Flame-retardant mechanism of zinc borate and magnesium hydroxide in aluminum hypophosphite–based combination for TPE-S composites
https://orcid.org/0000-0001-5298-0141
Aluminum hypophosphite combined with melamine cyanurate and poly(phenylene oxide) was applied to flame retard TPE-S system (blends of SEBS and polyolefin). TPE-S containing 16 wt% aluminum hypophosphite, 20 wt% melamine cyanurate, and 10 wt% poly(phenylene oxide) pass a V-0 rating in the UL-94 test and its limiting oxygen index value is 28.2%. Zinc borate and magnesium hydroxide were added to modify the AHP/MCA/PPO formulation. Thermogravimetric–Fourier transform infrared analysis tests showed that aluminum hypophosphite and melaminecyanurate acted in gaseous phase while aluminum hypophosphite and poly(phenylene oxide) helped to form char residue. TPE-S/AHP/MCA/PPO significantly decreased the heat release rate (reduction in peak heat release rate from 2001 to 494 kW m−2). Scanning electron microscopy/energy dispersive spectrometry results demonstrated that zinc borate and magnesium hydroxide promoted to retain more P and O elements in residue. Zinc borate and magnesium hydroxide in AHP/MCA/PPO formulation enhanced the char formation and reduced gas evolution of TPE-S, thus deteriorating the combination between gaseous phase and condensed phase.
Flame-retardant mechanism of zinc borate and magnesium hydroxide in aluminum hypophosphite–based combination for TPE-S composites
https://orcid.org/0000-0001-5298-0141
Aluminum hypophosphite combined with melamine cyanurate and poly(phenylene oxide) was applied to flame retard TPE-S system (blends of SEBS and polyolefin). TPE-S containing 16 wt% aluminum hypophosphite, 20 wt% melamine cyanurate, and 10 wt% poly(phenylene oxide) pass a V-0 rating in the UL-94 test and its limiting oxygen index value is 28.2%. Zinc borate and magnesium hydroxide were added to modify the AHP/MCA/PPO formulation. Thermogravimetric–Fourier transform infrared analysis tests showed that aluminum hypophosphite and melaminecyanurate acted in gaseous phase while aluminum hypophosphite and poly(phenylene oxide) helped to form char residue. TPE-S/AHP/MCA/PPO significantly decreased the heat release rate (reduction in peak heat release rate from 2001 to 494 kW m−2). Scanning electron microscopy/energy dispersive spectrometry results demonstrated that zinc borate and magnesium hydroxide promoted to retain more P and O elements in residue. Zinc borate and magnesium hydroxide in AHP/MCA/PPO formulation enhanced the char formation and reduced gas evolution of TPE-S, thus deteriorating the combination between gaseous phase and condensed phase.
Flame-retardant mechanism of zinc borate and magnesium hydroxide in aluminum hypophosphite–based combination for TPE-S composites
https://orcid.org/0000-0001-5298-0141
Aluminum hypophosphite combined with melamine cyanurate and poly(phenylene oxide) was applied to flame retard TPE-S system (blends of SEBS and polyolefin). TPE-S containing 16 wt% aluminum hypophosphite, 20 wt% melamine cyanurate, and 10 wt% poly(phenylene oxide) pass a V-0 rating in the UL-94 test and its limiting oxygen index value is 28.2%. Zinc borate and magnesium hydroxide were added to modify the AHP/MCA/PPO formulation. Thermogravimetric–Fourier transform infrared analysis tests showed that aluminum hypophosphite and melaminecyanurate acted in gaseous phase while aluminum hypophosphite and poly(phenylene oxide) helped to form char residue. TPE-S/AHP/MCA/PPO significantly decreased the heat release rate (reduction in peak heat release rate from 2001 to 494 kW m−2). Scanning electron microscopy/energy dispersive spectrometry results demonstrated that zinc borate and magnesium hydroxide promoted to retain more P and O elements in residue. Zinc borate and magnesium hydroxide in AHP/MCA/PPO formulation enhanced the char formation and reduced gas evolution of TPE-S, thus deteriorating the combination between gaseous phase and condensed phase.
Flame-retardant mechanism of zinc borate and magnesium hydroxide in aluminum hypophosphite–based combination for TPE-S composites
Cheng, Xi (author) / Wu, Jianming (author) / Yao, Chenguang (author) / Yang, Guisheng (author)
Journal of Fire Sciences ; 37 ; 273-300
2019-05-01
28 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2018
| British Library Online Contents | 2018
Magnesium hydroxide/zinc borate/talc compositions as flame-retardants in EVA copolymer
| Tema Archive | 2000
Study of using aluminum hypophosphite as a flame retardant for low‐density polyethylene
| British Library Online Contents | 2017