SILICON CARBIDE-CALCIUM ZIRCONATE COMPOSITE REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
The present invention relates to the technical field of refractory materials. Disclosed are a silicon carbide (SiC)-calcium zirconate composite refractory material, a raw material composition thereof, and a preparation method therefor. The SiC-calcium zirconate composite refractory material disclosed in the present invention takes SiC as a main crystal phase and calcium zirconate as a secondary crystal phase, and the sum of the mass fractions of SiC, CaO and ZrO2 in the composite refractory material is greater than or equal to 95%, wherein the mass fraction of SiC is 53-75%, the mass fraction of CaO is 5-12%, and the mass fraction of ZrO2 is 18-33%. For the composite refractory material of the present invention, the apparent porosity is 12-20%, the volume density is 2.9-3.3 g/cm3, the flexural strength at room temperature is 15-40 MPa, the flexural strength at a high temperature of 1400°C is 10-30 MPa, and the refractoriness under load is 1700°C or higher; and the composite refractory material has good fire resistance, high use temperature and good slag resistance, is green and chromium-free, and can replace a chromium-containing refractory material to be applied to a harsh part of thermal equipment which violently reacts with slag in a high-temperature reducing atmosphere.
La présente invention se rapporte au domaine technique des matériaux réfractaires. Sont divulgués un matériau réfractaire composite de carbure de silicium (SiC)-zirconate de calcium, une composition de matière première de celui-ci et son procédé de préparation. Le matériau réfractaire de zirconate de calcium SiC décrit dans la présente invention prend le SiC en tant que phase cristalline principale et le zirconate de calcium en tant que phase cristalline secondaire, et la somme des fractions massiques de SiC, CaO et ZrO2 dans le matériau réfractaire composite est supérieure ou égale à 95 %, la fraction massique de SiC étant de 53 à 75 %, la fraction massique de CaO étant de 5 à 12 %, et la fraction massique de ZrO2 étant de 18 à 33 %. Pour le matériau réfractaire composite de la présente invention, la porosité apparente est de 12 à 20 %, la densité volumique est de 2,9 à 3,3 g/cm3, la résistance à la flexion à température ambiante est de 15 à 40 MPa, la résistance à la flexion à une température élevée de 1 400 °C est de 10 à 30 MPa, et l'indice de réfraction sous charge est de 1 700 °C ou plus ; et le matériau réfractaire composite présente une bonne résistance au feu, une température d'utilisation élevée et une bonne résistance aux scories, est écologique et exempt de chrome, et peut remplacer un matériau réfractaire contenant du chrome à appliquer à une partie agressive d'équipement thermique qui réagit violemment aux scories dans une atmosphère réductrice à haute température.
本发明公开了一种碳化硅-锆酸钙复合耐火材料及其原料组合物和制备方法，属于耐火材料技术领域。本发明公开的碳化硅-锆酸钙复合耐火材料以碳化硅为主晶相、以锆酸钙为次晶相，所述复合耐火材料中SiC、CaO和ZrO 2的质量分数之和大于等于95％，其中SiC质量分数为53％～75％、CaO质量分数为5％～12％、ZrO 2质量分数为18％～33％。本发明的复合耐火材料显气孔率为12％～20％，体积密度2.9～3.3g/cm 3，常温抗折强度15～40MPa，1400℃高温抗折强度10～30MPa，荷重软化温度大于1700℃，具有很好的耐火性能，使用温度高，抗渣性能好，且绿色无铬，可替代含铬耐火材料应用于高温、还原气氛热工设备中与熔渣反应剧烈的苛刻部位。
SILICON CARBIDE-CALCIUM ZIRCONATE COMPOSITE REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
The present invention relates to the technical field of refractory materials. Disclosed are a silicon carbide (SiC)-calcium zirconate composite refractory material, a raw material composition thereof, and a preparation method therefor. The SiC-calcium zirconate composite refractory material disclosed in the present invention takes SiC as a main crystal phase and calcium zirconate as a secondary crystal phase, and the sum of the mass fractions of SiC, CaO and ZrO2 in the composite refractory material is greater than or equal to 95%, wherein the mass fraction of SiC is 53-75%, the mass fraction of CaO is 5-12%, and the mass fraction of ZrO2 is 18-33%. For the composite refractory material of the present invention, the apparent porosity is 12-20%, the volume density is 2.9-3.3 g/cm3, the flexural strength at room temperature is 15-40 MPa, the flexural strength at a high temperature of 1400°C is 10-30 MPa, and the refractoriness under load is 1700°C or higher; and the composite refractory material has good fire resistance, high use temperature and good slag resistance, is green and chromium-free, and can replace a chromium-containing refractory material to be applied to a harsh part of thermal equipment which violently reacts with slag in a high-temperature reducing atmosphere.
