Effect of Retained Austenite on the Fatigue Properties of Carburized 9310 Steel
The effect of retained austenite on the bending fatigue durability of carburized 9310 steel was investigated. It was found that nonfrozen test bars, containing 13.8 to 18.5% retained austenite had superior fatigue resistance than frozen test bars, containing 5.3-7.3% retained austenite. The mean fatigue life ratio of nonfrozen to frozen bars at 155 KSI was determined to be 3.5, with a 99% confidence. (Author)
Effect of Retained Austenite on the Fatigue Properties of Carburized 9310 Steel
The effect of retained austenite on the bending fatigue durability of carburized 9310 steel was investigated. It was found that nonfrozen test bars, containing 13.8 to 18.5% retained austenite had superior fatigue resistance than frozen test bars, containing 5.3-7.3% retained austenite. The mean fatigue life ratio of nonfrozen to frozen bars at 155 KSI was determined to be 3.5, with a 99% confidence. (Author)
Effect of Retained Austenite on the Fatigue Properties of Carburized 9310 Steel
M. Raefsky (author)
1968
20 pages
Report
No indication
English
Examination of pitting fatigue in carburized steels with controlled retained austenite fractions
| Automotive engineering | 2006
Retained Austenite - Residual Stress - Distortion Relationships in Carburized SAE 6820 Steel
| British Library Online Contents | 2007
| British Library Online Contents | 2015
| British Library Online Contents | 2019
| British Library Online Contents | 2014