Influence of residual stresses in the tensile test of cold drawn wires
Abstract The aim of this paper is to investigate the influence of residual stresses, due to cold-drawing, on the shape of the tensile stress-strain curve and particularly its influence on the ratio σ0.2/σmax through a numerical and experimental work. It was found that residual stresses favours the onset of yielding and the ratio σ0.2/σmax decreases with increasing values of residual stresses. Because of the deleterious effect of residual stresses on fatigue and stress corrosion and because such stresses affect the ratio σ0.2/σmax, it is reasonable to-put a lower limit to σ0.2/σmax in the standards. The ratio σ0.2/σmax can be increased by relieving residual stresses, a common procedure after drawing. This fact is also ascertained.
Résumé L'objectif de cet article est la recherche numérique et expérimentale de l'influence des contraintes résiduelles dues au tréfilage à froid sur la forme de la courbe contrainte-déformation et, plus particulièrement, son influence sur le ratio σ0.2/σmax. Cet article montre que les contraintes résiduelles favorisent la plastification. Le ratio σ0.2/σmax diminue au fur et à mesure que les contraintes résiduelles augmentent. À cause des effets négatifs des contraintes résiduelles sur la fatigue et la corrosion des matériaux, il est raisonnable de demander une valeur limite pour σ0.2/σmax. Le ratio σ0.2/σmax peut être augmenté à condition de relâcher les contraintes résiduelles, une procédure normale après le tréfilage.
Influence of residual stresses in the tensile test of cold drawn wires
Abstract The aim of this paper is to investigate the influence of residual stresses, due to cold-drawing, on the shape of the tensile stress-strain curve and particularly its influence on the ratio σ0.2/σmax through a numerical and experimental work. It was found that residual stresses favours the onset of yielding and the ratio σ0.2/σmax decreases with increasing values of residual stresses. Because of the deleterious effect of residual stresses on fatigue and stress corrosion and because such stresses affect the ratio σ0.2/σmax, it is reasonable to-put a lower limit to σ0.2/σmax in the standards. The ratio σ0.2/σmax can be increased by relieving residual stresses, a common procedure after drawing. This fact is also ascertained.
Résumé L'objectif de cet article est la recherche numérique et expérimentale de l'influence des contraintes résiduelles dues au tréfilage à froid sur la forme de la courbe contrainte-déformation et, plus particulièrement, son influence sur le ratio σ0.2/σmax. Cet article montre que les contraintes résiduelles favorisent la plastification. Le ratio σ0.2/σmax diminue au fur et à mesure que les contraintes résiduelles augmentent. À cause des effets négatifs des contraintes résiduelles sur la fatigue et la corrosion des matériaux, il est raisonnable de demander une valeur limite pour σ0.2/σmax. Le ratio σ0.2/σmax peut être augmenté à condition de relâcher les contraintes résiduelles, une procédure normale après le tréfilage.
Influence of residual stresses in the tensile test of cold drawn wires
Atienza, J. M. (author) / Elices, M. (author)
Materials and Structures ; 36 ; 548-552
2003-10-01
5 pages
Article (Journal)
Electronic Resource
English
Influence of residual stresses in the tensile test of cold drawn wires
| British Library Online Contents | 2003
Influence of residual stresses in the tensile test of cold drawn wires
| Online Contents | 2003
Influence of residual stresses in the tensile test of cold drawn wires
| Online Contents | 2003
Influence of residual stresses on hydrogen embrittlement of cold drawn wires
| British Library Online Contents | 2004
Influence of residual stresses on hydrogen embrittlement of cold drawn wires
| Online Contents | 2004