PROCESS FOR OBTAINING FIBRE-REINFORCED COMPOSITE MATERIALS
The present invention relates to a process for obtaining a flame-resistant fibre-reinforced composite material or laminate of a fibre-reinforced composite material, said method comprising the following steps a) obtaining an inorganic matrix by mixing - 70% to 80% by weight of an alkaline silicate component, preferably chosen from the group consisting of caesium (Cs) silicate, sodium (Na) silicate or potassium (K) silicate, more preferably potassium (K) silicate, said silicate component being present in an aqueous solution; - 20% to 30% by weight of a mixture of an amorphous silica component and aann aluminosilicate component, for example aa reactive aluminosilicate powder, with a silica to aluminosilicate component weight ratio of between 5: 1 and 25: 1; b) pre-impregnating a reinforcing fibre, preferably chosen from the group consisting of carbon fibre, basalt fibre and glass fibre, more preferably carbon fibre, with the inorganic matrix obtained in step a), thereby obtaining a pre-impregnated composite material; c) subjecting the pre-impregnated composite material obtained in step b) to a pressure ranging from 3 to 20 bar and a temperature ranging from 180°C to 220°C, for a time ranging from 90 minutes to 12 minutes. The invention also relates to a composite material obtained from the previously defined process, a process for producing an inorganic matrix for the production of a flame-resistant fibre-reinforced composite material and an inorganic matrix obtained from said process.
La présente invention concerne un procédé d'obtention d'un matériau composite renforcé par des fibres ignifuges ou un stratifié d'un matériau composite renforcé par des fibres, ledit procédé comprenant les étapes suivantes : a) obtention d'une matrice inorganique par mélange de 70 % à 80 % en poids d'un composant de silicate alcalin, de préférence choisi dans le groupe constitué par le silicate de césium (Cs), le silicate de sodium (Na) ou le silicate de potassium (K), plus préférablement le silicate de potassium (K), ledit composant de silicate étant présent dans une solution aqueuse ; 20 % à 30 % en poids d'un mélange d'un composant silice amorphe et d'un composant aluminosilicate aann, par exemple une poudre d'aluminosilicate réactif, avec un rapport pondéral silice/composant aluminosilicate compris entre 5:1 et 25:1 ; b) pré-imprégnation d'une fibre de renfort, de préférence choisie dans le groupe constitué de fibre de carbone, fibre de basalte et fibre de verre, plus préférentiellement de fibre de carbone, avec la matrice inorganique obtenue à l'étape a), ce qui permet d'obtenir un matériau composite pré-imprégné ; c) soumission du matériau composite pré-imprégné obtenu à l'étape b) à une pression allant de 3 à 20 bar et à une température allant de 180 °C à 220 °C, pendant une durée allant de 90 minutes à 12 minutes. L'invention concerne également un matériau composite obtenu à partir du procédé défini précédemment, un procédé de production d'une matrice inorganique pour la production d'un matériau composite renforcé par des fibres ignifuges et une matrice inorganique obtenue à partir dudit procédé.
PROCESS FOR OBTAINING FIBRE-REINFORCED COMPOSITE MATERIALS
The present invention relates to a process for obtaining a flame-resistant fibre-reinforced composite material or laminate of a fibre-reinforced composite material, said method comprising the following steps a) obtaining an inorganic matrix by mixing - 70% to 80% by weight of an alkaline silicate component, preferably chosen from the group consisting of caesium (Cs) silicate, sodium (Na) silicate or potassium (K) silicate, more preferably potassium (K) silicate, said silicate component being present in an aqueous solution; - 20% to 30% by weight of a mixture of an amorphous silica component and aann aluminosilicate component, for example aa reactive aluminosilicate powder, with a silica to aluminosilicate component weight ratio of between 5: 1 and 25: 1; b) pre-impregnating a reinforcing fibre, preferably chosen from the group consisting of carbon fibre, basalt fibre and glass fibre, more preferably carbon fibre, with the inorganic matrix obtained in step a), thereby obtaining a pre-impregnated composite material; c) subjecting the pre-impregnated composite material obtained in step b) to a pressure ranging from 3 to 20 bar and a temperature ranging from 180°C to 220°C, for a time ranging from 90 minutes to 12 minutes. The invention also relates to a composite material obtained from the previously defined process, a process for producing an inorganic matrix for the production of a flame-resistant fibre-reinforced composite material and an inorganic matrix obtained from said process.
La présente invention concerne un procédé d'obtention d'un matériau composite renforcé par des fibres ignifuges ou un stratifié d'un matériau composite renforcé par des fibres, ledit procédé comprenant les étapes suivantes : a) obtention d'une matrice inorganique par mélange de 70 % à 80 % en poids d'un composant de silicate alcalin, de préférence choisi dans le groupe constitué par le silicate de césium (Cs), le silicate de sodium (Na) ou le silicate de potassium (K), plus préférablement le silicate de potassium (K), ledit composant de silicate étant présent dans une solution aqueuse ; 20 % à 30 % en poids d'un mélange d'un composant silice amorphe et d'un composant aluminosilicate aann, par exemple une poudre d'aluminosilicate réactif, avec un rapport pondéral silice/composant aluminosilicate compris entre 5:1 et 25:1 ; b) pré-imprégnation d'une fibre de renfort, de préférence choisie dans le groupe constitué de fibre de carbone, fibre de basalte et fibre de verre, plus préférentiellement de fibre de carbone, avec la matrice inorganique obtenue à l'étape a), ce qui permet d'obtenir un matériau composite pré-imprégné ; c) soumission du matériau composite pré-imprégné obtenu à l'étape b) à une pression allant de 3 à 20 bar et à une température allant de 180 °C à 220 °C, pendant une durée allant de 90 minutes à 12 minutes. L'invention concerne également un matériau composite obtenu à partir du procédé défini précédemment, un procédé de production d'une matrice inorganique pour la production d'un matériau composite renforcé par des fibres ignifuges et une matrice inorganique obtenue à partir dudit procédé.
PROCESS FOR OBTAINING FIBRE-REINFORCED COMPOSITE MATERIALS
PROCÉDÉ D'OBTENTION DE MATÉRIAUX COMPOSITES RENFORCÉS PAR DES FIBRES
BORDIGNON CRISTIANO (author) / RUSPOLI MARESCOTTI (author)
2024-12-05
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
PROCESS FOR OBTAINING COMPOSITE, ULTRA-REFRACTORY, FIBRE-REINFORCED CERAMIC MATERIALS
| European Patent Office | 2022
PROCESS FOR OBTAINING COMPOSITE, ULTRA-REFRACTORY, FIBRE-REINFORCED CERAMIC MATERIALS
| European Patent Office | 2021
PROCESS FOR OBTAINING COMPOSITE, ULTRA-REFRACTORY, FIBRE-REINFORCED CERAMIC MATERIALS
| European Patent Office | 2020
Fibre reinforced composite materials for reinforced concrete construction
| British Library Conference Proceedings | 1994
Fundamentals of Fibre Reinforced Composite Materials
British Library Online Contents | 2005