料中，能水解生成硅胶，硅胶可与钙离子反应生成C-S-H凝胶，填充基体孔隙，提高水泥基材料早期强度。
USE OF GRAPHENE OXIDE/BUTYL ACRYLATE/SILANE COMPOSITE EMULSION AS SHRINKAGE REDUCING AGENT
Provided is the use of a graphene oxide/butyl acrylate/silane composite emulsion as a shrinkage reducing agent for cement-based materials, which belongs to the technical field of cement-based materials. Active groups on isobutyltriethoxysilane molecules react with hydroxyl groups on the surface of mortar to form a layered hydrophobic structure, such that the loss of water in the mortar of a cement-based material is slowed down and cracking caused by drying shrinkage is avoided. Butyl acrylate can be dehydrated to form spatial network polymer fibers, which fill the pores of cement paste and consequently restrict the shrinkage of the mortar. Graphene oxide, with a large specific surface area and oxygen-containing functional groups on the surface, can provide growth sites for a hydration product and promote the formation of a regular and dense structure from the hydration product in the manner of a template, thereby ensuring the strength of the cement-based material. When blended into the cement-based material, sodium silicate can be hydrolyzed to form a silica gel, and the silica gel can react with calcium ions to form a C-S-H gel that fills the pores of a matrix, such that the early strength of the cement-based material is improved.
L'invention concerne l'utilisation d'une émulsion composite d'oxyde de graphène/acrylate de butyle/silane en tant qu'agent de réduction du retrait dans des matériaux à base de ciment, qui relève du domaine technique des matériaux à base de ciment. Les groupes actifs présents sur les molécules d'isobutyltriéthoxysilane réagissent avec les groupes hydroxyle présents sur la surface du mortier pour former une structure hydrophobe en couches, de telle sorte que la perte d'eau dans le mortier d'un matériau à base de ciment est ralentie et que la fissuration provoquée par le retrait au séchage est évitée. L'acrylate de butyle peut être déshydraté pour former des fibres de polymère à réseau spatial, qui remplissent les pores de la pâte de ciment et limitent par conséquent le retrait du mortier. L'oxyde de graphène, doté d'une surface spécifique importante et de groupes fonctionnels contenant de l'oxygène sur la surface, peut fournir des sites de croissance pour un produit d'hydratation et favoriser la formation d'une structure régulière et dense à partir du produit d'hydratation à la manière d'une matrice, ce qui permet d'assurer la résistance du matériau à base de ciment. Lorsqu'il est mélangé dans le matériau à base de ciment, le silicate de sodium peut être hydrolysé pour former un gel de silice et le gel de silice peut réagir avec des ions calcium pour former un gel C-S-H qui remplit les pores d'une matrice, de telle sorte que la résistance initiale du matériau à base de ciment est améliorée.
提供了氧化石墨烯/丙烯酸丁酯/硅烷复合乳液作为水泥基材料抗收缩剂的应用，属于水泥基材料技术领域。异丁基三乙氧基硅烷分子上的活性基团通过与砂浆表面的羟基反应，形成了层状憎水结构，减缓水泥基材料砂浆内部水分的散失，避免干燥收缩导致的开裂；丙烯酸丁酯可脱水形成空间网络状的聚合物纤维，填充在水泥浆体孔隙内，进而限制砂浆的收缩；氧化石墨烯具有较大的比表面积和表面含氧官能团，可以为水化产物提供生长位点，并以模板的方式促进水化产物形成规整致密的结构，保证水泥基材料的强度；硅酸钠掺入水泥基材料中，能水解生成硅胶，硅胶可与钙离子反应生成C-S-H凝胶，填充基体孔隙，提高水泥基材料早期强度。
USE OF GRAPHENE OXIDE/BUTYL ACRYLATE/SILANE COMPOSITE EMULSION AS SHRINKAGE REDUCING AGENT
UTILISATION D'UNE ÉMULSION COMPOSITE D'OXYDE DE GRAPHÈNE/ACRYLATE DE BUTYLE/SILANE EN TANT QU'AGENT DE RÉDUCTION DU RETRAIT
氧化石墨烯/丙烯酸丁酯/硅烷复合乳液作为抗收缩剂的应用
LI SHAOCHUN (author) / XU SHILIN (author) / LIU ANG (author) / GENG YONGJUAN (author) / HOU DONGSHUAI (author) / ZHANG RUIYONG (author) / JIN ZUQUAN (author) / GAO SONG (author)
2023-01-05
Patent
Electronic Resource
Chinese
USE OF GRAPHENE OXIDE/BUTYL ACRYLATE/SILANE COMPOSITE EMULSION AS ANTI-SHRINKAGE AGENT
| European Patent Office | 2024
Use of graphene oxide/butylacrylate/silane composite emulsion as anti-shrinkage agent
| European Patent Office | 2024
USE OF SILANE COMPOSITE EMULSION AS ANTI-CRACKING REINFORCING AGENT
| European Patent Office | 2023
Use of silane composite emulsion as anti-cracking reinforcing agent
| European Patent Office | 2024