Technical activities report - July 1952 graphite development - pile graphite
Physical data are presented for transverse CSF samples with capsule exposures of 568, 1049, and 1617 MD/CT. The higher exposures indicate a sharper damage gradient toward the front of the pile. Additional casings of various types of graphite were loaded into test holes during this month. Average values of the thermal conductivity and electrical resistivity for several types of virgin graphites are presented. Data of this nature will be a regular portion of this report henceforth. Process tube channel 2677-H was mined and traversed for bore diameter. Although several of the tube block junctions were obscured, the channel was quite uniform. Examination of all previously mined graphite powder samples for aluminum oxide corrosion product has been completed and the results are reported.
Technical activities report - July 1952 graphite development - pile graphite
Physical data are presented for transverse CSF samples with capsule exposures of 568, 1049, and 1617 MD/CT. The higher exposures indicate a sharper damage gradient toward the front of the pile. Additional casings of various types of graphite were loaded into test holes during this month. Average values of the thermal conductivity and electrical resistivity for several types of virgin graphites are presented. Data of this nature will be a regular portion of this report henceforth. Process tube channel 2677-H was mined and traversed for bore diameter. Although several of the tube block junctions were obscured, the channel was quite uniform. Examination of all previously mined graphite powder samples for aluminum oxide corrosion product has been completed and the results are reported.
Technical activities report - July 1952 graphite development - pile graphite
J. F. Music (author) / H. F. Zuhr (author)
1952
34 pages
Report
No indication
English
Reactor Engineering & Nuclear Power Plants , Carbon & Graphite , Materials Degradation & Fouling , Physical & Theoretical Chemistry , Graphite , Graphite Moderated Reactors , Aluminium Oxides , Burnout , Chemical Radiation Effects , Corrosion , Degassing , Historical Aspects , Mass Spectroscopy , Microstructure , Physical Properties , Physical Radiation Effects , Progress Report , Thermal Conductivity , X-Ray Diffraction , EDB/210300 , EDB/220600
Technical activities report, June 1952: Pile Physics
| NTIS | 1952