A platform for research: civil engineering, architecture and urbanism
A platform for research: civil engineering, architecture and urbanism
Flexural behaviour of glass fibre-reinforced polymer and ultra-high-strength fibre-reinforced concrete composite beams subjected to elevated temperature
Composite beams consisting of pultruded glass fibre-reinforced polymer (GFRP) I-beams and ultra-high-strength fibre-reinforced concrete (UFC) slabs have been developed for use in short-span bridges. Fibre-reinforced polymer bolts (fibre-reinforced polymer threaded rods) and epoxy adhesive were used to connect the UFC slab to the GFRP I-beam. The authors conducted material tests and large-scale static bending tests at room and elevated temperatures (less than 90°C) to investigate the flexural behaviour of GFRP-UFC composite beams subjected to elevated temperature. The test results demonstrated that the mechanical properties of the GFRP I-beams, fibre-reinforced polymer bolts and epoxy adhesive were significantly deteriorated at elevated temperatures due to the glass transition of their polymer resin matrices. As a result, the stiffness and ultimate flexural capacity of the GFRP-UFC composite beams under elevated temperatures were significantly reduced. More than 85% of the flexural capacity of the GFRP-UFC composite beams was retained up to 60°C but that was decreased to 50% at 90°C. Fibre model analysis results confirmed that the stiffness of the GFRP-UFC composite beams is not significantly affected by actual hot environments, where there is a moderate temperature gradient across the beam cross-section.
Flexural behaviour of glass fibre-reinforced polymer and ultra-high-strength fibre-reinforced concrete composite beams subjected to elevated temperature
Composite beams consisting of pultruded glass fibre-reinforced polymer (GFRP) I-beams and ultra-high-strength fibre-reinforced concrete (UFC) slabs have been developed for use in short-span bridges. Fibre-reinforced polymer bolts (fibre-reinforced polymer threaded rods) and epoxy adhesive were used to connect the UFC slab to the GFRP I-beam. The authors conducted material tests and large-scale static bending tests at room and elevated temperatures (less than 90°C) to investigate the flexural behaviour of GFRP-UFC composite beams subjected to elevated temperature. The test results demonstrated that the mechanical properties of the GFRP I-beams, fibre-reinforced polymer bolts and epoxy adhesive were significantly deteriorated at elevated temperatures due to the glass transition of their polymer resin matrices. As a result, the stiffness and ultimate flexural capacity of the GFRP-UFC composite beams under elevated temperatures were significantly reduced. More than 85% of the flexural capacity of the GFRP-UFC composite beams was retained up to 60°C but that was decreased to 50% at 90°C. Fibre model analysis results confirmed that the stiffness of the GFRP-UFC composite beams is not significantly affected by actual hot environments, where there is a moderate temperature gradient across the beam cross-section.
Flexural behaviour of glass fibre-reinforced polymer and ultra-high-strength fibre-reinforced concrete composite beams subjected to elevated temperature
2017
Article (Journal)
English
| Springer Verlag | 2020