NICKEL-MAGNESIUM-ZINC-COPPER FERRITE AND PREPARATION METHOD THEREFOR AND USE THEREOF
A nickel-magnesium-zinc-copper ferrite and a preparation method therefor and a use thereof. The ferrite comprises: main components comprising, by mass fraction, 66.95%-71.8% of Fe2O3, 15.6%-19.7% of ZnO, 2.1%-4.2% of NiO, 2.1%-5.0% of MnO, 2.0%-4.9% of CuO and 1.82%-2.98% of MgO; and auxiliary additives comprising CaCO3, Bi2O3, MoO3, and Co2O3. The preparation method comprises: weighing the main components, and wet-grinding same to obtain a first mixture; drying and pre-sintering the first mixture to obtain a pre-sintered material; weighing the auxiliary additives, wet-grinding same with the pre-sintered material, and drying to obtain a second mixture; and pulverizing, forming and sintering the second mixture to obtain the nickel-magnesium-zinc-copper ferrite. The nickel-magnesium-zinc-copper ferrite can be applied to a magnetic device.
La présente invention concerne une ferrite de nickel-magnésium-zinc-cuivre et son procédé de préparation et son utilisation. La ferrite comprend des composants principaux comprenant, en fraction massique, de 66,95 % à 71,8 % de Fe2O3, de 15,6 % à 19,7 % de ZnO, de 2,1 % à 4,2 % de NiO, de 2,1 % à 5,0 % de MnO, de 2,0 % à 4,9 % de CuO et de 1,82 % à 2,98 % de MgO ; et des additifs auxiliaires comprenant du CaCO3, du Bi2O3, du MoO3 et du Co2O3. Le procédé de préparation comprend le pesage des composants principaux et leur broyage par voie humide pour obtenir un premier mélange ; le séchage et le préfrittage du premier mélange pour obtenir un matériau préfritté ; le pesage des additifs auxiliaires, leur broyage par voie humide avec le matériau préfritté,et le séchage pour obtenir un second mélange ; et la pulvérisation, la formation et le frittage du second mélange pour obtenir la ferrite de nickel-magnésium-zinc-cuivre. La ferrite de nickel-magnésium-zinc-cuivre peut être appliquée à un dispositif magnétique.
一种镍镁锌铜铁氧体及其制备方法和应用。该铁氧体包括：主成分以质量分数计，包括66.95％-71.8％的Fe2O3、15.6％-19.7％的ZnO、2.1％-4.2％的NiO、2.1％-5.0％的MnO、2.0％-4.9％的CuO及1.82％-2.98％的MgO；辅助添加剂包括CaCO3、Bi2O3、MoO3及Co2O3。该制备方法包括：称取主成分、湿磨，得到第一混合料；将第一混合料干燥、预烧，得到预烧料；称取辅助添加剂，与预烧料湿磨，干燥得到第二混合料；将第二混合料制粉、成型和烧结，得到镍镁锌铜铁氧体。该镍镁锌铜铁氧体可以应用于磁性器件中。
NICKEL-MAGNESIUM-ZINC-COPPER FERRITE AND PREPARATION METHOD THEREFOR AND USE THEREOF
A nickel-magnesium-zinc-copper ferrite and a preparation method therefor and a use thereof. The ferrite comprises: main components comprising, by mass fraction, 66.95%-71.8% of Fe2O3, 15.6%-19.7% of ZnO, 2.1%-4.2% of NiO, 2.1%-5.0% of MnO, 2.0%-4.9% of CuO and 1.82%-2.98% of MgO; and auxiliary additives comprising CaCO3, Bi2O3, MoO3, and Co2O3. The preparation method comprises: weighing the main components, and wet-grinding same to obtain a first mixture; drying and pre-sintering the first mixture to obtain a pre-sintered material; weighing the auxiliary additives, wet-grinding same with the pre-sintered material, and drying to obtain a second mixture; and pulverizing, forming and sintering the second mixture to obtain the nickel-magnesium-zinc-copper ferrite. The nickel-magnesium-zinc-copper ferrite can be applied to a magnetic device.
La présente invention concerne une ferrite de nickel-magnésium-zinc-cuivre et son procédé de préparation et son utilisation. La ferrite comprend des composants principaux comprenant, en fraction massique, de 66,95 % à 71,8 % de Fe2O3, de 15,6 % à 19,7 % de ZnO, de 2,1 % à 4,2 % de NiO, de 2,1 % à 5,0 % de MnO, de 2,0 % à 4,9 % de CuO et de 1,82 % à 2,98 % de MgO ; et des additifs auxiliaires comprenant du CaCO3, du Bi2O3, du MoO3 et du Co2O3. Le procédé de préparation comprend le pesage des composants principaux et leur broyage par voie humide pour obtenir un premier mélange ; le séchage et le préfrittage du premier mélange pour obtenir un matériau préfritté ; le pesage des additifs auxiliaires, leur broyage par voie humide avec le matériau préfritté,et le séchage pour obtenir un second mélange ; et la pulvérisation, la formation et le frittage du second mélange pour obtenir la ferrite de nickel-magnésium-zinc-cuivre. La ferrite de nickel-magnésium-zinc-cuivre peut être appliquée à un dispositif magnétique.
一种镍镁锌铜铁氧体及其制备方法和应用。该铁氧体包括：主成分以质量分数计，包括66.95％-71.8％的Fe2O3、15.6％-19.7％的ZnO、2.1％-4.2％的NiO、2.1％-5.0％的MnO、2.0％-4.9％的CuO及1.82％-2.98％的MgO；辅助添加剂包括CaCO3、Bi2O3、MoO3及Co2O3。该制备方法包括：称取主成分、湿磨，得到第一混合料；将第一混合料干燥、预烧，得到预烧料；称取辅助添加剂，与预烧料湿磨，干燥得到第二混合料；将第二混合料制粉、成型和烧结，得到镍镁锌铜铁氧体。该镍镁锌铜铁氧体可以应用于磁性器件中。
NICKEL-MAGNESIUM-ZINC-COPPER FERRITE AND PREPARATION METHOD THEREFOR AND USE THEREOF
FERRITE DE NICKEL-MAGNÉSIUM-ZINC-CUIVRE ET SON PROCÉDÉ DE PRÉPARATION ET SON UTILISATION
镍镁锌铜铁氧体及其制备方法和应用
JIANG YUMEI (author) / ZHENG GUOYOU (author) / ZHU XIAOLI (author)
2024-06-20
Patent
Electronic Resource
Chinese
Nickel-copper-zinc ferrite and preparation method thereof
| European Patent Office | 2015
Nickel-magnesium-zinc-copper ferrite as well as preparation method and application thereof
| European Patent Office | 2024
Nickel-zinc-copper ferrite powder and preparation method thereof
| European Patent Office | 2015
NICKEL-ZINC FERRITE MATERIAL, AND PREPARATION METHOD THEREFOR AND USE THEREOF
| European Patent Office | 2024
Nickel-zinc-copper ferrite as well as preparation method and application thereof
| European Patent Office | 2024