Cu-Mn-Ce ternary mixed-oxide catalysts for catalytic combustion of toluene
Cu-Mn, Cu-Mn-Ce, and Cu-Ce mixed-oxide catalysts were prepared by a citric acid sol-gel method and then characterized by XRD, BET, H_2-TPR and XPS analyses. Their catalytic properties were investigated in the toluene combustion reaction. Results showed that the Cu-Mn-Ce ternary mixed-oxide catalyst with 1：2：4 mole ratios had the highest catalytic activity, and 99% toluene conversion was achieved at temperatures below 220°C. In the Cu-Mn-Ce catalyst, a portion of Cu and Mn species entered into the Ce O2 fluorite lattice, which led to the formation of a ceria-based solid solution. Excess Cu and Mn oxides existed on the surface of the ceria-based solid solution. The coexistence of Cu-Mn mixed oxides and the ceria-based solid solution resulted in a better synergetic interaction than the Cu-Mn and Cu-Ce catalysts, which promoted catalyst reducibility, increased oxygen mobility, and enhanced the formation of abundant active oxygen species.
Cu-Mn-Ce ternary mixed-oxide catalysts for catalytic combustion of toluene
Cu-Mn, Cu-Mn-Ce, and Cu-Ce mixed-oxide catalysts were prepared by a citric acid sol-gel method and then characterized by XRD, BET, H_2-TPR and XPS analyses. Their catalytic properties were investigated in the toluene combustion reaction. Results showed that the Cu-Mn-Ce ternary mixed-oxide catalyst with 1：2：4 mole ratios had the highest catalytic activity, and 99% toluene conversion was achieved at temperatures below 220°C. In the Cu-Mn-Ce catalyst, a portion of Cu and Mn species entered into the Ce O2 fluorite lattice, which led to the formation of a ceria-based solid solution. Excess Cu and Mn oxides existed on the surface of the ceria-based solid solution. The coexistence of Cu-Mn mixed oxides and the ceria-based solid solution resulted in a better synergetic interaction than the Cu-Mn and Cu-Ce catalysts, which promoted catalyst reducibility, increased oxygen mobility, and enhanced the formation of abundant active oxygen species.
Cu-Mn-Ce ternary mixed-oxide catalysts for catalytic combustion of toluene
2015
Article (Journal)
English
Hydrotalcite-derived cobalt–aluminum mixed oxide catalysts for toluene combustion
| British Library Online Contents | 2016
Hydrotalcite-derived cobalt–aluminum mixed oxide catalysts for toluene combustion
| British Library Online Contents | 2016
Hydrotalcite-derived cobalt–aluminum mixed oxide catalysts for toluene combustion
| British Library Online Contents | 2016
| British Library Online Contents | 2009
Oxidative dehydrodimerization of toluene on lead-tin oxide catalysts
| Elsevier | 1983