BLACK TALC MINERAL MICROWAVE DIELECTRIC CERAMIC MATERIAL AND PREPARATION METHOD THEREFOR
A black talc mineral microwave dielectric ceramic material, prepared by sintering the following components in percentage by mass: 54-61% of black talc mineral powder, 33-40% of MgO powder, 2-5% of MnCO3 powder, and 1-4% of TiO2 powder. The main phase of the black talc mineral microwave dielectric ceramic material is an Mg2SiO4 solid solution phase. A preparation method for the black talc mineral microwave dielectric ceramic material comprises: uniformly mixing MgO powder and MnCO3 powder with pre-treated black talc mineral powder according to a ratio and by means of wet ball milling, drying, calcining, then uniformly mixing the calcined powder with TiO2 powder, a binder and a defoaming agent by means of wet ball milling, then drying to prepare a blank, and finally sintering. The method can prepare a black talc mineral microwave dielectric ceramic material having high quality by means of the combination of component compounding and ion modification.
La présente invention concerne un matériau céramique diélectrique pour micro-ondes minéral à base de talc noir, préparé par frittage des composants suivants en pourcentage en masse : de 54 à 61 % de poudre minérale de talc noir, de 33 à 40 % de poudre de MgO, de 2 à 5 % de poudre de MnCO3, et de 1 à 4 % de poudre de TiO2. La phase principale du matériau céramique diélectrique pour micro-ondes minéral à base de talc noir est une phase de solution solide de Mg2SiO4. Un procédé de préparation du matériau céramique diélectrique pour micro-ondes minéral à base de talc noir comprend le mélange uniforme de poudre de MgO et de MnCO3 en poudre avec de la poudre minérale de talc noir prétraitée selon un rapport et au moyen d'un broyage à billes par voie humide, le séchage, la calcination, puis le mélange uniforme de la poudre calcinée avec du TiO2 en poudre, un liant et un agent antimousse au moyen d'un broyage à billes par voie humide, puis le séchage pour préparer une ébauche, et enfin le frittage. Le procédé peut préparer un matériau céramique diélectrique pour micro-ondes minéral à base de talc noir de haute qualité au moyen de la combinaison du mélange de composants et de la modification d'ions.
一种黑滑石矿质微波介质陶瓷材料，由以下质量百分比的组分原料烧结制成：54～61％黑滑石矿粉末，33～40％MgO粉末，2～5％MnCO 3粉末和1～4％TiO 2粉末，所述黑滑石矿质微波介质陶瓷材料的主物相是Mg 2SiO 4固溶相。所述黑滑石矿质微波介质陶瓷材料的制备方法，包括通过湿法球磨的方式将MgO粉末、MnCO 3粉末与预处理后的黑滑石矿粉末按比例混合均匀后烘干煅烧，再通过湿法球磨的方式将煅烧后粉体与TiO 2粉末、粘结剂和消泡剂混合均匀烘干制坯，最后烧结。该方法通过组分复配、离子改性相结合的方法实现高品质因素的黑滑石矿质微波介质陶瓷材料的制备。
BLACK TALC MINERAL MICROWAVE DIELECTRIC CERAMIC MATERIAL AND PREPARATION METHOD THEREFOR
A black talc mineral microwave dielectric ceramic material, prepared by sintering the following components in percentage by mass: 54-61% of black talc mineral powder, 33-40% of MgO powder, 2-5% of MnCO3 powder, and 1-4% of TiO2 powder. The main phase of the black talc mineral microwave dielectric ceramic material is an Mg2SiO4 solid solution phase. A preparation method for the black talc mineral microwave dielectric ceramic material comprises: uniformly mixing MgO powder and MnCO3 powder with pre-treated black talc mineral powder according to a ratio and by means of wet ball milling, drying, calcining, then uniformly mixing the calcined powder with TiO2 powder, a binder and a defoaming agent by means of wet ball milling, then drying to prepare a blank, and finally sintering. The method can prepare a black talc mineral microwave dielectric ceramic material having high quality by means of the combination of component compounding and ion modification.
La présente invention concerne un matériau céramique diélectrique pour micro-ondes minéral à base de talc noir, préparé par frittage des composants suivants en pourcentage en masse : de 54 à 61 % de poudre minérale de talc noir, de 33 à 40 % de poudre de MgO, de 2 à 5 % de poudre de MnCO3, et de 1 à 4 % de poudre de TiO2. La phase principale du matériau céramique diélectrique pour micro-ondes minéral à base de talc noir est une phase de solution solide de Mg2SiO4. Un procédé de préparation du matériau céramique diélectrique pour micro-ondes minéral à base de talc noir comprend le mélange uniforme de poudre de MgO et de MnCO3 en poudre avec de la poudre minérale de talc noir prétraitée selon un rapport et au moyen d'un broyage à billes par voie humide, le séchage, la calcination, puis le mélange uniforme de la poudre calcinée avec du TiO2 en poudre, un liant et un agent antimousse au moyen d'un broyage à billes par voie humide, puis le séchage pour préparer une ébauche, et enfin le frittage. Le procédé peut préparer un matériau céramique diélectrique pour micro-ondes minéral à base de talc noir de haute qualité au moyen de la combinaison du mélange de composants et de la modification d'ions.
一种黑滑石矿质微波介质陶瓷材料，由以下质量百分比的组分原料烧结制成：54～61％黑滑石矿粉末，33～40％MgO粉末，2～5％MnCO 3粉末和1～4％TiO 2粉末，所述黑滑石矿质微波介质陶瓷材料的主物相是Mg 2SiO 4固溶相。所述黑滑石矿质微波介质陶瓷材料的制备方法，包括通过湿法球磨的方式将MgO粉末、MnCO 3粉末与预处理后的黑滑石矿粉末按比例混合均匀后烘干煅烧，再通过湿法球磨的方式将煅烧后粉体与TiO 2粉末、粘结剂和消泡剂混合均匀烘干制坯，最后烧结。该方法通过组分复配、离子改性相结合的方法实现高品质因素的黑滑石矿质微波介质陶瓷材料的制备。
BLACK TALC MINERAL MICROWAVE DIELECTRIC CERAMIC MATERIAL AND PREPARATION METHOD THEREFOR
MATÉRIAU CÉRAMIQUE DIÉLECTRIQUE POUR MICRO-ONDES MINÉRAL À BASE DE TALC NOIR ET SON PROCÉDÉ DE PRÉPARATION
一种黑滑石矿质微波介质陶瓷材料及其制备方法
KONG JIANJUN (author) / HU MINGWEI (author) / LAI WEI (author) / DING QINHUA (author) / ZHANG MING (author) / WANG ZHEFEI (author) / LIU WEIZHOU (author) / HE YUGUO (author) / ZHAO SHUAIYU (author) / LIU ZIZHENG (author)
2024-06-06
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Wollastonite mineral microwave dielectric ceramic material and preparation method thereof
| European Patent Office | 2024
| European Patent Office | 2022
| European Patent Office | 2022
| European Patent Office | 2020
| European Patent Office | 2022