LOW-POISSON'S-RATIO ELASTOMER, SEAMLESS EXPANSION DEVICE, AND CONSTRUCTION PROCESS
The present invention relates to the technical field of bridge expansion joint engineering, and in particular, to a low-Poisson's-ratio elastomer, a seamless expansion device, and a construction process. The low-Poisson's-ratio elastomer comprises, in percentage by weight: 70-80% of a negative-Poisson's-ratio unit and 20-30% of a high-toughness resin cementing material. After testing, the low-Poisson's-ratio elastomer has a Poisson's ratio of 0-0.01, a hardness of 60-70 IRHD and an elastic modulus at definite elongation of less than or equal to 2 Mpa, and the bonding tensile strength of the low-Poisson's-ratio elastomer with a steel plate is greater than or equal to 2.5 Mpa. According to the present invention, a low-Poisson's-ratio elastomer is formed by mixing a negative-Poisson's-ratio unit with a high-toughness resin cementing material, a low Poisson's ratio of a resin elastomer material of an expansion joint is achieved, the problem of changed surface flatness of a device due to unchanged volume of a resin elastomer under stretching and compression is solved, and the low-Poisson's-ratio elastomer can meet a larger expansion deformation amount under the same width.
La présente invention concerne le domaine technique de l'ingénierie des joints de dilatation de pont, et en particulier, un élastomère à faible coefficient de Poisson, un dispositif de dilatation sans soudure et un procédé de construction. L'élastomère à faible coefficient de Poisson comprend, en pourcentage en poids : 70 à 80% d'une unité à coefficient de Poisson négatif et 20 à 30% d'un matériau de cimentation de résine à ténacité élevée. Après test, l'élastomère à faible coefficient de Poisson a un coefficient de Poisson de 0 à 0,01, une dureté de 60 à 70 IRHD et un module élastique à un allongement défini inférieur ou égal à 2 Mpa, et la résistance à la traction de liaison de l'élastomère à faible coefficient de Poisson avec une plaque d'acier est supérieure ou égale à 2,5 Mpa. Selon la présente invention, un élastomère à faible coefficient de Poisson est formé par mélange d'une unité à coefficient de Poisson négatif avec un matériau de cimentation de résine à ténacité élevée, un faible coefficient de Poisson d'un matériau élastomère de résine d'un joint de dilatation est obtenu, le problème de planéité de surface modifiée d'un dispositif dû à un volume inchangé d'un élastomère de résine sous étirement et compression est résolu, et l'élastomère à faible coefficient de Poisson peut satisfaire une plus grande quantité de déformation de dilatation sous la même largeur.
本发明涉及桥梁伸缩缝工程技术领域，尤其涉及一种低泊松比弹性体、无缝式伸缩装置及施工工艺，其中，低泊松比弹性体按照重量分数计算，包括：70%～80% 负泊松比单元和20%～30% 高韧树脂胶结料，经过测试，低泊松比弹性体的泊松比为0～0.01，硬度为60～70IRHD，定伸弹性模量≤2Mpa，与钢板的粘结拉伸强度≥2.5Mpa，本发明采用负泊松比单元与高韧树脂胶结料拌合形成低泊松比弹性体，实现伸缩缝树脂弹性体材料的低泊松比化，解决了树脂弹性体在受到拉伸和压缩的情况下体积不变引起的装置表面平整度变化问题，在相同宽度下，低泊松比弹性体能够满足更大的伸缩变形量。
LOW-POISSON'S-RATIO ELASTOMER, SEAMLESS EXPANSION DEVICE, AND CONSTRUCTION PROCESS
The present invention relates to the technical field of bridge expansion joint engineering, and in particular, to a low-Poisson's-ratio elastomer, a seamless expansion device, and a construction process. The low-Poisson's-ratio elastomer comprises, in percentage by weight: 70-80% of a negative-Poisson's-ratio unit and 20-30% of a high-toughness resin cementing material. After testing, the low-Poisson's-ratio elastomer has a Poisson's ratio of 0-0.01, a hardness of 60-70 IRHD and an elastic modulus at definite elongation of less than or equal to 2 Mpa, and the bonding tensile strength of the low-Poisson's-ratio elastomer with a steel plate is greater than or equal to 2.5 Mpa. According to the present invention, a low-Poisson's-ratio elastomer is formed by mixing a negative-Poisson's-ratio unit with a high-toughness resin cementing material, a low Poisson's ratio of a resin elastomer material of an expansion joint is achieved, the problem of changed surface flatness of a device due to unchanged volume of a resin elastomer under stretching and compression is solved, and the low-Poisson's-ratio elastomer can meet a larger expansion deformation amount under the same width.