La présente invention se rapporte au domaine technique des matériaux réfractaires. Sont divulgués un matériau réfractaire composite de carbure de silicium (SiC)-zirconate de calcium, une composition de matière première de celui-ci et son procédé de préparation. Le matériau réfractaire de zirconate de calcium SiC décrit dans la présente invention prend le SiC en tant que phase cristalline principale et le zirconate de calcium en tant que phase cristalline secondaire, et la somme des fractions massiques de SiC, CaO et ZrO2 dans le matériau réfractaire composite est supérieure ou égale à 95 %, la fraction massique de SiC étant de 53 à 75 %, la fraction massique de CaO étant de 5 à 12 %, et la fraction massique de ZrO2 étant de 18 à 33 %. Pour le matériau réfractaire composite de la présente invention, la porosité apparente est de 12 à 20 %, la densité volumique est de 2,9 à 3,3 g/cm3, la résistance à la flexion à température ambiante est de 15 à 40 MPa, la résistance à la flexion à une température élevée de 1 400 °C est de 10 à 30 MPa, et l'indice de réfraction sous charge est de 1 700 °C ou plus ; et le matériau réfractaire composite présente une bonne résistance au feu, une température d'utilisation élevée et une bonne résistance aux scories, est écologique et exempt de chrome, et peut remplacer un matériau réfractaire contenant du chrome à appliquer à une partie agressive d'équipement thermique qui réagit violemment aux scories dans une atmosphère réductrice à haute température.
本发明公开了一种碳化硅-锆酸钙复合耐火材料及其原料组合物和制备方法，属于耐火材料技术领域。本发明公开的碳化硅-锆酸钙复合耐火材料以碳化硅为主晶相、以锆酸钙为次晶相，所述复合耐火材料中SiC、CaO和ZrO 2的质量分数之和大于等于95％，其中SiC质量分数为53％～75％、CaO质量分数为5％～12％、ZrO 2质量分数为18％～33％。本发明的复合耐火材料显气孔率为12％～20％，体积密度2.9～3.3g/cm 3，常温抗折强度15～40MPa，1400℃高温抗折强度10～30MPa，荷重软化温度大于1700℃，具有很好的耐火性能，使用温度高，抗渣性能好，且绿色无铬，可替代含铬耐火材料应用于高温、还原气氛热工设备中与熔渣反应剧烈的苛刻部位。
SILICON CARBIDE-CALCIUM ZIRCONATE COMPOSITE REFRACTORY MATERIAL AND PREPARATION METHOD THEREFOR
MATÉRIAU RÉFRACTAIRE COMPOSITE DE CARBURE DE SILICIUM-ZIRCONATE DE CALCIUM ET SON PROCÉDÉ DE PRÉPARATION
一种碳化硅-锆酸钙复合耐火材料及其制备方法
SUN HONGGANG (author) / LI HONGXIA (author) / LYU SHIPING (author) / WEI YI (author) / WANG HAN (author) / WAN LONGGANG (author) / DU YIHAO (author)
2024-02-01
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Preparation method of novel calcium zirconate refractory material
| European Patent Office | 2024
Silicon carbide-calcium hexaluminate-aluminum composite refractory material
| European Patent Office | 2020
Silicon nitride binding silicon carbide refractory material and preparation method therefor
| European Patent Office | 2015