Investigation of ductile fracture behavior of lap-welded joints with 460 MPa steel
Fractures in welded connections usually occurred at Earthquake. The lap-welded joints are an important type of welded connections in high strength steel structures. In this article, the ductile fracture behavior of lap-welded joints has been studied experimentally and numerically with 460 MPa steel. A series of coupon tests were used to determine two corresponding weld materials (ER55-D2 and ER55-G) mechanical properties. Two micromechanics models (void growth model and stress-modified critical strain models) had been calibrated by circumferentially notched tension specimens and calculated the fracture parameters numerically, which had been applied in predicting in five lap-welded joints. The experimental study showed that the fracture mode of 460 MPa lap-welded joints exhibited plastic damage under the tension tests. Numerical analysis of the fracture parameters also showed that the ductile fracture behavior of lap-welded joint with ER55-G was better. The study establishes an accurate numerical model for analyzing the ductile fracture behavior of Q460 high strength steel lap-welded joints that is applicable in predicting the fracture failure of welded steel structures.
Investigation of ductile fracture behavior of lap-welded joints with 460 MPa steel
Fractures in welded connections usually occurred at Earthquake. The lap-welded joints are an important type of welded connections in high strength steel structures. In this article, the ductile fracture behavior of lap-welded joints has been studied experimentally and numerically with 460 MPa steel. A series of coupon tests were used to determine two corresponding weld materials (ER55-D2 and ER55-G) mechanical properties. Two micromechanics models (void growth model and stress-modified critical strain models) had been calibrated by circumferentially notched tension specimens and calculated the fracture parameters numerically, which had been applied in predicting in five lap-welded joints. The experimental study showed that the fracture mode of 460 MPa lap-welded joints exhibited plastic damage under the tension tests. Numerical analysis of the fracture parameters also showed that the ductile fracture behavior of lap-welded joint with ER55-G was better. The study establishes an accurate numerical model for analyzing the ductile fracture behavior of Q460 high strength steel lap-welded joints that is applicable in predicting the fracture failure of welded steel structures.
Investigation of ductile fracture behavior of lap-welded joints with 460 MPa steel
Shi, Gang (author) / Chen, Yufeng (author)
Advances in Structural Engineering ; 21 ; 1376-1387
2018-07-01
12 pages
Article (Journal)
Electronic Resource
English
Ductile fracture of welded steel structures
| TIBKAT | 2020
A Ductile Tear Fracture Analysis of Lap Welded Joints
| British Library Online Contents | 2004
Effect of pitting degradation on ductile fracture initiation of steel butt-welded joints
| British Library Online Contents | 2018
Assessment and representation of ductile fracture failure for welded tubular joints
| British Library Conference Proceedings | 2015