3D Printing of Fast Setting Basalt Fiber Reinforced Cement-Based Materials
https://orcid.org/http://orcid.org/0000-0002-2008-2977
https://orcid.org/http://orcid.org/0000-0003-3098-2108
https://orcid.org/http://orcid.org/0000-0003-2364-6616
In this study, the traditional 3D printing process was enhanced, the mixing and pumping processes were removed, and the concrete 3D printer with simultaneous mixing and extrusion of materials was independently developed. The printing of rapid-setting cement-based materials was successfully realized, and the printing performance of rapid-setting basalt fiber reinforced cement-based materials were tested. The results show that the mixing-extrusion integrated concrete 3D printer can successfully print the rapid solidification cement-based composite material with the final setting time of less than 5 min. Under the requirements of printing performance, the dosage range of basalt fiber is 0–2.0%, and the printing performance is the best when the dosage is 1.5%.
3D Printing of Fast Setting Basalt Fiber Reinforced Cement-Based Materials
https://orcid.org/http://orcid.org/0000-0002-2008-2977
https://orcid.org/http://orcid.org/0000-0003-3098-2108
https://orcid.org/http://orcid.org/0000-0003-2364-6616
In this study, the traditional 3D printing process was enhanced, the mixing and pumping processes were removed, and the concrete 3D printer with simultaneous mixing and extrusion of materials was independently developed. The printing of rapid-setting cement-based materials was successfully realized, and the printing performance of rapid-setting basalt fiber reinforced cement-based materials were tested. The results show that the mixing-extrusion integrated concrete 3D printer can successfully print the rapid solidification cement-based composite material with the final setting time of less than 5 min. Under the requirements of printing performance, the dosage range of basalt fiber is 0–2.0%, and the printing performance is the best when the dosage is 1.5%.
3D Printing of Fast Setting Basalt Fiber Reinforced Cement-Based Materials
https://orcid.org/http://orcid.org/0000-0002-2008-2977
https://orcid.org/http://orcid.org/0000-0003-3098-2108
https://orcid.org/http://orcid.org/0000-0003-2364-6616
In this study, the traditional 3D printing process was enhanced, the mixing and pumping processes were removed, and the concrete 3D printer with simultaneous mixing and extrusion of materials was independently developed. The printing of rapid-setting cement-based materials was successfully realized, and the printing performance of rapid-setting basalt fiber reinforced cement-based materials were tested. The results show that the mixing-extrusion integrated concrete 3D printer can successfully print the rapid solidification cement-based composite material with the final setting time of less than 5 min. Under the requirements of printing performance, the dosage range of basalt fiber is 0–2.0%, and the printing performance is the best when the dosage is 1.5%.
3D Printing of Fast Setting Basalt Fiber Reinforced Cement-Based Materials
Lecture Notes in Civil Engineering
Guo, Wei (editor) / Qian, Kai (editor) / Li, Weihong (author) / Chen, Xuhao (author) / Li, Nan (author)
International Conference on Green Building, Civil Engineering and Smart City ; 2022 ; Guilin, China
2022-09-08
8 pages
Article/Chapter (Book)
Electronic Resource
English
Basalt Fiber Reinforce Cement-Based Composite Materials
| Tema Archive | 2011
Basalt Fiber Reinforce Cement-Based Composite Materials
| British Library Conference Proceedings | 2012
Basalt fiber reinforced cement-based composite material and preparation method thereof
| European Patent Office | 2023