A toughness based deformation limit for X- and K-joints under brace axial tension
Abstract This study reports a deformation limit for the initiation of ductile fracture failure in fatigue-cracked circular hollow section (CHS) X- and K-joints subjected to brace axial tension. The proposed approach sets the deformation limit as the numerically computed crack driving force in a fatigue crack at the hot-spot location in the tubular joint reaches the material fracture toughness measured from standard fracture specimens. The calibration of the numerical procedure predicates on reported numerical computations on the crack driving force and previously published verification study against large-scale CHS X-joints with fatigue generated surface cracks. The development of the deformation limit includes a normalization procedure, which covers a wide range of the geometric parameters and material toughness levels. The lower-bound deformation limits thus developed follow a linear relationship with respect to the crack-depth ratio for both X- and K-joints. Comparison of the predicated deformation limit against experimental on cracked tubular X- and K-joints demonstrates the conservative nature of the proposed deformation limit. The proposed deformation limit, when extrapolated to a zero crack depth, provides an estimate on the deformation limits for intact X- and K-joints under brace axial loads.
A toughness based deformation limit for X- and K-joints under brace axial tension
Abstract This study reports a deformation limit for the initiation of ductile fracture failure in fatigue-cracked circular hollow section (CHS) X- and K-joints subjected to brace axial tension. The proposed approach sets the deformation limit as the numerically computed crack driving force in a fatigue crack at the hot-spot location in the tubular joint reaches the material fracture toughness measured from standard fracture specimens. The calibration of the numerical procedure predicates on reported numerical computations on the crack driving force and previously published verification study against large-scale CHS X-joints with fatigue generated surface cracks. The development of the deformation limit includes a normalization procedure, which covers a wide range of the geometric parameters and material toughness levels. The lower-bound deformation limits thus developed follow a linear relationship with respect to the crack-depth ratio for both X- and K-joints. Comparison of the predicated deformation limit against experimental on cracked tubular X- and K-joints demonstrates the conservative nature of the proposed deformation limit. The proposed deformation limit, when extrapolated to a zero crack depth, provides an estimate on the deformation limits for intact X- and K-joints under brace axial loads.
A toughness based deformation limit for X- and K-joints under brace axial tension
Gu, Bo (author) / Qian, Xudong (author) / Ahmed, Aziz (author)
Frontiers of Structural and Civil Engineering ; 10 ; 345-362
2016-03-11
18 pages
Article (Journal)
Electronic Resource
English
Capacity Difference of Circular Hollow Section X-joints Under Brace Axial Compression and Tension
| Springer Verlag | 2020
A toughness based deformation limit for fatigue-cracked X-joints under in-plane bending
| Online Contents | 2015
Stress concentration factors of bird-beak SHS X-joints under brace axial forces
| British Library Online Contents | 2018
Design of CHS brace-to-H-shaped chord T-joints under axial compression
| Online Contents | 2016