Evaluation of Stress Corrosion Cracking Characteristics of Selected Fastener Systems in 7075-T6 Aluminum

N. R. Ontko

This effort evaluated the stress corrosion cracking characteristics of selected fatigue rated fastener systems in 7075-T6 Aluminum extruded material. The fastener systems used were installed with equivalent amounts of interference in the test blocks and subjected to 1700 hours of alternate immersion exposure in 3.5 % salt water. (Author)

Access

Check availability in my library

Page navigation

Document information

Export, share and cite

Evaluation of Stress Corrosion Cracking Characteristics of Selected Fastener Systems in 7075-T6 Aluminum

N. R. Ontko

This effort evaluated the stress corrosion cracking characteristics of selected fatigue rated fastener systems in 7075-T6 Aluminum extruded material. The fastener systems used were installed with equivalent amounts of interference in the test blocks and subjected to 1700 hours of alternate immersion exposure in 3.5 % salt water. (Author)

Evaluation of Stress Corrosion Cracking Characteristics of Selected Fastener Systems in 7075-T6 Aluminum

N. R. Ontko

This effort evaluated the stress corrosion cracking characteristics of selected fatigue rated fastener systems in 7075-T6 Aluminum extruded material. The fastener systems used were installed with equivalent amounts of interference in the test blocks and subjected to 1700 hours of alternate immersion exposure in 3.5 % salt water. (Author)

Access

Check availability in my library

Page navigation

Document information

Export, share and cite

Document information

Title:

Evaluation of Stress Corrosion Cracking Characteristics of Selected Fastener Systems in 7075-T6 Aluminum

Contributors:

N. R. Ontko (author)

Publication date:

1983

Size:

40 pages

Type of media:

Report

Type of material:

No indication

Language:

English

Keywords:

Industrial & Mechanical Engineering , Joining , Tribology , Corrosion & Corrosion Inhibition , Aluminum , Aluminum alloys , Fastenings , Stress corrosion , Cracking(Fracturing) , Test and evaluation , Fatigue(Mechanics) , Salt water , Cold working , Expansion , Steel , Cadmium , Aluminum 7075 T6 , Aluminum alloy 2024

Similar titles

Stress corrosion cracking behavior of Nd:YAG laser-treated aluminum alloy 7075

Yue, T. M. / Yan, L. J. / Chan, C. P. | British Library Online Contents | 2006

Effect of Electrode Polarization on Stress Corrosion Cracking of 7075 Aluminum Alloys

Liu, J.-h. / Zhu, G.-w. / Li, D. et al. | British Library Online Contents | 2005

Stress corrosion cracking of aluminium alloy 7075(W) under tensile and compressive loading

Dollah, M. / Robinson, M.J. | British Library Online Contents | 2011

Effects of Prior Corrosion and Stress in Corrosion Fatigue of Aluminum Alloy 7075-T6

Arriscorreta, C.A. / Hoeppner, D.W. | British Library Online Contents | 2012

Improvements in Strength and Stress Corrosion Cracking Properties in Aluminum Alloy 7075 via Low-Temperature Retrogression and Re-Aging Heat Treatments

Ferrer, C. P. / Koul, M. G. / Connolly, B. J. et al. | British Library Online Contents | 2003