La présente invention concerne le domaine technique de l'ingénierie des joints de dilatation de pont, et en particulier, un élastomère à faible coefficient de Poisson, un dispositif de dilatation sans soudure et un procédé de construction. L'élastomère à faible coefficient de Poisson comprend, en pourcentage en poids : 70 à 80% d'une unité à coefficient de Poisson négatif et 20 à 30% d'un matériau de cimentation de résine à ténacité élevée. Après test, l'élastomère à faible coefficient de Poisson a un coefficient de Poisson de 0 à 0,01, une dureté de 60 à 70 IRHD et un module élastique à un allongement défini inférieur ou égal à 2 Mpa, et la résistance à la traction de liaison de l'élastomère à faible coefficient de Poisson avec une plaque d'acier est supérieure ou égale à 2,5 Mpa. Selon la présente invention, un élastomère à faible coefficient de Poisson est formé par mélange d'une unité à coefficient de Poisson négatif avec un matériau de cimentation de résine à ténacité élevée, un faible coefficient de Poisson d'un matériau élastomère de résine d'un joint de dilatation est obtenu, le problème de planéité de surface modifiée d'un dispositif dû à un volume inchangé d'un élastomère de résine sous étirement et compression est résolu, et l'élastomère à faible coefficient de Poisson peut satisfaire une plus grande quantité de déformation de dilatation sous la même largeur.
本发明涉及桥梁伸缩缝工程技术领域，尤其涉及一种低泊松比弹性体、无缝式伸缩装置及施工工艺，其中，低泊松比弹性体按照重量分数计算，包括：70%～80% 负泊松比单元和20%～30% 高韧树脂胶结料，经过测试，低泊松比弹性体的泊松比为0～0.01，硬度为60～70IRHD，定伸弹性模量≤2Mpa，与钢板的粘结拉伸强度≥2.5Mpa，本发明采用负泊松比单元与高韧树脂胶结料拌合形成低泊松比弹性体，实现伸缩缝树脂弹性体材料的低泊松比化，解决了树脂弹性体在受到拉伸和压缩的情况下体积不变引起的装置表面平整度变化问题，在相同宽度下，低泊松比弹性体能够满足更大的伸缩变形量。
LOW-POISSON'S-RATIO ELASTOMER, SEAMLESS EXPANSION DEVICE, AND CONSTRUCTION PROCESS
ÉLASTOMÈRE À FAIBLE COEFFICIENT DE POISSON, DISPOSITIF DE DILATATION SANS SOUDURE ET PROCÉDÉ DE CONSTRUCTION
一种低泊松比弹性体、无缝式伸缩装置及施工工艺
ZHANG ZHIXIANG (author) / ZHANG HUI (author) / ZHAO MENGLONG (author) / PAN YOUQIANG (author) / LI QINGXIANG (author)
2024-07-04
Patent
Electronic Resource
Chinese
Polyurethane elastomer seamless expansion device and construction process thereof
| European Patent Office | 2024
Low-Poisson-ratio elastomer, seamless telescopic device and construction technology
| European Patent Office | 2023
Super-tough elastomer seamless expansion joint and construction method
| European Patent Office | 2024
Seamless vibration and noise reduction elastomer bridge expansion device and method
| European Patent Office | 2022
| Springer Verlag | 1999