CO2Z-TYPE FERRITE MAGNETIC POWDER, METHOD FOR PREPARING SAME, AND MAGNETIC-PLASTIC COMPOSITE MATERIAL
The present application provides a Co2Z-type ferrite magnetic powder, a method for preparing same, and a magnetic-plastic composite material. The method for preparing the Co2Z-type ferrite magnetic powder comprises: step S1, mixing an M-type ferrite precursor, a Y-type ferrite precursor and an optional binder for first sintering to obtain a first sintered body, crushing the first sintered body into a powder to obtain first sintered body particles with the particle size of 0.5-4 μm, and mixing the first sintered body particles with a salt for second sintering to obtain a second sintered body; and step S3, sequentially carrying out salt elution and drying on the second sintered body to obtain the Co2Z-type ferrite magnetic powder. According to the method for preparing the Co2Z-type ferrite magnetic powder provided by the present application, by means of the combination of the first sintering, the second sintering and the molten salt process, the prepared Co2Z-type ferrite magnetic powder phase has high purity, uniform granularity and morphology, and an excellent electromagnetic characteristic.
La présente invention concerne une poudre magnétique de ferrite de type Co2Z, sa méthode de préparation, et un matériau composite magnétique-plastique. La méthode de préparation de la poudre magnétique de ferrite de type Co2Z comprend : étape S1, le mélange d'un précurseur de ferrite de type M, d'un précurseur de ferrite de type Y et d'un liant facultatif pour un premier frittage pour obtenir un premier corps fritté, le broyage du premier corps fritté en une poudre pour obtenir des premières particules de corps fritté ayant la taille de particule de 0,5 à 4 µm, et le mélange des premières particules de corps fritté avec un sel pour un second frittage pour obtenir un second corps fritté ; et étape S3, la réalisation séquentielle d'une élution de sel et d'un séchage sur le second corps fritté pour obtenir la poudre magnétique de ferrite de type Co2Z. Selon la méthode de préparation de la poudre magnétique de ferrite de type Co2Z fournie par la présente invention, au moyen de la combinaison du premier frittage, du second frittage et du procédé de sel fondu, la phase de poudre magnétique de ferrite de type Co2Z préparée présente une pureté élevée, une granularité et une morphologie uniformes, et une excellente caractéristique électromagnétique.
本申请提供了一种Co2Z型铁氧体磁粉及其制备方法和磁塑复合材料。该Co2Z型铁氧体磁粉的制备方法包括：步骤S1，将M型铁氧体前驱体、Y型铁氧体前驱体以及可选的粘结剂混合进行第一烧结，得到第一烧结体，将第一烧结体破碎成粉体状，得到粒度为0.5～4μm的第一烧结体颗粒，将第一烧结体颗粒与盐混合进行第二烧结，得到第二烧结体；步骤S3，将第二烧结体依次进行盐洗脱和干燥，得到Co2Z型铁氧体磁粉。本申请提供的Co2Z型铁氧体磁粉的制备方法通过第一烧结、第二烧结以及熔盐工艺相结合，制备得到的Co2Z型铁氧体磁粉相纯度高、粒度和形貌均匀，具备优异的电磁特性。
CO2Z-TYPE FERRITE MAGNETIC POWDER, METHOD FOR PREPARING SAME, AND MAGNETIC-PLASTIC COMPOSITE MATERIAL
The present application provides a Co2Z-type ferrite magnetic powder, a method for preparing same, and a magnetic-plastic composite material. The method for preparing the Co2Z-type ferrite magnetic powder comprises: step S1, mixing an M-type ferrite precursor, a Y-type ferrite precursor and an optional binder for first sintering to obtain a first sintered body, crushing the first sintered body into a powder to obtain first sintered body particles with the particle size of 0.5-4 μm, and mixing the first sintered body particles with a salt for second sintering to obtain a second sintered body; and step S3, sequentially carrying out salt elution and drying on the second sintered body to obtain the Co2Z-type ferrite magnetic powder. According to the method for preparing the Co2Z-type ferrite magnetic powder provided by the present application, by means of the combination of the first sintering, the second sintering and the molten salt process, the prepared Co2Z-type ferrite magnetic powder phase has high purity, uniform granularity and morphology, and an excellent electromagnetic characteristic.
La présente invention concerne une poudre magnétique de ferrite de type Co2Z, sa méthode de préparation, et un matériau composite magnétique-plastique. La méthode de préparation de la poudre magnétique de ferrite de type Co2Z comprend : étape S1, le mélange d'un précurseur de ferrite de type M, d'un précurseur de ferrite de type Y et d'un liant facultatif pour un premier frittage pour obtenir un premier corps fritté, le broyage du premier corps fritté en une poudre pour obtenir des premières particules de corps fritté ayant la taille de particule de 0,5 à 4 µm, et le mélange des premières particules de corps fritté avec un sel pour un second frittage pour obtenir un second corps fritté ; et étape S3, la réalisation séquentielle d'une élution de sel et d'un séchage sur le second corps fritté pour obtenir la poudre magnétique de ferrite de type Co2Z. Selon la méthode de préparation de la poudre magnétique de ferrite de type Co2Z fournie par la présente invention, au moyen de la combinaison du premier frittage, du second frittage et du procédé de sel fondu, la phase de poudre magnétique de ferrite de type Co2Z préparée présente une pureté élevée, une granularité et une morphologie uniformes, et une excellente caractéristique électromagnétique.
本申请提供了一种Co2Z型铁氧体磁粉及其制备方法和磁塑复合材料。该Co2Z型铁氧体磁粉的制备方法包括：步骤S1，将M型铁氧体前驱体、Y型铁氧体前驱体以及可选的粘结剂混合进行第一烧结，得到第一烧结体，将第一烧结体破碎成粉体状，得到粒度为0.5～4μm的第一烧结体颗粒，将第一烧结体颗粒与盐混合进行第二烧结，得到第二烧结体；步骤S3，将第二烧结体依次进行盐洗脱和干燥，得到Co2Z型铁氧体磁粉。本申请提供的Co2Z型铁氧体磁粉的制备方法通过第一烧结、第二烧结以及熔盐工艺相结合，制备得到的Co2Z型铁氧体磁粉相纯度高、粒度和形貌均匀，具备优异的电磁特性。
CO2Z-TYPE FERRITE MAGNETIC POWDER, METHOD FOR PREPARING SAME, AND MAGNETIC-PLASTIC COMPOSITE MATERIAL
POUDRE MAGNÉTIQUE DE FERRITE DE TYPE CO2Z, SA MÉTHODE DE PRÉPARATION, ET MATÉRIAU COMPOSITE MAGNÉTIQUE-PLASTIQUE
Co2Z型铁氧体磁粉及其制备方法和磁塑复合材料
LIU LIDONG (author) / SHI FENG (author) / TANG ZISHUN (author) / ZHU HANGFEI (author) / SHAN ZHEN (author) / FU YAQI (author)
2024-01-04
Patent
Electronic Resource
Chinese
Co2Z type ferrite material and preparation method thereof
| European Patent Office | 2021
High frequency magnetic mechanism of Ni-substituted Co2Z hexagonal ferrite
| British Library Online Contents | 2009
Static and dynamic magnetic properties of Co2Z barium ferrite nanoparticle composites
| British Library Online Contents | 2005
Mo-doped Co2Z-type ferrite composite material for use ultra-high frequency antennas
| European Patent Office | 2020